  3. PA66
  4. DuPont Performance Polymers Zytel® 101F NC010 Nylon 66

DuPont Performance Polymers Zytel® 101F NC010 Nylon 66

DuPont Performance Polymers Zytel® 101F NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 101F NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 101F NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 101F NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.14
  • 吸水率 [%]: 1.2
  • 缺口冲击强度: 0.32
  • 拉伸强度 [MPa]: 55.0
  • 弯曲模量 [MPa]: 0.500
  • 硬度: 113.0
  • 热变形温度 [℃]: 200.0
  • 脆化温度 [℃]: -80.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.14 g/cc1.14 g/ccDAM; ASTM D792
Density 1.14 g/cc0.0412 lb/in³DAM; ISO 1183
Water Absorption  1.2 %
@Temperature 23.0 °C		1.2 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 2.6 %
@Temperature 23.0 °C		2.6 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 8.5 %
@Temperature 23.0 °C		8.5 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 8.5 %
@Temperature 23.0 °C		8.5 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Viscosity  15000 cP
@Shear Rate 7000 1/s,
Temperature 315 °C		15000 cP
@Shear Rate 7000 1/s,
Temperature 599 °F		DAM; ISO 11443
 16000 cP
@Shear Rate 5000 1/s,
Temperature 315 °C		16000 cP
@Shear Rate 5000 1/s,
Temperature 599 °F		DAM; ISO 11443
 19000 cP
@Shear Rate 2000 1/s,
Temperature 315 °C		19000 cP
@Shear Rate 2000 1/s,
Temperature 599 °F		DAM; ISO 11443
 20000 cP
@Shear Rate 1000 1/s,
Temperature 315 °C		20000 cP
@Shear Rate 1000 1/s,
Temperature 599 °F		DAM; ISO 11443
 21000 cP
@Shear Rate 500 1/s,
Temperature 315 °C		21000 cP
@Shear Rate 500 1/s,
Temperature 599 °F		DAM; ISO 11443
 21000 cP
@Shear Rate 700 1/s,
Temperature 315 °C		21000 cP
@Shear Rate 700 1/s,
Temperature 599 °F		DAM; ISO 11443
 28000 cP
@Shear Rate 7000 1/s,
Temperature 295 °C		28000 cP
@Shear Rate 7000 1/s,
Temperature 563 °F		DAM; ISO 11443
 32000 cP
@Shear Rate 5000 1/s,
Temperature 295 °C		32000 cP
@Shear Rate 5000 1/s,
Temperature 563 °F		DAM; ISO 11443
 39000 cP
@Shear Rate 2000 1/s,
Temperature 295 °C		39000 cP
@Shear Rate 2000 1/s,
Temperature 563 °F		DAM; ISO 11443
 44000 cP
@Shear Rate 1000 1/s,
Temperature 295 °C		44000 cP
@Shear Rate 1000 1/s,
Temperature 563 °F		DAM; ISO 11443
 47000 cP
@Shear Rate 700 1/s,
Temperature 295 °C		47000 cP
@Shear Rate 700 1/s,
Temperature 563 °F		DAM; ISO 11443
 47000 cP
@Shear Rate 7000 1/s,
Temperature 275 °C		47000 cP
@Shear Rate 7000 1/s,
Temperature 527 °F		DAM; ISO 11443
 48000 cP
@Shear Rate 500 1/s,
Temperature 295 °C		48000 cP
@Shear Rate 500 1/s,
Temperature 563 °F		DAM; ISO 11443
 54000 cP
@Shear Rate 5000 1/s,
Temperature 275 °C		54000 cP
@Shear Rate 5000 1/s,
Temperature 527 °F		DAM; ISO 11443
 76000 cP
@Shear Rate 2000 1/s,
Temperature 275 °C		76000 cP
@Shear Rate 2000 1/s,
Temperature 527 °F		DAM; ISO 11443
 93000 cP
@Shear Rate 1000 1/s,
Temperature 275 °C		93000 cP
@Shear Rate 1000 1/s,
Temperature 527 °F		DAM; ISO 11443
 101000 cP
@Shear Rate 700 1/s,
Temperature 275 °C		101000 cP
@Shear Rate 700 1/s,
Temperature 527 °F		DAM; ISO 11443
 109000 cP
@Shear Rate 500 1/s,
Temperature 275 °C		109000 cP
@Shear Rate 500 1/s,
Temperature 527 °F		DAM; ISO 11443
Linear Mold Shrinkage 0.015 cm/cm
@Thickness 3.20 mm		0.015 in/in
@Thickness 0.126 in		Flow; DAM
Linear Mold Shrinkage, Flow 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 7171DAM; ASTM D785
Hardness, Rockwell R 113113DAM; ASTM D785
Tensile Strength  64.0 MPa
@Temperature 23.0 °C		9280 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  0.410 MPa
@Strain 0.100 %,
Temperature 150 °C		59.5 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.440 MPa
@Strain 0.100 %,
Temperature 150 °C		63.8 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 0.460 MPa
@Strain 0.100 %,
Temperature 120 °C		66.7 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 0.510 MPa
@Strain 0.100 %,
Temperature 120 °C		74.0 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.600 MPa
@Strain 0.100 %,
Temperature 100 °C		87.0 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 0.600 MPa
@Strain 0.100 %,
Temperature 100 °C		87.0 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 0.640 MPa
@Strain 0.100 %,
Temperature 80.0 °C		92.8 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 0.700 MPa
@Strain 0.100 %,
Temperature 60.0 °C		102 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 0.800 MPa
@Strain 0.200 %,
Temperature 150 °C		116 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.880 MPa
@Strain 0.200 %,
Temperature 150 °C		128 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 0.900 MPa
@Strain 0.100 %,
Temperature 80.0 °C		131 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 0.920 MPa
@Strain 0.200 %,
Temperature 120 °C		133 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 1.03 MPa
@Strain 0.200 %,
Temperature 120 °C		149 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 1.20 MPa
@Strain 0.200 %,
Temperature 100 °C		174 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 1.20 MPa
@Strain 0.200 %,
Temperature 100 °C		174 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 1.21 MPa
@Strain 0.300 %,
Temperature 150 °C		175 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 1.30 MPa
@Strain 0.300 %,
Temperature 150 °C		189 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 1.30 MPa
@Strain 0.200 %,
Temperature 80.0 °C		189 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 1.40 MPa
@Strain 0.200 %,
Temperature 60.0 °C		203 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 1.41 MPa
@Strain 0.300 %,
Temperature 120 °C		205 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 1.45 MPa
@Strain 0.400 %,
Temperature 150 °C		210 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 1.51 MPa
@Strain 0.300 %,
Temperature 120 °C		219 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 1.60 MPa
@Strain 0.100 %,
Temperature 23.0 °C		232 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 1.66 MPa
@Strain 0.400 %,
Temperature 150 °C		241 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 1.73 MPa
@Strain 0.300 %,
Temperature 100 °C		251 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 1.75 MPa
@Strain 0.400 %,
Temperature 120 °C		254 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 1.75 MPa
@Strain 0.300 %,
Temperature 100 °C		254 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 1.76 MPa
@Strain 0.200 %,
Temperature 80.0 °C		255 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 1.83 MPa
@Strain 0.400 %,
Temperature 120 °C		265 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 1.89 MPa
@Strain 0.300 %,
Temperature 80.0 °C		274 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 1.90 MPa
@Strain 0.100 %,
Temperature 60.0 °C		276 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 2.01 MPa
@Strain 0.500 %,
Temperature 150 °C		292 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.08 MPa
@Strain 0.400 %,
Temperature 100 °C		302 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 2.08 MPa
@Strain 0.300 %,
Temperature 60.0 °C		302 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 2.15 MPa
@Strain 0.400 %,
Temperature 100 °C		312 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 2.29 MPa
@Strain 0.600 %,
Temperature 150 °C		332 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.31 MPa
@Strain 0.400 %,
Temperature 80.0 °C		335 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.34 MPa
@Strain 0.500 %,
Temperature 120 °C		339 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.34 MPa
@Strain 0.500 %,
Temperature 120 °C		339 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.37 MPa
@Strain 0.500 %,
Temperature 150 °C		344 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.56 MPa
@Strain 0.400 %,
Temperature 60.0 °C		371 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 2.68 MPa
@Strain 0.500 %,
Temperature 100 °C		389 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 2.69 MPa
@Strain 0.300 %,
Temperature 80.0 °C		390 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 2.73 MPa
@Strain 0.700 %,
Temperature 150 °C		396 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.80 MPa
@Strain 0.100 %,
Temperature 0.000 °C		406 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 2.84 MPa
@Strain 0.600 %,
Temperature 120 °C		412 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.84 MPa
@Strain 0.500 %,
Temperature 100 °C		412 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 2.90 MPa
@Strain 0.100 %,
Temperature 23.0 °C		421 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 2.98 MPa
@Strain 0.600 %,
Temperature 120 °C		432 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 3.02 MPa
@Strain 0.700 %,
Temperature 150 °C		438 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.07 MPa
@Strain 0.800 %,
Temperature 150 °C		445 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.15 MPa
@Strain 0.500 %,
Temperature 80.0 °C		457 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 3.16 MPa
@Strain 0.200 %,
Temperature 23.0 °C		458 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 3.20 MPa
@Strain 0.100 %,
Temperature 0.000 °C		464 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 3.23 MPa
@Strain 0.600 %,
Temperature 100 °C		468 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 3.30 MPa
@Strain 0.100 %,
Temperature -40.0 °C		479 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 3.35 MPa
@Strain 0.700 %,
Temperature 120 °C		486 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.40 MPa
@Strain 0.400 %,
Temperature 80.0 °C		493 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 3.45 MPa
@Strain 0.700 %,
Temperature 120 °C		500 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 3.49 MPa
@Strain 0.600 %,
Temperature 100 °C		506 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 3.51 MPa
@Strain 0.900 %,
Temperature 150 °C		509 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.57 MPa
@Strain 0.500 %,
Temperature 60.0 °C		518 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 3.62 MPa
@Strain 0.900 %,
Temperature 150 °C		525 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.72 MPa
@Strain 0.200 %,
Temperature 60.0 °C		540 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 3.74 MPa
@Strain 0.700 %,
Temperature 100 °C		542 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 3.76 MPa
@Strain 0.600 %,
Temperature 80.0 °C		545 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 3.79 MPa
@Strain 0.800 %,
Temperature 120 °C		550 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.85 MPa
@Strain 1.00 %,
Temperature 150 °C		558 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.91 MPa
@Strain 0.800 %,
Temperature 120 °C		567 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.06 MPa
@Strain 0.100 %,
Temperature -40.0 °C		589 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 4.09 MPa
@Strain 0.700 %,
Temperature 100 °C		593 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 4.09 MPa
@Strain 1.00 %,
Temperature 150 °C		593 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.21 MPa
@Strain 0.600 %,
Temperature 60.0 °C		611 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 4.24 MPa
@Strain 0.900 %,
Temperature 120 °C		615 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.24 MPa
@Strain 1.10 %,
Temperature 150 °C		615 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.35 MPa
@Strain 0.700 %,
Temperature 80.0 °C		631 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 4.43 MPa
@Strain 0.800 %,
Temperature 100 °C		643 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 4.50 MPa
@Strain 1.00 %,
Temperature 120 °C		653 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.50 MPa
@Strain 0.500 %,
Temperature 80.0 °C		653 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 4.51 MPa
