- 缺口冲击强度: 0.427
- 拉伸强度 [MPa]: 96.5
- 断裂伸长率 [%]: 152
- 弯曲模量 [MPa]: 4.62
- 热变形温度 [℃]: 243.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 96.5 MPa | 14000 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 4.62 GPa | 670 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Temperature 22.8 °C | 0.800 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 79.4 - 93.3 °C | 175 - 200 °F | |
| Dry Time | 2 - 4 hour @Temperature 71.1 °C | 2 - 4 hour @Temperature 160 °F | to eliminate surface defects |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm | |