- 吸水率 [%]: 1.2
- 缺口冲击强度: 8.01
- 拉伸强度 [MPa]: 50.3
- 弯曲模量 [MPa]: 1.65
- 硬度: 119.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hours Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 50.3 MPa | 7300 psi | ASTM D638 |
| Elongation at Break | 50 - 60 % | 50 - 60 % | ASTM D638 |
| Flexural Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 1.65 GPa | 240 ksi | ASTM D790 |
| Izod Impact, Notched | 8.01 - 9.08 J/cm | 15.0 - 17.0 ft-lb/in | 1/8 in specimen; ASTM D256 |
| NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | 1.33 - 1.60 J/cm | 2.50 - 3.00 ft-lb/in | ASTM D256 |
| 1.33 - 1.60 J/cm @Temperature -40.0 °C | 2.50 - 3.00 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | ASTM D648 |