- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 5.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | in normal climate 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 5.5 % | 5.5 % | in water at 23°C; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 76 @Thickness 10.0 mm | 76 @Thickness 0.394 in | ISO 2039-2 |
| Ball Indentation Hardness | 165 MPa | 23900 psi | value at 30 sec.; ISO 2039-1 |
| Tensile Strength at Break | 100 MPa | 14500 psi | v = 5 mm/min; ISO 527-2 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-2 |
| Tensile Modulus | 5.90 GPa | 856 ksi | ISO 527-2 |
| Charpy Impact Unnotched | >= 5.00 J/cm² | >= 23.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 µm/m-°C @Temperature 20.0 °C | 27.8 µin/in-°F @Temperature 68.0 °F | ISO 11359 |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | |
| Melting Point | 255 °C | 491 °F | 10K/min; ISO 3146 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Long Term |
| 240 °C | 464 °F | Short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -20.0 °C | -4.00 °F | |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| HB @Thickness 6.00 mm | HB @Thickness 0.236 in | ||