@Strain 1.10 %,
Temperature 150 °C		654 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.56 MPa
@Strain 0.300 %,
Temperature 23.0 °C		661 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 4.57 MPa
@Strain 1.20 %,
Temperature 150 °C		663 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.62 MPa
@Strain 0.800 %,
Temperature 100 °C		670 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 4.79 MPa
@Strain 1.00 %,
Temperature 120 °C		695 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.85 MPa
@Strain 1.30 %,
Temperature 150 °C		703 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.85 MPa
@Strain 1.10 %,
Temperature 120 °C		703 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.85 MPa
@Strain 0.800 %,
Temperature 80.0 °C		703 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 4.91 MPa
@Strain 0.700 %,
Temperature 60.0 °C		712 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 4.98 MPa
@Strain 1.20 %,
Temperature 150 °C		722 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.07 MPa
@Strain 0.900 %,
Temperature 100 °C		735 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.19 MPa
@Strain 1.10 %,
Temperature 120 °C		753 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.19 MPa
@Strain 1.40 %,
Temperature 150 °C		753 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.19 MPa
@Strain 0.900 %,
Temperature 80.0 °C		753 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 5.21 MPa
@Strain 0.900 %,
Temperature 100 °C		756 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.28 MPa
@Strain 1.30 %,
Temperature 150 °C		766 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.32 MPa
@Strain 0.600 %,
Temperature 80.0 °C		772 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 5.32 MPa
@Strain 0.400 %,
Temperature 23.0 °C		772 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 5.35 MPa
@Strain 0.800 %,
Temperature 60.0 °C		776 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.35 MPa
@Strain 1.00 %,
Temperature 100 °C		776 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.43 MPa
@Strain 1.20 %,
Temperature 120 °C		788 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.52 MPa
@Strain 1.20 %,
Temperature 120 °C		801 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.52 MPa
@Strain 1.50 %,
Temperature 150 °C		801 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.61 MPa
@Strain 0.200 %,
Temperature 0.000 °C		814 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 5.63 MPa
@Strain 0.300 %,
Temperature 60.0 °C		817 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 5.63 MPa
@Strain 1.00 %,
Temperature 80.0 °C		817 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 5.63 MPa
@Strain 1.40 %,
Temperature 150 °C		817 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.78 MPa
@Strain 0.200 %,
Temperature 23.0 °C		838 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 5.80 MPa
@Strain 1.10 %,
Temperature 100 °C		841 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.80 MPa
@Strain 1.00 %,
Temperature 100 °C		841 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.85 MPa
@Strain 1.60 %,
Temperature 150 °C		848 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.90 MPa
@Strain 1.30 %,
Temperature 120 °C		856 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.97 MPa
@Strain 1.30 %,
Temperature 120 °C		866 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.08 MPa
@Strain 0.700 %,
Temperature 80.0 °C		882 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 6.08 MPa
@Strain 0.900 %,
Temperature 60.0 °C		882 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 6.11 MPa
@Strain 1.50 %,
Temperature 150 °C		886 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.19 MPa
@Strain 1.70 %,
Temperature 150 °C		898 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.22 MPa
@Strain 1.10 %,
Temperature 100 °C		902 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 6.25 MPa
@Strain 1.40 %,
Temperature 120 °C		906 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 6.30 MPa
@Strain 1.20 %,
Temperature 100 °C		914 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 6.31 MPa
@Strain 0.200 %,
Temperature 0.000 °C		915 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 6.36 MPa
@Strain 1.10 %,
Temperature 80.0 °C		922 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.40 MPa
@Strain 1.60 %,
Temperature 150 °C		928 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.41 MPa
@Strain 1.40 %,
Temperature 120 °C		930 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.52 MPa
@Strain 1.80 %,
Temperature 150 °C		946 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.52 MPa
@Strain 0.200 %,
Temperature -40.0 °C		946 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 6.53 MPa
@Strain 1.00 %,
Temperature 60.0 °C		947 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 6.69 MPa
@Strain 1.30 %,
Temperature 100 °C		970 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 6.70 MPa
@Strain 1.70 %,
Temperature 150 °C		972 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.72 MPa
@Strain 1.50 %,
Temperature 120 °C		975 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 6.75 MPa
@Strain 1.50 %,
Temperature 120 °C		979 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.80 MPa
@Strain 1.90 %,
Temperature 150 °C		986 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.81 MPa
@Strain 1.20 %,
Temperature 100 °C		988 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 6.89 MPa
@Strain 0.800 %,
Temperature 80.0 °C		999 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 6.92 MPa
@Strain 1.20 %,
Temperature 80.0 °C		1000 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.92 MPa
@Strain 0.400 %,
Temperature 60.0 °C		1000 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 7.03 MPa
@Strain 1.10 %,
Temperature 60.0 °C		1020 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.03 MPa
@Strain 2.10 %,
Temperature 150 °C		1020 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.13 MPa
@Strain 1.60 %,
Temperature 120 °C		1030 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.14 MPa
@Strain 1.60 %,
Temperature 120 °C		1040 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.19 MPa
@Strain 1.40 %,
Temperature 100 °C		1040 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.23 MPa
@Strain 1.80 %,
Temperature 150 °C		1050 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.31 MPa
@Strain 1.30 %,
Temperature 80.0 °C		1060 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.40 MPa
@Strain 1.30 %,
Temperature 100 °C		1070 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.42 MPa
@Strain 2.20 %,
Temperature 150 °C		1080 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.44 MPa
@Strain 0.500 %,
Temperature 23.0 °C		1080 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 7.53 MPa
@Strain 1.90 %,
Temperature 150 °C		1090 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.58 MPa
@Strain 1.70 %,
Temperature 120 °C		1100 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.61 MPa
@Strain 1.20 %,
Temperature 60.0 °C		1100 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.64 MPa
@Strain 1.50 %,
Temperature 100 °C		1110 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.65 MPa
@Strain 1.70 %,
Temperature 120 °C		1110 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.75 MPa
@Strain 2.30 %,
Temperature 150 °C		1120 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.77 MPa
@Strain 0.900 %,
Temperature 80.0 °C		1130 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 7.83 MPa
@Strain 2.00 %,
Temperature 150 °C		1140 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.83 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1140 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 7.86 MPa
@Strain 1.40 %,
Temperature 80.0 °C		1140 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.88 MPa
@Strain 1.40 %,
Temperature 100 °C		1140 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.92 MPa
@Strain 1.80 %,
Temperature 120 °C		1150 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.03 MPa
@Strain 2.40 %,
Temperature 150 °C		1160 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.12 MPa
@Strain 1.80 %,
Temperature 120 °C		1180 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.14 MPa
@Strain 1.60 %,
Temperature 100 °C		1180 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 8.18 MPa
@Strain 2.10 %,
Temperature 150 °C		1190 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.20 MPa
@Strain 1.30 %,
Temperature 60.0 °C		1190 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.31 MPa
@Strain 1.90 %,
Temperature 120 °C		1210 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.31 MPa
@Strain 2.50 %,
Temperature 150 °C		1210 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.34 MPa
@Strain 1.50 %,
Temperature 80.0 °C		1210 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.35 MPa
@Strain 1.50 %,
Temperature 100 °C		1210 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.47 MPa
@Strain 1.90 %,
Temperature 120 °C		1230 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.48 MPa
@Strain 2.20 %,
Temperature 150 °C		1230 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.53 MPa
@Strain 1.00 %,
Temperature 80.0 °C		1240 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 8.59 MPa
@Strain 2.60 %,
Temperature 150 °C		1250 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.59 MPa
@Strain 1.70 %,
Temperature 100 °C		1250 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 8.71 MPa
@Strain 1.60 %,
Temperature 100 °C		1260 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.75 MPa
@Strain 2.00 %,
Temperature 120 °C		1270 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.78 MPa
@Strain 0.300 %,
Temperature 0.000 °C		1270 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 8.81 MPa
@Strain 1.40 %,
Temperature 60.0 °C		1280 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.82 MPa
@Strain 2.10 %,
Temperature 120 °C		1280 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.84 MPa
@Strain 1.60 %,
Temperature 80.0 °C		1280 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.86 MPa
@Strain 0.500 %,
Temperature 60.0 °C		1290 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 8.87 MPa
@Strain 0.300 %,
Temperature 23.0 °C		1290 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 8.89 MPa
@Strain 2.30 %,
Temperature 150 °C		1290 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.92 MPa
@Strain 2.70 %,
Temperature 150 °C		1290 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.03 MPa
@Strain 1.80 %,
Temperature 100 °C		1310 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.07 MPa
@Strain 2.40 %,
Temperature 150 °C		1320 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.09 MPa
@Strain 2.10 %,
Temperature 120 °C		1320 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.14 MPa
@Strain 2.80 %,
Temperature 150 °C		1330 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.15 MPa
@Strain 0.600 %,
Temperature 23.0 °C		1330 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 9.23 MPa
@Strain 1.10 %,
Temperature 80.0 °C		1340 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.24 MPa
@Strain 1.70 %,
Temperature 100 °C		1340 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.29 MPa
@Strain 2.20 %,
Temperature 120 °C		1350 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.31 MPa
@Strain 1.70 %,
Temperature 80.0 °C		1350 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.34 MPa
@Strain 1.50 %,
Temperature 60.0 °C		1350 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 9.37 MPa
@Strain 2.90 %,
Temperature 150 °C		1360 psi
@Strain 2.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.42 MPa
