- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.2
- 缺口冲击强度: 2.3
- 弯曲模量 [MPa]: 1.93
- 硬度: 115.0
- 热变形温度 [℃]: 229.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | ASTM D638 |
| Flexural Modulus | 1.93 GPa | 280 ksi | ASTM D790 |
| Izod Impact, Notched | 2.30 J/cm | 4.30 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 229 °C | 444 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Unannealed; ASTM D648 |