- 密度 [g/cm3]: 1.22
- 缺口冲击强度: 1.33
- 断裂伸长率 [%]: 131
- 弯曲强度 [MPa]: 86.0
- 弯曲模量 [MPa]: 3.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 3.70 GPa | 537 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 279 °C | 534 °F | |