- 密度 [g/cm3]: 1.5
- 吸水率 [%]: 0.6
- 缺口冲击强度: 1.6
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Filler Content | 43 % | 43 % | |
| Water Absorption | 0.60 % | 0.60 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 100 | 100 | ASTM D785 |
| Tensile Strength at Break | 214 MPa | 31000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Unannealed; ASTM D648 |