  4. DuPont Performance Polymers Zytel® 101 NC010 Nylon 66

DuPont Performance Polymers Zytel® 101 NC010 Nylon 66

DuPont Performance Polymers Zytel® 101 NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 101 NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 101 NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 101 NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.14
  • 吸水率 [%]: 1.2
  • 缺口冲击强度: 0.27
  • 拉伸强度 [MPa]: 28.0
  • 弯曲模量 [MPa]: 0.414
  • 硬度: 108.0
  • 热变形温度 [℃]: 200.0
  • 脆化温度 [℃]: -80.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.14 g/cc1.14 g/ccDAM; ASTM D792
Density 1.14 g/cc0.0412 lb/in³DAM; ISO 1183
Water Absorption  1.2 %
@Temperature 23.0 °C		1.2 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 2.6 %
@Temperature 23.0 °C		2.6 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 8.5 %
@Temperature 23.0 °C		8.5 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 8.5 %
@Temperature 23.0 °C		8.5 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage 0.015 cm/cm
@Thickness 3.20 mm		0.015 in/in
@Thickness 0.126 in		Flow; DAM
Linear Mold Shrinkage, Flow 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
Melt Index of Compound 24 g/10 min
@Load 1.20 kg,
Temperature 275 °C		24 g/10 min
@Load 2.65 lb,
Temperature 527 °F		DAM; cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 595950%RH; ASTM D785
 7979DAM; ASTM D785
Hardness, Rockwell R 10810850%RH; ASTM D785
 121121DAM; ASTM D785
Tensile Strength  38.0 MPa
@Temperature 121 °C		5510 psi
@Temperature 250 °F		50%RH; ASTM D638
 41.0 MPa
@Temperature 77.0 °C		5950 psi
@Temperature 171 °F		50%RH; ASTM D638
 43.0 MPa
@Temperature 121 °C		6240 psi
@Temperature 250 °F		DAM; ASTM D638
 62.0 MPa
@Temperature 77.0 °C		8990 psi
@Temperature 171 °F		DAM; ASTM D638
 77.0 MPa
@Temperature 23.0 °C		11200 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		DAM; ASTM D638
 110 MPa
@Temperature -40.0 °C		16000 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 114 MPa
@Temperature -40.0 °C		16500 psi
@Temperature -40.0 °F		DAM; ASTM D638
Tensile Strength, Yield  28.0 MPa
@Temperature 121 °C		4060 psi
@Temperature 250 °F		50%RH; ASTM D638
 33.0 MPa
@Temperature 121 °C		4790 psi
@Temperature 250 °F		DAM; ASTM D638
 40.0 MPa
@Temperature 77.0 °C		5800 psi
@Temperature 171 °F		50%RH; ASTM D638
 45.0 MPa
@Temperature 77.0 °C		6530 psi
@Temperature 171 °F		DAM; ASTM D638
 55.0 MPa
@Temperature 23.0 °C		7980 psi
@Temperature 73.4 °F		50%RH; ISO 527
 58.0 MPa
@Temperature 23.0 °C		8410 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 82.0 MPa
@Temperature 23.0 °C		11900 psi
@Temperature 73.4 °F		DAM; ISO 527
 83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		DAM; ASTM D638
 110 MPa
@Temperature -40.0 °C		16000 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 114 MPa
@Temperature -40.0 °C		16500 psi
@Temperature -40.0 °F		DAM; ASTM D638
Elongation at Break  15 %
@Temperature -40.0 °C		15 %
@Temperature -40.0 °F		DAM; ASTM D638
 20 %
@Temperature -40.0 °C		20 %
@Temperature -40.0 °F		50%RH; ASTM D638
 25 %
@Temperature 23.0 °C		25 %
@Temperature 73.4 °F		DAM; nominal; ISO 527
 45 %
@Temperature 23.0 °C		45 %
@Temperature 73.4 °F		50mm/min; DAM; ISO 527
 >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 60 %
@Temperature 23.0 °C		60 %
@Temperature 73.4 °F		DAM; ASTM D638
 >= 300 %
@Temperature 23.0 °C		>= 300 %
@Temperature 73.4 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 77.0 °C		>= 300 %
@Temperature 171 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 77.0 °C		>= 300 %
@Temperature 171 °F		DAM; ASTM D638
 >= 300 %
@Temperature 121 °C		>= 300 %
@Temperature 250 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 121 °C		>= 300 %
@Temperature 250 °F		DAM; ASTM D638
Elongation at Yield  4.0 %
@Temperature -40.0 °C		4.0 %
@Temperature -40.0 °F		DAM; ASTM D638
 4.5 %
@Temperature 23.0 °C		4.5 %
@Temperature 73.4 °F		DAM; ISO 527
 5.0 %
@Temperature 23.0 °C		5.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 25 %
@Temperature 23.0 °C		25 %
@Temperature 73.4 °F		50%RH; ASTM D638