@Strain 2.20 %,
Temperature 120 °C		1370 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.42 MPa
@Strain 1.90 %,
Temperature 100 °C		1370 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.43 MPa
@Strain 2.50 %,
Temperature 150 °C		1370 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.64 MPa
@Strain 2.30 %,
Temperature 120 °C		1400 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.65 MPa
@Strain 1.80 %,
Temperature 100 °C		1400 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.70 MPa
@Strain 2.40 %,
Temperature 120 °C		1410 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.76 MPa
@Strain 3.00 %,
Temperature 150 °C		1420 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.76 MPa
@Strain 2.00 %,
Temperature 100 °C		1420 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.78 MPa
@Strain 2.60 %,
Temperature 150 °C		1420 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.81 MPa
@Strain 0.300 %,
Temperature 0.000 °C		1420 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 9.82 MPa
@Strain 1.60 %,
Temperature 60.0 °C		1420 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 9.84 MPa
@Strain 0.300 %,
Temperature -40.0 °C		1430 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 9.84 MPa
@Strain 1.80 %,
Temperature 80.0 °C		1430 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.87 MPa
@Strain 3.10 %,
Temperature 150 °C		1430 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.93 MPa
@Strain 2.40 %,
Temperature 120 °C		1440 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.99 MPa
@Strain 1.20 %,
Temperature 80.0 °C		1450 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 10.08 MPa
@Strain 2.70 %,
Temperature 150 °C		1462 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.09 MPa
@Strain 2.50 %,
Temperature 120 °C		1463 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.13 MPa
@Strain 1.90 %,
Temperature 100 °C		1469 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.15 MPa
@Strain 3.30 %,
Temperature 150 °C		1472 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.26 MPa
@Strain 2.10 %,
Temperature 100 °C		1488 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.37 MPa
@Strain 2.60 %,
Temperature 120 °C		1504 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.38 MPa
@Strain 0.700 %,
Temperature 23.0 °C		1505 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 10.4 MPa
@Strain 2.50 %,
Temperature 120 °C		1510 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.43 MPa
@Strain 3.40 %,
Temperature 150 °C		1513 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.43 MPa
@Strain 1.70 %,
Temperature 60.0 °C		1513 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 10.44 MPa
@Strain 2.90 %,
Temperature 150 °C		1514 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.49 MPa
@Strain 0.600 %,
Temperature 60.0 °C		1521 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 10.51 MPa
@Strain 2.00 %,
Temperature 80.0 °C		1524 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 10.58 MPa
@Strain 1.30 %,
Temperature 80.0 °C		1535 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 10.6 MPa
@Strain 2.00 %,
Temperature 100 °C		1540 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.65 MPa
@Strain 2.20 %,
Temperature 100 °C		1545 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.65 MPa
@Strain 3.50 %,
Temperature 150 °C		1545 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.75 MPa
@Strain 2.60 %,
Temperature 120 °C		1559 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.76 MPa
@Strain 2.70 %,
Temperature 120 °C		1561 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.87 MPa
@Strain 3.60 %,
Temperature 150 °C		1577 psi
@Strain 3.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.91 MPa
@Strain 3.10 %,
Temperature 150 °C		1582 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.93 MPa
@Strain 2.10 %,
Temperature 80.0 °C		1585 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 10.98 MPa
@Strain 2.70 %,
Temperature 120 °C		1593 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.99 MPa
@Strain 1.80 %,
Temperature 60.0 °C		1594 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.02 MPa
@Strain 2.10 %,
Temperature 100 °C		1598 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.09 MPa
@Strain 2.30 %,
Temperature 100 °C		1608 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.09 MPa
@Strain 3.20 %,
Temperature 150 °C		1608 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.1 MPa
@Strain 2.80 %,
Temperature 120 °C		1610 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.15 MPa
@Strain 3.70 %,
Temperature 150 °C		1617 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.22 MPa
@Strain 1.40 %,
Temperature 80.0 °C		1627 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.32 MPa
@Strain 3.80 %,
Temperature 150 °C		1642 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.35 MPa
@Strain 0.400 %,
Temperature 23.0 °C		1646 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 11.38 MPa
@Strain 1.90 %,
Temperature 60.0 °C		1651 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.39 MPa
@Strain 2.80 %,
Temperature 120 °C		1652 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.41 MPa
@Strain 2.20 %,
Temperature 80.0 °C		1655 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.43 MPa
@Strain 2.30 %,
Temperature 100 °C		1658 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.43 MPa
@Strain 2.90 %,
Temperature 120 °C		1658 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.44 MPa
@Strain 3.30 %,
Temperature 150 °C		1659 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.48 MPa
@Strain 2.50 %,
Temperature 100 °C		1665 psi
@Strain 2.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.54 MPa
@Strain 3.90 %,
Temperature 150 °C		1674 psi
@Strain 3.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.63 MPa
@Strain 0.400 %,
Temperature 0.000 °C		1687 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 11.65 MPa
@Strain 3.00 %,
Temperature 120 °C		1690 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.68 MPa
@Strain 3.40 %,
Temperature 150 °C		1694 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.69 MPa
@Strain 0.800 %,
Temperature 23.0 °C		1695 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 11.71 MPa
@Strain 2.00 %,
Temperature 60.0 °C		1698 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.74 MPa
@Strain 2.90 %,
Temperature 120 °C		1703 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.76 MPa
@Strain 4.00 %,
Temperature 150 °C		1706 psi
@Strain 4.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.8 MPa
@Strain 1.50 %,
Temperature 80.0 °C		1710 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.82 MPa
@Strain 2.60 %,
Temperature 100 °C		1714 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.82 MPa
@Strain 2.30 %,
Temperature 80.0 °C		1714 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.85 MPa
@Strain 2.40 %,
Temperature 100 °C		1719 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.88 MPa
@Strain 4.10 %,
Temperature 150 °C		1723 psi
@Strain 4.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.92 MPa
@Strain 3.50 %,
Temperature 150 °C		1729 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.94 MPa
@Strain 0.300 %,
Temperature -40.0 °C		1732 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 11.99 MPa
@Strain 3.10 %,
Temperature 120 °C		1739 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.09 MPa
@Strain 3.00 %,
Temperature 120 °C		1754 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.13 MPa
@Strain 0.400 %,
Temperature 0.000 °C		1759 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 12.15 MPa
@Strain 0.700 %,
Temperature 60.0 °C		1762 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 12.2 MPa
@Strain 2.50 %,
Temperature 100 °C		1770 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.21 MPa
@Strain 2.70 %,
Temperature 100 °C		1771 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.21 MPa
@Strain 4.30 %,
Temperature 150 °C		1771 psi
@Strain 4.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.22 MPa
@Strain 3.60 %,
Temperature 150 °C		1772 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.24 MPa
@Strain 2.10 %,
Temperature 60.0 °C		1775 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.27 MPa
@Strain 2.40 %,
Temperature 80.0 °C		1780 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.32 MPa
@Strain 3.20 %,
Temperature 120 °C		1787 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.32 MPa
@Strain 4.40 %,
Temperature 150 °C		1787 psi
@Strain 4.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.44 MPa
@Strain 3.10 %,
Temperature 120 °C		1804 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.5 MPa
@Strain 1.60 %,
Temperature 80.0 °C		1810 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.51 MPa
@Strain 3.70 %,
Temperature 150 °C		1814 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.54 MPa
@Strain 2.80 %,
Temperature 100 °C		1819 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.56 MPa
@Strain 2.60 %,
Temperature 100 °C		1822 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.6 MPa
@Strain 3.30 %,
Temperature 120 °C		1830 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.6 MPa
@Strain 4.50 %,
Temperature 150 °C		1830 psi
@Strain 4.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.61 MPa
@Strain 2.50 %,
Temperature 80.0 °C		1829 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.63 MPa
@Strain 3.80 %,
Temperature 150 °C		1832 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.74 MPa
@Strain 3.30 %,
Temperature 120 °C		1848 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.74 MPa
@Strain 2.20 %,
Temperature 60.0 °C		1848 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.75 MPa
@Strain 0.400 %,
Temperature -40.0 °C		1849 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 12.77 MPa
@Strain 4.60 %,
Temperature 150 °C		1852 psi
@Strain 4.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.87 MPa
@Strain 3.90 %,
Temperature 150 °C		1867 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.88 MPa
@Strain 3.50 %,
Temperature 120 °C		1868 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.88 MPa
@Strain 2.60 %,
Temperature 80.0 °C		1868 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.9 MPa
@Strain 0.900 %,
Temperature 23.0 °C		1870 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 12.93 MPa
@Strain 2.90 %,
Temperature 100 °C		1875 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.94 MPa
@Strain 4.70 %,
Temperature 150 °C		1877 psi
@Strain 4.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.03 MPa
@Strain 3.40 %,
Temperature 120 °C		1890 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.03 MPa
@Strain 2.70 %,
Temperature 100 °C		1890 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.09 MPa
@Strain 1.70 %,
Temperature 80.0 °C		1899 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 13.1 MPa
@Strain 4.80 %,
Temperature 150 °C		1900 psi
@Strain 4.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.1 MPa
@Strain 3.60 %,
Temperature 120 °C		1900 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.1 MPa
@Strain 4.00 %,
Temperature 150 °C		1900 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.21 MPa
@Strain 4.90 %,
Temperature 150 °C		1916 psi
@Strain 4.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.25 MPa
@Strain 2.30 %,
Temperature 60.0 °C		1922 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 13.27 MPa
@Strain 3.00 %,
Temperature 100 °C		1925 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.32 MPa
@Strain 3.50 %,
Temperature 120 °C		1932 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.33 MPa
@Strain 2.70 %,
Temperature 80.0 °C		1933 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.34 MPa
