BASF Ultramid® A3WG10 BK 00564 50% Glass Filled PA66 (Conditioned)

BASF Ultramid® A3WG10 BK 00564 50% Glass Filled PA66 (Conditioned) 物性表: BASF Ultramid® A3WG10 BK 00564 50% Glass Filled PA66 (Conditioned)物性表及特性介绍,BASF Ultramid® A3WG10 BK 00564 50% Glass Filled PA66 (Conditioned)注塑参数详情,如需BASF Ultramid® A3WG10 BK 00564 50% Glass Filled PA66 (Conditioned)下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 31.2
  • 密度 [g/cm3]: 1.56
  • 吸水率 [%]: 3.7
  • 缺口冲击强度: 14.5
  • 拉伸强度 [MPa]: 180.0
  • 弯曲模量 [MPa]: 13.5
 
Physical PropertiesMetricEnglishComments
Density 1.56 g/cc0.0564 lb/in³ISO 1183
Water Absorption 3.7 - 4.3 %3.7 - 4.3 %Saturation; ISO 62
Moisture Absorption at Equilibrium 1.0 - 1.4 %1.0 - 1.4 %23°C; 50% RH; ISO 62
Viscosity Measurement 130130ISO 307
Linear Mold Shrinkage 0.0045 cm/cm0.0045 in/inrestricted
Melt Flow 31.2 g/10 min
@Load 5.00 kg,
Temperature 275 °C
31.2 g/10 min
@Load 11.0 lb,
Temperature 527 °F
ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Yield 180 MPa26100 psi50 mm/min; ISO 527-1/-2
Elongation at Yield 3.5 %3.5 %50 mm/min; ISO 527-1/-2
Modulus of Elasticity 12.5 GPa1810 ksiISO 527-1/-2
Flexural Strength 300 MPa43500 psiat max force; ISO 178
Flexural Modulus 13.5 GPa1960 ksiISO 178
Izod Impact, Notched (ISO) 14.5 kJ/m²
@Temperature 23.0 °C
6.90 ft-lb/in²
@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 10.0 J/cm²
@Temperature 23.0 °C
47.6 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 2.50 J/cm²
@Temperature 23.0 °C
11.9 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 7800 MPa
@Strain <=0.500 %
1.13e+6 psi
@Strain <=0.500 %
ISO 899-1
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+10 ohm-cm1.00e+10 ohm-cmIEC 60093
Surface Resistance 1.00e+10 ohm1.00e+10 ohmIEC 60093
Dielectric Constant 6.6
@Frequency 1.00 Hz
6.6
@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.30
@Frequency 1.00e+6 Hz
0.30
@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 450 V450 VTest solution A; IEC 60112
 
Thermal PropertiesMetricEnglishComments
Thermal Conductivity 0.370 W/m-K2.57 BTU-in/hr-ft²-°FDIN 52612
Melting Point 260 °C500 °FDIN 53765
Maximum Service Temperature, Air 145 °C293 °Ffor 50% loss of tensile strength after 20000hr
 175 °C347 °Ffor 50% loss of tensile strength after 5000hr
 240 °C464 °F
 
Processing PropertiesMetricEnglishComments
Melt Temperature 290 - 310 °C554 - 590 °FInjection-molding/Extrusion
Mold Temperature 80.0 - 90.0 °C176 - 194 °FInjection-molding
 
Descriptive Properties
ColorBK 00564
Commercial StatusEurope

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45099.html

免责声明: 本文 BASF Ultramid® A3WG10 BK 00564 50% Glass Filled PA66 (Conditioned) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4