- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 8.5
- 缺口冲击强度: 14.0
- 拉伸强度 [MPa]: 54.0
- 弯曲模量 [MPa]: 1.10
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 8.5 % | 8.5 % | beginning dry; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50mm/min; ISO 527 | ||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 25 % | 25 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 1.10 GPa | 160 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO Test | ||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179 | ||
| 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 257 °C | 495 °F | 10 K/min | ||
| 257 °C | 495 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||