@Strain 4.10 %,
Temperature 150 °C		1935 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.38 MPa
@Strain 3.70 %,
Temperature 120 °C		1941 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.39 MPa
@Strain 2.80 %,
Temperature 100 °C		1942 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.52 MPa
@Strain 4.20 %,
Temperature 150 °C		1961 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.61 MPa
@Strain 3.60 %,
Temperature 120 °C		1974 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.61 MPa
@Strain 1.80 %,
Temperature 80.0 °C		1974 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 13.66 MPa
@Strain 3.10 %,
Temperature 100 °C		1981 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.66 MPa
@Strain 3.80 %,
Temperature 120 °C		1981 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.69 MPa
@Strain 2.40 %,
Temperature 60.0 °C		1986 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 13.7 MPa
@Strain 0.800 %,
Temperature 60.0 °C		1990 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 13.72 MPa
@Strain 2.80 %,
Temperature 80.0 °C		1990 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.74 MPa
@Strain 2.90 %,
Temperature 100 °C		1993 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.76 MPa
@Strain 4.30 %,
Temperature 150 °C		1996 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.88 MPa
@Strain 3.90 %,
Temperature 120 °C		2013 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.9 MPa
@Strain 5.40 %,
Temperature 150 °C		2020 psi
@Strain 5.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.94 MPa
@Strain 4.40 %,
Temperature 150 °C		2022 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.96 MPa
@Strain 3.70 %,
Temperature 120 °C		2025 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.99 MPa
@Strain 3.20 %,
Temperature 100 °C		2029 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.0 MPa
@Strain 1.00 %,
Temperature 23.0 °C		2030 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 14.11 MPa
@Strain 2.90 %,
Temperature 80.0 °C		2046 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.14 MPa
@Strain 2.50 %,
Temperature 60.0 °C		2051 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.15 MPa
@Strain 3.00 %,
Temperature 100 °C		2052 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.16 MPa
@Strain 4.00 %,
Temperature 120 °C		2054 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.17 MPa
@Strain 4.60 %,
Temperature 150 °C		2055 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.26 MPa
@Strain 3.80 %,
Temperature 120 °C		2068 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.27 MPa
@Strain 3.30 %,
Temperature 100 °C		2070 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.39 MPa
@Strain 3.10 %,
Temperature 100 °C		2087 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.4 MPa
@Strain 2.00 %,
Temperature 80.0 °C		2090 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 14.41 MPa
@Strain 4.70 %,
Temperature 150 °C		2090 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.44 MPa
@Strain 4.10 %,
Temperature 120 °C		2094 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.49 MPa
@Strain 3.90 %,
Temperature 120 °C		2102 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.5 MPa
@Strain 2.60 %,
Temperature 60.0 °C		2100 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.53 MPa
@Strain 4.80 %,
Temperature 150 °C		2107 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.56 MPa
@Strain 3.00 %,
Temperature 80.0 °C		2112 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.66 MPa
@Strain 3.50 %,
Temperature 100 °C		2126 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.71 MPa
@Strain 4.90 %,
Temperature 150 °C		2134 psi
@Strain 4.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.71 MPa
@Strain 5.90 %,
Temperature 150 °C		2134 psi
@Strain 5.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.72 MPa
@Strain 4.00 %,
Temperature 120 °C		2135 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.78 MPa
@Strain 3.10 %,
Temperature 80.0 °C		2144 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.78 MPa
@Strain 4.30 %,
Temperature 120 °C		2144 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.78 MPa
@Strain 0.400 %,
Temperature -40.0 °C		2144 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 14.81 MPa
@Strain 3.20 %,
Temperature 100 °C		2148 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.81 MPa
@Strain 2.70 %,
Temperature 60.0 °C		2148 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.88 MPa
@Strain 5.00 %,
Temperature 150 °C		2158 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.89 MPa
@Strain 4.40 %,
Temperature 120 °C		2160 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.94 MPa
@Strain 3.60 %,
Temperature 100 °C		2167 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.02 MPa
@Strain 4.20 %,
Temperature 120 °C		2178 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.06 MPa
@Strain 3.20 %,
Temperature 80.0 °C		2184 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.1 MPa
@Strain 3.30 %,
Temperature 100 °C		2190 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.11 MPa
@Strain 4.50 %,
Temperature 120 °C		2192 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.12 MPa
@Strain 0.500 %,
Temperature 23.0 °C		2193 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 15.15 MPa
@Strain 1.10 %,
Temperature 23.0 °C		2197 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 15.19 MPa
@Strain 2.20 %,
Temperature 80.0 °C		2203 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.27 MPa
@Strain 3.70 %,
Temperature 100 °C		2215 psi
@Strain 3.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.28 MPa
@Strain 6.40 %,
Temperature 150 °C		2216 psi
@Strain 6.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.31 MPa
@Strain 2.80 %,
Temperature 60.0 °C		2221 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 15.37 MPa
@Strain 4.30 %,
Temperature 120 °C		2229 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.39 MPa
@Strain 4.60 %,
Temperature 120 °C		2232 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.4 MPa
@Strain 3.40 %,
Temperature 100 °C		2230 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.44 MPa
@Strain 3.80 %,
Temperature 100 °C		2239 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.48 MPa
@Strain 3.30 %,
Temperature 80.0 °C		2245 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.5 MPa
@Strain 4.70 %,
Temperature 120 °C		2250 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.52 MPa
@Strain 0.500 %,
Temperature 0.000 °C		2251 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 15.53 MPa
@Strain 5.50 %,
Temperature 150 °C		2252 psi
@Strain 5.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.54 MPa
@Strain 4.40 %,
Temperature 120 °C		2254 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.6 MPa
@Strain 2.30 %,
Temperature 80.0 °C		2260 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.7 MPa
@Strain 2.90 %,
Temperature 60.0 °C		2280 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 15.71 MPa
@Strain 0.900 %,
Temperature 60.0 °C		2279 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 15.73 MPa
@Strain 3.40 %,
Temperature 80.0 °C		2281 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.75 MPa
@Strain 3.50 %,
Temperature 100 °C		2284 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.75 MPa
@Strain 6.90 %,
Temperature 150 °C		2284 psi
@Strain 6.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.77 MPa
@Strain 4.50 %,
Temperature 120 °C		2287 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.78 MPa
@Strain 4.80 %,
Temperature 120 °C		2289 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.83 MPa
@Strain 3.90 %,
Temperature 100 °C		2296 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.0 MPa
@Strain 4.90 %,
Temperature 120 °C		2320 psi
@Strain 4.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.01 MPa
@Strain 4.60 %,
Temperature 120 °C		2322 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.01 MPa
@Strain 2.40 %,
Temperature 80.0 °C		2322 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.12 MPa
@Strain 3.00 %,
Temperature 60.0 °C		2338 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.12 MPa
@Strain 3.50 %,
Temperature 80.0 °C		2338 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.17 MPa
@Strain 3.60 %,
Temperature 100 °C		2345 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.2 MPa
@Strain 1.20 %,
Temperature 23.0 °C		2350 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 16.22 MPa
@Strain 4.00 %,
Temperature 100 °C		2353 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.24 MPa
@Strain 4.70 %,
Temperature 120 °C		2355 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.35 MPa
@Strain 7.40 %,
Temperature 150 °C		2371 psi
@Strain 7.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.41 MPa
@Strain 3.80 %,
Temperature 100 °C		2380 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.43 MPa
@Strain 6.00 %,
Temperature 150 °C		2383 psi
@Strain 6.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.45 MPa
@Strain 4.10 %,
Temperature 100 °C		2386 psi
@Strain 4.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.47 MPa
@Strain 0.500 %,
Temperature 0.000 °C		2389 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 16.48 MPa
@Strain 2.50 %,
Temperature 80.0 °C		2390 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.48 MPa
@Strain 4.80 %,
Temperature 120 °C		2390 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.62 MPa
@Strain 3.10 %,
Temperature 60.0 °C		2411 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.68 MPa
@Strain 3.70 %,
Temperature 80.0 °C		2419 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.68 MPa
@Strain 5.40 %,
Temperature 120 °C		2419 psi
@Strain 5.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.72 MPa
@Strain 0.500 %,
Temperature -40.0 °C		2425 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 16.72 MPa
@Strain 4.20 %,
Temperature 100 °C		2425 psi
@Strain 4.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.76 MPa
@Strain 3.90 %,
Temperature 100 °C		2431 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.77 MPa
@Strain 4.90 %,
Temperature 120 °C		2432 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.84 MPa
@Strain 7.90 %,
Temperature 150 °C		2442 psi
@Strain 7.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.84 MPa
@Strain 3.20 %,
Temperature 60.0 °C		2442 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.89 MPa
@Strain 2.60 %,
Temperature 80.0 °C		2450 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.89 MPa
@Strain 4.40 %,
Temperature 100 °C		2450 psi
@Strain 4.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.96 MPa
@Strain 3.80 %,
Temperature 80.0 °C		2460 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.0 MPa
@Strain 4.00 %,
Temperature 100 °C		2470 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.09 MPa
@Strain 6.50 %,
Temperature 150 °C		2479 psi
@Strain 6.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.15 MPa
@Strain 3.30 %,
Temperature 60.0 °C		2487 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.19 MPa
@Strain 1.00 %,
Temperature 60.0 °C		2493 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 17.19 MPa
@Strain 1.30 %,
Temperature 23.0 °C		2493 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 17.23 MPa
@Strain 4.10 %,
Temperature 100 °C		2499 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.23 MPa
@Strain 4.50 %,
Temperature 100 °C		2499 psi
@Strain 4.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.24 MPa
@Strain 8.40 %,
Temperature 150 °C		2500 psi
@Strain 8.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.32 MPa
@Strain 3.90 %,
Temperature 80.0 °C		2512 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.35 MPa
@Strain 2.70 %,
