- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 4.0
- 缺口冲击强度: 15.0
- 弯曲强度 [MPa]: 254.0
- 弯曲模量 [MPa]: 16.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.0 % | 4.0 % | ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 254 MPa | 36800 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 14.7 GPa | 2130 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 16.1 GPa | 2340 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10 K/min | ||
| Descriptive Properties | |||||
| Color | BK00564 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||