- 密度 [g/cm3]: 1.46
- 缺口冲击强度: 12.0
- 弯曲模量 [MPa]: 12.0
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 220 MPa | 31900 psi | ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 | ||
| Tensile Modulus | 13.2 GPa | 1910 ksi | ISO 527 | ||
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -40.0 °C | 5.71 ft-lb/in² @Temperature -40.0 °F | ISO 180 | ||
| 14.0 kJ/m² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | ISO 180 | |||
| Charpy Impact Unnotched | 8.30 J/cm² @Temperature -30.0 °C | 39.5 ft-lb/in² @Temperature -22.0 °F | ISO 179 | ||
| 9.50 J/cm² @Temperature 23.0 °C | 45.2 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C | 5.23 ft-lb/in² @Temperature -22.0 °F | ISO 179 | ||
| 1.30 J/cm² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 3146 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 305 °C | 536 - 581 °F | |||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | >= 0.12 % | >= 0.12 % | |||
| Injection Pressure | 35.0 - 125 MPa | 5080 - 18100 psi | |||
| Descriptive Properties | |||||
| Color | BK 20560 | ||||
| Commercial Status | North America | ||||