Temperature 80.0 °C		2516 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.45 MPa
@Strain 4.60 %,
Temperature 100 °C		2531 psi
@Strain 4.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.48 MPa
@Strain 5.40 %,
Temperature 120 °C		2535 psi
@Strain 5.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.51 MPa
@Strain 3.40 %,
Temperature 60.0 °C		2540 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.53 MPa
@Strain 4.20 %,
Temperature 100 °C		2543 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.58 MPa
@Strain 7.00 %,
Temperature 150 °C		2550 psi
@Strain 7.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.6 MPa
@Strain 5.90 %,
Temperature 120 °C		2550 psi
@Strain 5.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.6 MPa
@Strain 8.90 %,
Temperature 150 °C		2550 psi
@Strain 8.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.68 MPa
@Strain 4.00 %,
Temperature 80.0 °C		2564 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.73 MPa
@Strain 4.70 %,
Temperature 100 °C		2572 psi
@Strain 4.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.73 MPa
@Strain 0.600 %,
Temperature 23.0 °C		2572 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 17.76 MPa
@Strain 2.80 %,
Temperature 80.0 °C		2576 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.89 MPa
@Strain 4.30 %,
Temperature 100 °C		2595 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.9 MPa
@Strain 4.10 %,
Temperature 80.0 °C		2600 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.93 MPa
@Strain 3.50 %,
Temperature 60.0 °C		2601 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.94 MPa
@Strain 9.40 %,
Temperature 150 °C		2602 psi
@Strain 9.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.06 MPa
@Strain 4.80 %,
Temperature 100 °C		2619 psi
@Strain 4.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.11 MPa
@Strain 7.50 %,
Temperature 150 °C		2627 psi
@Strain 7.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.11 MPa
@Strain 2.90 %,
Temperature 80.0 °C		2627 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.15 MPa
@Strain 4.20 %,
Temperature 80.0 °C		2632 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.17 MPa
@Strain 1.40 %,
Temperature 23.0 °C		2635 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 18.18 MPa
@Strain 4.40 %,
Temperature 100 °C		2637 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.23 MPa
@Strain 4.90 %,
Temperature 100 °C		2644 psi
@Strain 4.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.29 MPa
@Strain 9.90 %,
Temperature 150 °C		2653 psi
@Strain 9.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.3 MPa
@Strain 0.600 %,
Temperature 0.000 °C		2650 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 18.32 MPa
@Strain 6.40 %,
Temperature 120 °C		2657 psi
@Strain 6.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.35 MPa
@Strain 3.60 %,
Temperature 60.0 °C		2661 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.41 MPa
@Strain 4.30 %,
Temperature 80.0 °C		2670 psi
@Strain 4.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.48 MPa
@Strain 4.50 %,
Temperature 100 °C		2680 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.52 MPa
@Strain 3.00 %,
Temperature 80.0 °C		2686 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.58 MPa
@Strain 1.10 %,
Temperature 60.0 °C		2695 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 18.58 MPa
@Strain 5.90 %,
Temperature 120 °C		2695 psi
@Strain 5.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.62 MPa
@Strain 8.00 %,
Temperature 150 °C		2701 psi
@Strain 8.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.71 MPa
@Strain 3.70 %,
Temperature 60.0 °C		2714 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.72 MPa
@Strain 4.60 %,
Temperature 100 °C		2715 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.74 MPa
@Strain 4.40 %,
Temperature 80.0 °C		2718 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.8 MPa
@Strain 10.9 %,
Temperature 150 °C		2730 psi
@Strain 10.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.89 MPa
@Strain 6.90 %,
Temperature 120 °C		2740 psi
@Strain 6.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.89 MPa
@Strain 4.70 %,
Temperature 100 °C		2740 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.93 MPa
@Strain 3.10 %,
Temperature 80.0 °C		2746 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.96 MPa
@Strain 3.80 %,
Temperature 60.0 °C		2750 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.96 MPa
@Strain 4.50 %,
Temperature 80.0 °C		2750 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.0 MPa
@Strain 8.50 %,
Temperature 150 °C		2760 psi
@Strain 8.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.05 MPa
@Strain 1.50 %,
Temperature 23.0 °C		2763 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 19.09 MPa
@Strain 0.600 %,
Temperature 0.000 °C		2769 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 19.12 MPa
@Strain 5.40 %,
Temperature 100 °C		2773 psi
@Strain 5.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 19.19 MPa
@Strain 4.60 %,
Temperature 80.0 °C		2783 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.25 MPa
@Strain 4.80 %,
Temperature 100 °C		2792 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 19.3 MPa
@Strain 3.90 %,
Temperature 60.0 °C		2800 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.33 MPa
@Strain 0.600 %,
Temperature -40.0 °C		2804 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 19.35 MPa
@Strain 11.9 %,
Temperature 150 °C		2806 psi
@Strain 11.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.37 MPa
@Strain 6.40 %,
Temperature 120 °C		2809 psi
@Strain 6.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.4 MPa
@Strain 3.20 %,
Temperature 80.0 °C		2810 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.42 MPa
@Strain 9.00 %,
Temperature 150 °C		2817 psi
@Strain 9.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.46 MPa
@Strain 7.40 %,
Temperature 120 °C		2822 psi
@Strain 7.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.49 MPa
@Strain 4.70 %,
Temperature 80.0 °C		2827 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.54 MPa
@Strain 4.90 %,
Temperature 100 °C		2834 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 19.63 MPa
@Strain 4.00 %,
Temperature 60.0 °C		2847 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.75 MPa
@Strain 3.30 %,
Temperature 80.0 °C		2865 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.78 MPa
@Strain 9.50 %,
Temperature 150 °C		2869 psi
@Strain 9.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.79 MPa
@Strain 12.9 %,
Temperature 150 °C		2870 psi
@Strain 12.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.83 MPa
@Strain 4.80 %,
Temperature 80.0 °C		2876 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.88 MPa
@Strain 4.10 %,
Temperature 60.0 °C		2883 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.97 MPa
@Strain 4.90 %,
Temperature 80.0 °C		2896 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.98 MPa
@Strain 1.60 %,
Temperature 23.0 °C		2898 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 20.08 MPa
@Strain 7.90 %,
Temperature 120 °C		2912 psi
@Strain 7.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.1 MPa
@Strain 3.40 %,
Temperature 80.0 °C		2920 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.16 MPa
@Strain 13.9 %,
Temperature 150 °C		2924 psi
@Strain 13.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.18 MPa
@Strain 6.90 %,
Temperature 120 °C		2927 psi
@Strain 6.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.2 MPa
@Strain 10.0 %,
Temperature 150 °C		2930 psi
@Strain 10.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.22 MPa
@Strain 5.90 %,
Temperature 100 °C		2933 psi
@Strain 5.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.22 MPa
@Strain 5.00 %,
Temperature 80.0 °C		2933 psi
@Strain 5.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.28 MPa
@Strain 1.20 %,
Temperature 60.0 °C		2941 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.33 MPa
@Strain 4.20 %,
Temperature 60.0 °C		2949 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.45 MPa
@Strain 3.50 %,
Temperature 80.0 °C		2966 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.47 MPa
@Strain 5.40 %,
Temperature 100 °C		2969 psi
@Strain 5.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.49 MPa
@Strain 14.9 %,
Temperature 150 °C		2972 psi
@Strain 14.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.54 MPa
@Strain 0.500 %,
Temperature -40.0 °C		2979 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 20.58 MPa
@Strain 11.0 %,
Temperature 150 °C		2985 psi
@Strain 11.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.62 MPa
@Strain 8.40 %,
Temperature 120 °C		2991 psi
@Strain 8.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.69 MPa
@Strain 4.30 %,
Temperature 60.0 °C		3001 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.78 MPa
@Strain 15.9 %,
Temperature 150 °C		3014 psi
@Strain 15.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.8 MPa
@Strain 3.70 %,
Temperature 80.0 °C		3020 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.84 MPa
@Strain 1.70 %,
Temperature 23.0 °C		3023 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 20.88 MPa
@Strain 0.700 %,
Temperature 23.0 °C		3028 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 20.89 MPa
@Strain 7.40 %,
Temperature 120 °C		3030 psi
@Strain 7.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.97 MPa
@Strain 4.40 %,
Temperature 60.0 °C		3041 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.03 MPa
@Strain 3.80 %,
Temperature 80.0 °C		3050 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.03 MPa
@Strain 16.9 %,
Temperature 150 °C		3050 psi
@Strain 16.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.04 MPa
@Strain 6.40 %,
Temperature 100 °C		3052 psi
@Strain 6.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.06 MPa
@Strain 8.90 %,
Temperature 120 °C		3055 psi
@Strain 8.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.09 MPa
@Strain 0.700 %,
Temperature 0.000 °C		3059 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 21.15 MPa
@Strain 5.50 %,
Temperature 80.0 °C		3068 psi
@Strain 5.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.17 MPa
@Strain 4.50 %,
Temperature 60.0 °C		3070 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.24 MPa
@Strain 12.0 %,
Temperature 150 °C		3081 psi
@Strain 12.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.27 MPa
@Strain 17.9 %,
Temperature 150 °C		3085 psi
@Strain 17.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.38 MPa
@Strain 3.90 %,
Temperature 80.0 °C		3101 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.47 MPa
@Strain 7.90 %,
Temperature 120 °C		3114 psi
@Strain 7.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.51 MPa
@Strain 18.9 %,
Temperature 150 °C		3120 psi
@Strain 18.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.52 MPa
@Strain 9.40 %,
Temperature 120 °C		3121 psi
@Strain 9.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.53 MPa
@Strain 4.60 %,
Temperature 60.0 °C		3123 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.57 MPa
@Strain 1.80 %,
Temperature 23.0 °C		3128 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 21.62 MPa
@Strain 5.90 %,
Temperature 100 °C		3136 psi
@Strain 5.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.64 MPa
@Strain 1.30 %,
Temperature 60.0 °C		3139 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 21.66 MPa
@Strain 13.0 %,
Temperature 150 °C		3142 psi
@Strain 13.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.72 MPa
@Strain 19.9 %,
Temperature 150 °C		3150 psi
@Strain 19.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.73 MPa
@Strain 4.00 %,
Temperature 80.0 °C		3152 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.75 MPa
