- 缺口冲击强度: 9.6
- 拉伸强度 [MPa]: 48.0
- 弯曲模量 [MPa]: 1.71
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm @Thickness 3.17 mm | 0.014 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Modulus | 1.71 GPa | 248 ksi | ASTM D790 |
| Izod Impact, Notched | 9.60 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 18.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ASTM D648 |