 25 %
@Temperature 23.0 °C		25 %
@Temperature 73.4 °F		50%RH; ISO 527
 30 %
@Temperature 77.0 °C		30 %
@Temperature 171 °F		50%RH; ASTM D638
 30 %
@Temperature 77.0 °C		30 %
@Temperature 171 °F		DAM; ASTM D638
 40 %
@Temperature 121 °C		40 %
@Temperature 250 °F		50%RH; ASTM D638
 45 %
@Temperature 121 °C		45 %
@Temperature 250 °F		DAM; ASTM D638
Tensile Modulus  1.40 GPa
@Temperature 23.0 °C		203 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 3.10 GPa
@Temperature 23.0 °C		450 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  0.414 GPa
@Temperature 121 °C		60.0 ksi
@Temperature 250 °F		50%RH; ASTM D790
 0.538 GPa
@Temperature 121 °C		78.0 ksi
@Temperature 250 °F		DAM; ASTM D790
 0.565 GPa
@Temperature 77.0 °C		81.9 ksi
@Temperature 171 °F		50%RH; ASTM D790
 0.689 GPa
@Temperature 77.0 °C		99.9 ksi
@Temperature 171 °F		DAM; ASTM D790
 1.20 GPa
@Temperature 23.0 °C		174 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 1.21 GPa
@Temperature 23.0 °C		175 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 2.80 GPa
@Temperature 23.0 °C		406 ksi
@Temperature 73.4 °F		DAM; ISO 178
 2.83 GPa
@Temperature 23.0 °C		410 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 3.241 GPa
@Temperature -40.0 °C		470.1 ksi
@Temperature -40.0 °F		DAM; ASTM D790
 3.447 GPa
@Temperature -40.0 °C		499.9 ksi
@Temperature -40.0 °F		50%RH; ASTM D790
Shear Strength 66.2 MPa
@Temperature 23.0 °C		9600 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  0.270 J/cm
@Temperature -40.0 °C		0.506 ft-lb/in
@Temperature -40.0 °F		50%RH; ASTM D256
 0.320 J/cm
@Temperature -40.0 °C		0.599 ft-lb/in
@Temperature -40.0 °F		DAM; ASTM D256
 0.530 J/cm
@Temperature 23.0 °C		0.993 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 1.12 J/cm
@Temperature 23.0 °C		2.10 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  5.50 kJ/m²
@Temperature -40.0 °C		2.62 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 5.50 kJ/m²
@Temperature -30.0 °C		2.62 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 5.50 kJ/m²
@Temperature 23.0 °C		2.62 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 12.0 kJ/m²
@Temperature 23.0 °C		5.71 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  300 kJ/m²
@Temperature -30.0 °C		143 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 180/1U
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 180/1U
Charpy Impact Unnotched  40.0 J/cm²
@Temperature -30.0 °C		190 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.300 J/cm²
@Temperature -40.0 °C		1.43 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.300 J/cm²
@Temperature -30.0 °C		1.43 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.450 J/cm²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.550 J/cm²
@Temperature 23.0 °C		2.62 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 1.50 J/cm²
@Temperature 23.0 °C		7.14 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Impact Strength  158 kJ/m²
@Temperature 23.0 °C		75.2 ft-lb/in²
@Temperature 73.4 °F		DAM; Short specimen; ASTM D1822
 232 kJ/m²
@Temperature 23.0 °C		110 ft-lb/in²
@Temperature 73.4 °F		50%RH; Short specimen; ASTM D1822
 504 kJ/m²
@Temperature 23.0 °C		240 ft-lb/in²
@Temperature 73.4 °F		DAM; Long specimen; ASTM D1822
 1470 kJ/m²
@Temperature 23.0 °C		699 ft-lb/in²
@Temperature 73.4 °F		50%RH; Long specimen; ASTM D1822
Tensile Creep Modulus, 1 hour 1200 MPa
@Temperature 23.0 °C		174000 psi
@Temperature 73.4 °F		50%RH; ISO 899
Tensile Creep Modulus, 1000 hours 700 MPa
@Temperature 23.0 °C		102000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		50%RH; ASTM D257
 1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; ASTM D257
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Dielectric Constant  3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.8
@Frequency 100 Hz,
Temperature 23.0 °C		3.8
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 3.9
@Frequency 1000 Hz,
Temperature 23.0 °C		3.9
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.0
@Frequency 100 Hz,
Temperature 23.0 °C		4.0