@Strain 4.70 %,
Temperature 60.0 °C		3155 psi
@Strain 4.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.87 MPa
@Strain 9.90 %,
Temperature 120 °C		3172 psi
@Strain 9.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.89 MPa
@Strain 6.90 %,
Temperature 100 °C		3175 psi
@Strain 6.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.91 MPa
@Strain 20.9 %,
Temperature 150 °C		3178 psi
@Strain 20.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.92 MPa
@Strain 4.80 %,
Temperature 60.0 °C		3179 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.97 MPa
@Strain 4.10 %,
Temperature 80.0 °C		3186 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.97 MPa
@Strain 14.0 %,
Temperature 150 °C		3186 psi
@Strain 14.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.02 MPa
@Strain 21.9 %,
Temperature 150 °C		3194 psi
@Strain 21.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.08 MPa
@Strain 8.40 %,
Temperature 120 °C		3202 psi
@Strain 8.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.17 MPa
@Strain 1.90 %,
Temperature 23.0 °C		3215 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.21 MPa
@Strain 22.9 %,
Temperature 150 °C		3221 psi
@Strain 22.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.26 MPa
@Strain 0.700 %,
Temperature 0.000 °C		3229 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 22.31 MPa
@Strain 4.90 %,
Temperature 60.0 °C		3236 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.32 MPa
@Strain 4.20 %,
Temperature 80.0 °C		3237 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 22.36 MPa
@Strain 15.0 %,
Temperature 150 °C		3243 psi
@Strain 15.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.37 MPa
@Strain 23.9 %,
Temperature 150 °C		3245 psi
@Strain 23.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.47 MPa
@Strain 6.00 %,
Temperature 80.0 °C		3259 psi
@Strain 6.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 22.51 MPa
@Strain 24.9 %,
Temperature 150 °C		3265 psi
@Strain 24.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.53 MPa
@Strain 10.9 %,
Temperature 120 °C		3268 psi
@Strain 10.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.6 MPa
@Strain 6.40 %,
Temperature 100 °C		3280 psi
@Strain 6.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.62 MPa
@Strain 5.00 %,
Temperature 60.0 °C		3281 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.63 MPa
@Strain 2.00 %,
Temperature 23.0 °C		3282 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.63 MPa
@Strain 7.40 %,
Temperature 100 °C		3282 psi
@Strain 7.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.63 MPa
@Strain 25.9 %,
Temperature 150 °C		3282 psi
@Strain 25.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.65 MPa
@Strain 16.0 %,
Temperature 150 °C		3285 psi
@Strain 16.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.67 MPa
@Strain 4.30 %,
Temperature 80.0 °C		3288 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 22.67 MPa
@Strain 0.700 %,
Temperature -40.0 °C		3288 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 22.68 MPa
@Strain 8.90 %,
Temperature 120 °C		3289 psi
@Strain 8.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.76 MPa
@Strain 26.9 %,
Temperature 150 °C		3301 psi
@Strain 26.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.77 MPa
@Strain 1.40 %,
Temperature 60.0 °C		3303 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.87 MPa
@Strain 27.9 %,
Temperature 150 °C		3317 psi
@Strain 27.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.9 MPa
@Strain 4.40 %,
Temperature 80.0 °C		3320 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 22.93 MPa
@Strain 17.0 %,
Temperature 150 °C		3326 psi
@Strain 17.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.98 MPa
@Strain 28.9 %,
Temperature 150 °C		3333 psi
@Strain 28.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.07 MPa
@Strain 29.9 %,
Temperature 150 °C		3346 psi
@Strain 29.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.15 MPa
@Strain 30.9 %,
Temperature 150 °C		3358 psi
@Strain 30.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.2 MPa
@Strain 18.0 %,
Temperature 150 °C		3360 psi
@Strain 18.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.23 MPa
@Strain 31.9 %,
Temperature 150 °C		3369 psi
@Strain 31.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.25 MPa
@Strain 4.50 %,
Temperature 80.0 °C		3372 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.26 MPa
@Strain 11.9 %,
Temperature 120 °C		3374 psi
@Strain 11.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.27 MPa
@Strain 7.90 %,
Temperature 100 °C		3375 psi
@Strain 7.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 23.28 MPa
@Strain 9.40 %,
Temperature 120 °C		3376 psi
@Strain 9.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.34 MPa
@Strain 32.9 %,
Temperature 150 °C		3385 psi
@Strain 32.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.36 MPa
@Strain 19.0 %,
Temperature 150 °C		3388 psi
@Strain 19.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.39 MPa
@Strain 33.9 %,
Temperature 150 °C		3392 psi
@Strain 33.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.46 MPa
@Strain 0.800 %,
Temperature 23.0 °C		3403 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 23.47 MPa
@Strain 6.50 %,
Temperature 80.0 °C		3404 psi
@Strain 6.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.49 MPa
@Strain 34.9 %,
Temperature 150 °C		3407 psi
@Strain 34.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.49 MPa
@Strain 2.10 %,
Temperature 23.0 °C		3407 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 23.49 MPa
@Strain 4.60 %,
Temperature 80.0 °C		3407 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.53 MPa
@Strain 0.600 %,
Temperature -40.0 °C		3413 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 23.54 MPa
@Strain 6.90 %,
Temperature 100 °C		3414 psi
@Strain 6.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.55 MPa
@Strain 35.9 %,
Temperature 150 °C		3416 psi
@Strain 35.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.61 MPa
@Strain 36.9 %,
Temperature 150 °C		3424 psi
@Strain 36.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.62 MPa
@Strain 20.0 %,
Temperature 150 °C		3426 psi
@Strain 20.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.68 MPa
@Strain 37.9 %,
Temperature 150 °C		3434 psi
@Strain 37.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.68 MPa
@Strain 5.50 %,
Temperature 60.0 °C		3434 psi
@Strain 5.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.7 MPa
@Strain 0.800 %,
Temperature 0.000 °C		3440 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 23.72 MPa
@Strain 9.90 %,
Temperature 120 °C		3440 psi
@Strain 9.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.73 MPa
@Strain 38.9 %,
Temperature 150 °C		3442 psi
@Strain 38.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.78 MPa
@Strain 12.9 %,
Temperature 120 °C		3449 psi
@Strain 12.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.79 MPa
@Strain 39.9 %,
Temperature 150 °C		3450 psi
@Strain 39.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.83 MPa
@Strain 21.0 %,
Temperature 150 °C		3456 psi
@Strain 21.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.84 MPa
@Strain 40.9 %,
Temperature 150 °C		3458 psi
@Strain 40.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.84 MPa
@Strain 4.80 %,
Temperature 80.0 °C		3458 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.87 MPa
@Strain 41.9 %,
Temperature 150 °C		3462 psi
@Strain 41.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.87 MPa
@Strain 8.40 %,
Temperature 100 °C		3462 psi
@Strain 8.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 23.9 MPa
@Strain 42.9 %,
Temperature 150 °C		3470 psi
@Strain 42.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.97 MPa
@Strain 43.9 %,
Temperature 150 °C		3477 psi
@Strain 43.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.99 MPa
@Strain 2.20 %,
Temperature 23.0 °C		3479 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 24.0 MPa
@Strain 22.0 %,
Temperature 150 °C		3480 psi
@Strain 22.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.01 MPa
@Strain 44.9 %,
Temperature 150 °C		3482 psi
@Strain 44.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.02 MPa
@Strain 45.9 %,
Temperature 150 °C		3484 psi
@Strain 45.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.05 MPa
@Strain 46.9 %,
Temperature 150 °C		3488 psi
@Strain 46.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.07 MPa
@Strain 4.90 %,
Temperature 80.0 °C		3491 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.07 MPa
@Strain 1.50 %,
Temperature 60.0 °C		3491 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 24.09 MPa
@Strain 47.9 %,
Temperature 150 °C		3494 psi
@Strain 47.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.12 MPa
@Strain 48.9 %,
Temperature 150 °C		3498 psi
@Strain 48.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.16 MPa
@Strain 49.9 %,
Temperature 150 °C		3504 psi
@Strain 49.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.16 MPa
@Strain 23.0 %,
Temperature 150 °C		3504 psi
@Strain 23.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.25 MPa
@Strain 13.9 %,
Temperature 120 °C		3517 psi
@Strain 13.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.3 MPa
@Strain 7.00 %,
Temperature 80.0 °C		3520 psi
@Strain 7.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 24.31 MPa
@Strain 5.00 %,
Temperature 80.0 °C		3526 psi
@Strain 5.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.35 MPa
@Strain 7.40 %,
Temperature 100 °C		3532 psi
@Strain 7.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 24.35 MPa
@Strain 24.0 %,
Temperature 150 °C		3532 psi
@Strain 24.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.46 MPa
@Strain 8.90 %,
Temperature 100 °C		3548 psi
@Strain 8.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.46 MPa
@Strain 10.9 %,
Temperature 120 °C		3548 psi
@Strain 10.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.49 MPa
@Strain 25.0 %,
Temperature 150 °C		3552 psi
@Strain 25.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.53 MPa
@Strain 2.30 %,
Temperature 23.0 °C		3558 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 24.63 MPa
@Strain 26.0 %,
Temperature 150 °C		3572 psi
@Strain 26.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.69 MPa
@Strain 14.9 %,
Temperature 120 °C		3581 psi
@Strain 14.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.71 MPa
@Strain 27.0 %,
Temperature 150 °C		3584 psi
@Strain 27.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.88 MPa
@Strain 28.0 %,
Temperature 150 °C		3609 psi
@Strain 28.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.95 MPa
@Strain 9.40 %,
Temperature 100 °C		3619 psi
@Strain 9.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.0 MPa
@Strain 2.40 %,
Temperature 23.0 °C		3630 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.01 MPa
@Strain 29.0 %,
Temperature 150 °C		3627 psi
@Strain 29.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.07 MPa
@Strain 15.9 %,
Temperature 120 °C		3636 psi
@Strain 15.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.11 MPa
@Strain 6.00 %,
Temperature 60.0 °C		3642 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.13 MPa
@Strain 30.0 %,
Temperature 150 °C		3645 psi
@Strain 30.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.14 MPa
@Strain 7.90 %,
Temperature 100 °C		3646 psi
@Strain 7.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.14 MPa
@Strain 1.60 %,
Temperature 60.0 °C		3646 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 25.21 MPa
@Strain 7.50 %,
Temperature 80.0 °C		3656 psi
@Strain 7.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.22 MPa
@Strain 31.0 %,
Temperature 150 °C		3658 psi
