- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 7.4
- 缺口冲击强度: 5.2
- 弯曲强度 [MPa]: 125.0
- 弯曲模量 [MPa]: 5.17
- 热变形温度 [℃]: 257.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.4 % | 7.4 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 117 MPa | 17000 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 125 MPa | 18100 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 6.00 GPa | 870 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 190 MPa | 27600 psi | ASTM Test | ||
| Flexural Modulus | 5.17 GPa | 750 ksi | ASTM Test | ||
| 5.80 GPa | 841 ksi | ISO Data | |||
| Izod Impact, Notched (ISO) | 5.20 kJ/m² | 2.47 ft-lb/in² | ISO Test | ||
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179 | ||
| 4.50 J/cm² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179 | ||
| 0.450 J/cm² @Temperature -30.0 °C | 2.14 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 257 °C | 495 °F | 10 K/min | ||
| 257 °C | 495 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | ASTM Test | ||
| 262 °C | 504 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 231 °C | 448 °F | ASTM Test | ||
| 245 °C | 473 °F | ISO 75 | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||