- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.6
- 缺口冲击强度: 0.854
- 弯曲模量 [MPa]: 8.96
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.60 % | 0.60 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 148 MPa | 21500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm | 1.60 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | Unannealed; ASTM D648 |