@Strain 31.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.3 MPa
@Strain 11.9 %,
Temperature 120 °C		3670 psi
@Strain 11.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.32 MPa
@Strain 32.0 %,
Temperature 150 °C		3672 psi
@Strain 32.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.34 MPa
@Strain 5.50 %,
Temperature 80.0 °C		3675 psi
@Strain 5.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 25.4 MPa
@Strain 2.50 %,
Temperature 23.0 °C		3680 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.4 MPa
@Strain 33.0 %,
Temperature 150 °C		3680 psi
@Strain 33.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.42 MPa
@Strain 16.9 %,
Temperature 120 °C		3687 psi
@Strain 16.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.43 MPa
@Strain 9.90 %,
Temperature 100 °C		3688 psi
@Strain 9.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.45 MPa
@Strain 0.800 %,
Temperature 0.000 °C		3691 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 25.54 MPa
@Strain 34.0 %,
Temperature 150 °C		3704 psi
@Strain 34.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.57 MPa
@Strain 35.0 %,
Temperature 150 °C		3709 psi
@Strain 35.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.66 MPa
@Strain 36.0 %,
Temperature 150 °C		3722 psi
@Strain 36.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.74 MPa
@Strain 17.9 %,
Temperature 120 °C		3733 psi
@Strain 17.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.76 MPa
@Strain 37.0 %,
Temperature 150 °C		3736 psi
@Strain 37.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.79 MPa
@Strain 8.40 %,
Temperature 100 °C		3741 psi
@Strain 8.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.82 MPa
@Strain 38.0 %,
Temperature 150 °C		3745 psi
@Strain 38.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.9 MPa
@Strain 2.60 %,
Temperature 23.0 °C		3760 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.91 MPa
@Strain 39.0 %,
Temperature 150 °C		3758 psi
@Strain 39.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.95 MPa
@Strain 40.0 %,
Temperature 150 °C		3764 psi
@Strain 40.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.96 MPa
@Strain 12.9 %,
Temperature 120 °C		3765 psi
@Strain 12.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.99 MPa
@Strain 8.00 %,
Temperature 80.0 °C		3770 psi
@Strain 8.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.0 MPa
@Strain 18.9 %,
Temperature 120 °C		3770 psi
@Strain 18.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.03 MPa
@Strain 0.800 %,
Temperature -40.0 °C		3775 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 26.05 MPa
@Strain 41.0 %,
Temperature 150 °C		3778 psi
@Strain 41.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.08 MPa
@Strain 42.0 %,
Temperature 150 °C		3783 psi
@Strain 42.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.13 MPa
@Strain 43.0 %,
Temperature 150 °C		3790 psi
@Strain 43.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.19 MPa
@Strain 44.0 %,
Temperature 150 °C		3799 psi
@Strain 44.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.2 MPa
@Strain 10.9 %,
Temperature 100 °C		3800 psi
@Strain 10.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.21 MPa
@Strain 1.70 %,
Temperature 60.0 °C		3801 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.22 MPa
@Strain 45.0 %,
Temperature 150 °C		3803 psi
@Strain 45.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.23 MPa
@Strain 19.9 %,
Temperature 120 °C		3804 psi
@Strain 19.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.26 MPa
@Strain 2.70 %,
Temperature 23.0 °C		3809 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.29 MPa
@Strain 46.0 %,
Temperature 150 °C		3813 psi
@Strain 46.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.32 MPa
@Strain 6.50 %,
Temperature 60.0 °C		3817 psi
@Strain 6.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.35 MPa
@Strain 47.0 %,
Temperature 150 °C		3822 psi
@Strain 47.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.35 MPa
@Strain 48.0 %,
Temperature 150 °C		3822 psi
@Strain 48.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.39 MPa
@Strain 49.0 %,
Temperature 150 °C		3828 psi
@Strain 49.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.4 MPa
@Strain 50.0 %,
Temperature 150 °C		3830 psi
@Strain 50.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.46 MPa
@Strain 20.9 %,
Temperature 120 °C		3838 psi
@Strain 20.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.51 MPa
@Strain 8.90 %,
Temperature 100 °C		3845 psi
@Strain 8.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 26.53 MPa
@Strain 13.9 %,
Temperature 120 °C		3848 psi
@Strain 13.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.61 MPa
@Strain 2.80 %,
Temperature 23.0 °C		3859 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.65 MPa
@Strain 21.9 %,
Temperature 120 °C		3865 psi
@Strain 21.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.7 MPa
@Strain 8.50 %,
Temperature 80.0 °C		3870 psi
@Strain 8.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.71 MPa
@Strain 6.00 %,
Temperature 80.0 °C		3874 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.74 MPa
@Strain 0.900 %,
Temperature 23.0 °C		3878 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 26.85 MPa
@Strain 22.9 %,
Temperature 120 °C		3894 psi
@Strain 22.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.99 MPa
@Strain 14.9 %,
Temperature 120 °C		3915 psi
@Strain 14.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.01 MPa
@Strain 23.9 %,
Temperature 120 °C		3917 psi
@Strain 23.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.01 MPa
@Strain 0.900 %,
Temperature 0.000 °C		3917 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 27.04 MPa
@Strain 11.9 %,
Temperature 100 °C		3922 psi
@Strain 11.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.13 MPa
@Strain 2.90 %,
Temperature 23.0 °C		3935 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.16 MPa
@Strain 9.40 %,
Temperature 100 °C		3939 psi
@Strain 9.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.18 MPa
@Strain 24.9 %,
Temperature 120 °C		3942 psi
@Strain 24.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.24 MPa
@Strain 0.700 %,
Temperature -40.0 °C		3951 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 27.27 MPa
@Strain 1.80 %,
Temperature 60.0 °C		3955 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 27.32 MPa
@Strain 7.00 %,
Temperature 60.0 °C		3962 psi
@Strain 7.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.34 MPa
@Strain 9.00 %,
Temperature 80.0 °C		3965 psi
@Strain 9.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.36 MPa
@Strain 25.9 %,
Temperature 120 °C		3968 psi
@Strain 25.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.46 MPa
@Strain 26.9 %,
Temperature 120 °C		3983 psi
@Strain 26.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.53 MPa
@Strain 15.9 %,
Temperature 120 °C		3993 psi
@Strain 15.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.55 MPa
@Strain 3.00 %,
Temperature 23.0 °C		3996 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.61 MPa
@Strain 27.9 %,
Temperature 120 °C		4004 psi
@Strain 27.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.66 MPa
@Strain 9.90 %,
Temperature 100 °C		4012 psi
@Strain 9.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.69 MPa
@Strain 28.9 %,
Temperature 120 °C		4016 psi
@Strain 28.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.7 MPa
@Strain 12.9 %,
Temperature 100 °C		4020 psi
@Strain 12.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.82 MPa
@Strain 29.9 %,
Temperature 120 °C		4035 psi
@Strain 29.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.84 MPa
@Strain 6.50 %,
Temperature 80.0 °C		4038 psi
@Strain 6.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 27.85 MPa
@Strain 16.9 %,
Temperature 120 °C		4039 psi
@Strain 16.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.93 MPa
@Strain 30.9 %,
Temperature 120 °C		4051 psi
@Strain 30.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.95 MPa
@Strain 3.10 %,
Temperature 23.0 °C		4054 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.01 MPa
@Strain 9.50 %,
Temperature 80.0 °C		4063 psi
@Strain 9.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 28.03 MPa
@Strain 31.9 %,
Temperature 120 °C		4065 psi
@Strain 31.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.12 MPa
@Strain 32.9 %,
Temperature 120 °C		4078 psi
@Strain 32.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.17 MPa
@Strain 33.9 %,
Temperature 120 °C		4086 psi
@Strain 33.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.22 MPa
@Strain 13.9 %,
Temperature 100 °C		4093 psi
@Strain 13.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.22 MPa
@Strain 7.50 %,
Temperature 60.0 °C		4093 psi
@Strain 7.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.24 MPa
@Strain 3.20 %,
Temperature 23.0 °C		4096 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.26 MPa
@Strain 17.9 %,
Temperature 120 °C		4099 psi
@Strain 17.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.28 MPa
@Strain 34.9 %,
Temperature 120 °C		4102 psi
@Strain 34.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.28 MPa
@Strain 1.90 %,
Temperature 60.0 °C		4102 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 28.31 MPa
@Strain 35.9 %,
Temperature 120 °C		4106 psi
@Strain 35.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.39 MPa
@Strain 36.9 %,
Temperature 120 °C		4118 psi
@Strain 36.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.45 MPa
@Strain 0.900 %,
Temperature 0.000 °C		4126 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 28.48 MPa
@Strain 37.9 %,
Temperature 120 °C		4131 psi
@Strain 37.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.53 MPa
@Strain 38.9 %,
Temperature 120 °C		4138 psi
@Strain 38.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.55 MPa
@Strain 3.30 %,
Temperature 23.0 °C		4141 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.56 MPa
@Strain 39.9 %,
Temperature 120 °C		4142 psi
@Strain 39.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.6 MPa
@Strain 40.9 %,
Temperature 120 °C		4150 psi
@Strain 40.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.6 MPa
@Strain 10.0 %,
Temperature 80.0 °C		4150 psi
@Strain 10.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 28.61 MPa
@Strain 18.9 %,
Temperature 120 °C		4150 psi
@Strain 18.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.65 MPa
@Strain 41.9 %,
Temperature 120 °C		4155 psi
@Strain 41.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.67 MPa
@Strain 10.9 %,
Temperature 100 °C		4158 psi
@Strain 10.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.69 MPa
@Strain 14.9 %,
Temperature 100 °C		4161 psi
@Strain 14.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.71 MPa
@Strain 42.9 %,
Temperature 120 °C		4164 psi
@Strain 42.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.75 MPa
@Strain 43.9 %,
Temperature 120 °C		4170 psi
@Strain 43.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.77 MPa
@Strain 7.00 %,
Temperature 80.0 °C		4173 psi
@Strain 7.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.78 MPa
@Strain 44.9 %,
Temperature 120 °C		4174 psi
@Strain 44.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.79 MPa
@Strain 45.9 %,
Temperature 120 °C		4176 psi
@Strain 45.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.79 MPa
@Strain 46.9 %,
Temperature 120 °C		4176 psi
@Strain 46.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.88 MPa
@Strain 47.9 %,
Temperature 120 °C		4189 psi
@Strain 47.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.89 MPa
@Strain 19.9 %,
Temperature 120 °C		4190 psi
@Strain 19.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.89 MPa
@Strain 3.40 %,
