- 熔体流动速率 [g/10min]: 66.0
- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 5.7
- 缺口冲击强度: 9.5
- 拉伸强度 [MPa]: 120.0
- 弯曲模量 [MPa]: 7.60
- 热变形温度 [℃]: 250.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.7 - 6.3 % | 5.7 - 6.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.7 - 2.1 % | 1.7 - 2.1 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 145 | 145 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | restricted | ||
| Melt Flow | 66 g/10 min @Load 5.00 kg, Temperature 275 °C | 66 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 120 MPa | 17400 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 8.60 GPa | 1250 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 260 MPa | 37700 psi | at max force; ISO 178 | ||
| Flexural Modulus | 7.60 GPa | 1100 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 9.50 kJ/m² @Temperature 23.0 °C | 4.52 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C | 26.2 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 6.50 J/cm² @Temperature 23.0 °C | 30.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1.00 Hz | 3.5 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.250 - 0.350 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.139 - 0.194 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.600 - 0.700 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.333 - 0.389 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr | ||
| 165 °C | 329 °F | for 50% loss of tensile strength after 5000hr | |||
| 240 °C | 464 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||