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 6.0
@Frequency 100 Hz,
Temperature 23.0 °C		6.0
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 7.0
@Frequency 1000 Hz,
Temperature 23.0 °C		7.0
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 8.0
@Frequency 100 Hz,
Temperature 23.0 °C		8.0
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
Dielectric Strength 18.1 kV/mm
@Thickness 3.20 mm		460 kV/in
@Thickness 0.126 in		DAM; Short Time; ASTM D149
Dissipation Factor  0.010
@Frequency 100 Hz,
Temperature 23.0 °C		0.010
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.10
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.10
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.20
@Frequency 100 Hz,
Temperature 23.0 °C		0.20
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.20
@Frequency 1000 Hz,
Temperature 23.0 °C		0.20
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
Comparative Tracking Index  >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
CTE, linear, Transverse to Flow 110 µm/m-°C
@Temperature 23.0 - 55.0 °C		61.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
Melting Point 262 °C504 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 200 °C392 °FDAM; ISO 75-1/-2
 210 °C410 °FDAM; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C149 °FDAM; ASTM D648
 70.0 °C158 °FDAM; ISO 75-1/-2
Brittleness Temperature -80.0 °C-112 °FDAM; ASTM D746
 -65.0 °C-85.0 °F50%RH; ASTM D746
UL RTI, Electrical  130 °C
@Thickness 0.710 mm		266 °F
@Thickness 0.0280 in		DAM; UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		DAM; UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		DAM; UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical with Impact  75.0 °C
@Thickness 0.710 mm		167 °F
@Thickness 0.0280 in		DAM; UL 746B
 75.0 °C
@Thickness 3.00 mm		167 °F
@Thickness 0.118 in		DAM; UL 746B
 75.0 °C
@Thickness 6.00 mm		167 °F
@Thickness 0.236 in		DAM; UL 746B
 75.0 °C
@Thickness 1.50 mm		167 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical without Impact  85.0 °C
@Thickness 0.710 mm		185 °F
@Thickness 0.0280 in		DAM; UL 746B
 85.0 °C
@Thickness 3.00 mm		185 °F
@Thickness 0.118 in		DAM; UL 746B
 85.0 °C
@Thickness 6.00 mm		185 °F
@Thickness 0.236 in		DAM; UL 746B
 85.0 °C
@Thickness 1.50 mm		185 °F
@Thickness 0.0591 in		DAM; UL 746B
Flammability, UL94  V-2
@Thickness 6.00 mm		V-2
@Thickness 0.236 in		DAM; IEC 60695-11-10
 V-2
@Thickness 0.710 mm		V-2
@Thickness 0.0280 in		DAM; IEC 60695-11-10
 V-2
@Thickness 1.50 mm		V-2
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; IEC 60695-11-10
 V-2
@Thickness 1.50 mm		V-2
@Thickness 0.0591 in		DAM; UL94
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; UL94
 V-2
@Thickness 6.00 mm		V-2
@Thickness 0.236 in		DAM; UL94
 V-2
@Thickness 0.710 mm		V-2
@Thickness 0.0280 in		DAM; UL94
Oxygen Index 28 %28 %DAM; ASTM D2863
 28 %28 %DAM; ISO 4589-1/-2
 31 %31 %50%RH; ASTM D2863
Glow Wire Test  725 °C
@Thickness 0.710 mm		1340 °F
@Thickness 0.0280 in		DAM; Ignition; IEC 60695-2-13
 750 °C
@Thickness 1.50 mm		1380 °F
@Thickness 0.0591 in		DAM; Ignition; IEC 60695-2-13
 800 °C
@Thickness 3.00 mm		1470 °F
@Thickness 0.118 in		DAM; Ignition; IEC 60695-2-13
 960 °C
@Thickness 0.710 mm		1760 °F
@Thickness 0.0280 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 1.50 mm		1760 °F
@Thickness 0.0591 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		DAM; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 290 °C554 °FDAM; Optimum
 280 - 300 °C536 - 572 °FDAM
Mold Temperature 70.0 °C158 °FDAM; optimum
 50.0 - 90.0 °C122 - 194 °FDAM
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
Extrudable - FilamentYesDAM
FeaturesChemical Resistance, GoodDAM
 Electrical Properties, GoodDAM
 Wear Resistance, GoodDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodExtrusionDAM
 Injection MoldingDAM
Product CategoryExtrusion ResinsDAM
 Unreinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45423.html

免责声明: 本文 DuPont Performance Polymers Zytel® 101 NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4