- 缺口冲击强度: 8.01
- 拉伸强度 [MPa]: 41.4
- 断裂伸长率 [%]: 55.2
- 弯曲模量 [MPa]: 1.52
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 41.4 MPa | 6000 psi | ASTM D638 |
| Flexural Yield Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 1.52 GPa | 220 ksi | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 22.8 °C | 15.0 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistivity per Square | 1.00e+11 ohm | 1.00e+11 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 238 - 266 °C | 460 - 510 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C | 2 - 4 hour @Temperature 175 °F | to ensure moisture content is less than 0.05% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm | |