- 缺口冲击强度: 0.641
- 弯曲模量 [MPa]: 5.195
- 热变形温度 [℃]: 248.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm @Thickness 3.175 mm | 0.0070 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 115 MPa | 16700 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
| Flexural Modulus | 5.195 GPa | 753.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.11 J/cm | 7.70 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 262 °C | 504 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 248 °C | 478 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 244 °C | 471 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
| Moisture Content | 0.080 - 0.12 % | 0.080 - 0.12 % | |