- 缺口冲击强度: 1.6
- 拉伸强度 [MPa]: 51.7
- 断裂伸长率 [%]: 68.9
- 弯曲模量 [MPa]: 1.21
- 热变形温度 [℃]: 165.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Yield | 90 % | 90 % | ASTM D638 |
| Flexural Yield Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 1.21 GPa | 175 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Temperature 22.8 °C | 3.00 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 254 - 282 °C | 490 - 540 °F | |
| Middle Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Front Barrel Temperature | 266 - 293 °C | 510 - 560 °F | |
| Nozzle Temperature | 266 - 293 °C | 510 - 560 °F | |
| Melt Temperature | 266 - 288 °C | 510 - 550 °F | |
| Mold Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C | 2 - 4 hour @Temperature 175 °F | to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm | |