- 熔体流动速率 [g/10min]: 53.6
- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 5.7
- 缺口冲击强度: 17.0
- 拉伸强度 [MPa]: 100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.7 - 6.3 % | 5.7 - 6.3 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.2 - 1.6 % | 1.2 - 1.6 % | (23°C/50% R.H.); ISO 62 | ||
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number; ISO 307 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |||
| Melt Flow | 53.6 g/10 min @Load 5.00 kg, Temperature 275 °C | 53.6 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 100 MPa | 14500 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 4.5 % | 4.5 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 6.00 GPa | 870 ksi | ISO 527 | ||
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO 180/A | ||
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 3500 MPa | 508000 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 5.0 @Frequency 1.00e+6 Hz | 5.0 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.10 @Frequency 1.00e+6 Hz | 0.10 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 139 °C | 282 °F | for 50% loss of tensile strength after 20,000 hr | ||
| 157 °C | 315 °F | for 50% loss of tensile strength after 5,000 hr | |||
| 220 °C | 428 °F | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Flame retarding agent | ||||
| Heat stabilized or stable to heat | |||||
| Release agent | |||||