- 密度 [g/cm3]: 1.14
- 缺口冲击强度: 0.53
- 断裂伸长率 [%]: 114
- 弯曲强度 [MPa]: 83.0
- 弯曲模量 [MPa]: 2.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Yield Strength | 114 MPa | 16500 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 421 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 271 °C | 520 °F | |