Temperature 23.0 °C		4190 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.91 MPa
@Strain 48.9 %,
Temperature 120 °C		4193 psi
@Strain 48.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.95 MPa
@Strain 49.9 %,
Temperature 120 °C		4199 psi
@Strain 49.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.95 MPa
@Strain 54.9 %,
Temperature 120 °C		4199 psi
@Strain 54.9 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.13 MPa
@Strain 15.9 %,
Temperature 100 °C		4225 psi
@Strain 15.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.15 MPa
@Strain 3.50 %,
Temperature 23.0 °C		4228 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.16 MPa
@Strain 8.00 %,
Temperature 60.0 °C		4229 psi
@Strain 8.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.2 MPa
@Strain 20.9 %,
Temperature 120 °C		4240 psi
@Strain 20.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.23 MPa
@Strain 2.00 %,
Temperature 60.0 °C		4239 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.39 MPa
@Strain 0.900 %,
Temperature -40.0 °C		4263 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 29.45 MPa
@Strain 21.9 %,
Temperature 120 °C		4271 psi
@Strain 21.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.5 MPa
@Strain 16.9 %,
Temperature 100 °C		4280 psi
@Strain 16.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.53 MPa
@Strain 11.0 %,
Temperature 80.0 °C		4283 psi
@Strain 11.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.54 MPa
@Strain 3.60 %,
Temperature 23.0 °C		4284 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.68 MPa
@Strain 7.50 %,
Temperature 80.0 °C		4305 psi
@Strain 7.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.69 MPa
@Strain 22.9 %,
Temperature 120 °C		4306 psi
@Strain 22.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.72 MPa
@Strain 11.9 %,
Temperature 100 °C		4311 psi
@Strain 11.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 29.79 MPa
@Strain 17.9 %,
Temperature 100 °C		4321 psi
@Strain 17.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.85 MPa
@Strain 1.00 %,
Temperature 23.0 °C		4329 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 29.88 MPa
@Strain 3.70 %,
Temperature 23.0 °C		4334 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.88 MPa
@Strain 2.10 %,
Temperature 60.0 °C		4334 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.91 MPa
@Strain 23.9 %,
Temperature 120 °C		4338 psi
@Strain 23.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.04 MPa
@Strain 8.50 %,
Temperature 60.0 °C		4357 psi
@Strain 8.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.09 MPa
@Strain 18.9 %,
Temperature 100 °C		4364 psi
@Strain 18.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.11 MPa
@Strain 24.9 %,
Temperature 120 °C		4367 psi
@Strain 24.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.15 MPa
@Strain 3.80 %,
Temperature 23.0 °C		4373 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.15 MPa
@Strain 1.00 %,
Temperature 0.000 °C		4373 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 30.32 MPa
@Strain 25.9 %,
Temperature 120 °C		4398 psi
@Strain 25.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.35 MPa
@Strain 19.9 %,
Temperature 100 °C		4402 psi
@Strain 19.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.44 MPa
@Strain 3.90 %,
Temperature 23.0 °C		4415 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.46 MPa
@Strain 12.9 %,
Temperature 100 °C		4418 psi
@Strain 12.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.47 MPa
@Strain 2.20 %,
Temperature 60.0 °C		4419 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.51 MPa
@Strain 26.9 %,
Temperature 120 °C		4425 psi
@Strain 26.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.54 MPa
@Strain 12.0 %,
Temperature 80.0 °C		4429 psi
@Strain 12.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.54 MPa
@Strain 8.00 %,
Temperature 80.0 °C		4429 psi
@Strain 8.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 30.59 MPa
@Strain 20.9 %,
Temperature 100 °C		4437 psi
@Strain 20.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.67 MPa
@Strain 27.9 %,
Temperature 120 °C		4448 psi
@Strain 27.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.67 MPa
@Strain 4.00 %,
Temperature 23.0 °C		4448 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.76 MPa
@Strain 28.9 %,
Temperature 120 °C		4461 psi
@Strain 28.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.8 MPa
@Strain 9.00 %,
Temperature 60.0 °C		4470 psi
@Strain 9.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.81 MPa
@Strain 21.9 %,
Temperature 100 °C		4469 psi
@Strain 21.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.92 MPa
@Strain 29.9 %,
Temperature 120 °C		4485 psi
@Strain 29.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.98 MPa
@Strain 22.9 %,
Temperature 100 °C		4493 psi
@Strain 22.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.04 MPa
@Strain 4.10 %,
Temperature 23.0 °C		4502 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.07 MPa
@Strain 30.9 %,
Temperature 120 °C		4506 psi
@Strain 30.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.12 MPa
@Strain 23.9 %,
Temperature 100 °C		4514 psi
@Strain 23.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.19 MPa
@Strain 31.9 %,
Temperature 120 °C		4524 psi
@Strain 31.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.21 MPa
@Strain 13.9 %,
Temperature 100 °C		4527 psi
@Strain 13.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.24 MPa
@Strain 2.30 %,
Temperature 60.0 °C		4531 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.31 MPa
@Strain 24.9 %,
Temperature 100 °C		4541 psi
@Strain 24.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.32 MPa
@Strain 32.9 %,
Temperature 120 °C		4543 psi
@Strain 32.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.35 MPa
@Strain 8.50 %,
Temperature 80.0 °C		4547 psi
@Strain 8.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 31.36 MPa
@Strain 13.0 %,
Temperature 80.0 °C		4548 psi
@Strain 13.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.37 MPa
@Strain 33.9 %,
Temperature 120 °C		4550 psi
@Strain 33.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.38 MPa
@Strain 4.20 %,
Temperature 23.0 °C		4551 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.41 MPa
@Strain 1.00 %,
Temperature 0.000 °C		4556 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 31.48 MPa
@Strain 34.9 %,
Temperature 120 °C		4566 psi
@Strain 34.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.48 MPa
@Strain 25.9 %,
Temperature 100 °C		4566 psi
@Strain 25.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.58 MPa
@Strain 26.9 %,
Temperature 100 °C		4580 psi
@Strain 26.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.59 MPa
@Strain 9.50 %,
Temperature 60.0 °C		4582 psi
@Strain 9.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 31.61 MPa
@Strain 35.9 %,
Temperature 120 °C		4585 psi
@Strain 35.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.63 MPa
@Strain 36.9 %,
Temperature 120 °C		4588 psi
@Strain 36.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.64 MPa
@Strain 4.30 %,
Temperature 23.0 °C		4589 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.71 MPa
@Strain 27.9 %,
Temperature 100 °C		4599 psi
@Strain 27.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.73 MPa
@Strain 37.9 %,
Temperature 120 °C		4602 psi
@Strain 37.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.76 MPa
@Strain 0.800 %,
Temperature -40.0 °C		4606 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 31.77 MPa
@Strain 28.9 %,
Temperature 100 °C		4608 psi
@Strain 28.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.82 MPa
@Strain 14.9 %,
Temperature 100 °C		4615 psi
@Strain 14.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.86 MPa
@Strain 38.9 %,
Temperature 120 °C		4621 psi
@Strain 38.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.88 MPa
@Strain 29.9 %,
Temperature 100 °C		4624 psi
@Strain 29.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.89 MPa
@Strain 39.9 %,
Temperature 120 °C		4625 psi
@Strain 39.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.96 MPa
@Strain 4.40 %,
Temperature 23.0 °C		4635 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.96 MPa
@Strain 2.40 %,
Temperature 60.0 °C		4635 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.98 MPa
@Strain 30.9 %,
Temperature 100 °C		4638 psi
@Strain 30.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.99 MPa
@Strain 40.9 %,
Temperature 120 °C		4640 psi
@Strain 40.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.02 MPa
@Strain 14.0 %,
Temperature 80.0 °C		4644 psi
@Strain 14.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.03 MPa
@Strain 31.9 %,
Temperature 100 °C		4646 psi
@Strain 31.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.08 MPa
@Strain 41.9 %,
Temperature 120 °C		4653 psi
@Strain 41.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.09 MPa
@Strain 32.9 %,
Temperature 100 °C		4654 psi
@Strain 32.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.11 MPa
@Strain 42.9 %,
Temperature 120 °C		4657 psi
@Strain 42.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.11 MPa
@Strain 9.00 %,
Temperature 80.0 °C		4657 psi
@Strain 9.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.18 MPa
@Strain 43.9 %,
Temperature 120 °C		4667 psi
@Strain 43.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.18 MPa
@Strain 33.9 %,
Temperature 100 °C		4667 psi
@Strain 33.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.18 MPa
@Strain 34.9 %,
Temperature 100 °C		4667 psi
@Strain 34.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.2 MPa
@Strain 4.50 %,
Temperature 23.0 °C		4670 psi
@Strain 4.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.23 MPa
@Strain 44.9 %,
Temperature 120 °C		4675 psi
@Strain 44.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.24 MPa
@Strain 35.9 %,
Temperature 100 °C		4676 psi
@Strain 35.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.26 MPa
@Strain 10.0 %,
Temperature 60.0 °C		4679 psi
@Strain 10.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.28 MPa
@Strain 45.9 %,
Temperature 120 °C		4682 psi
@Strain 45.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.31 MPa
@Strain 36.9 %,
Temperature 100 °C		4686 psi
@Strain 36.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.33 MPa
@Strain 46.9 %,
Temperature 120 °C		4689 psi
@Strain 46.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.34 MPa
@Strain 37.9 %,
Temperature 100 °C		4691 psi
@Strain 37.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.37 MPa
@Strain 38.9 %,
Temperature 100 °C		4695 psi
@Strain 38.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.37 MPa
@Strain 39.9 %,
Temperature 100 °C		4695 psi
@Strain 39.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.41 MPa
@Strain 40.9 %,
Temperature 100 °C		4701 psi
@Strain 40.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.41 MPa
@Strain 48.9 %,
Temperature 120 °C		4701 psi
@Strain 48.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.43 MPa
@Strain 49.9 %,
Temperature 120 °C		4704 psi
@Strain 49.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.43 MPa
@Strain 50.0 %,
Temperature 120 °C		4704 psi
@Strain 50.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.43 MPa
@Strain 47.9 %,
Temperature 120 °C		4704 psi
@Strain 47.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.44 MPa
@Strain 41.9 %,
Temperature 100 °C		4705 psi
@Strain 41.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.44 MPa
@Strain 15.9 %,
Temperature 100 °C		4705 psi
@Strain 15.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.46 MPa
@Strain 43.9 %,
Temperature 100 °C		4708 psi
@Strain 43.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.46 MPa
@Strain 4.60 %,
Temperature 23.0 °C		4708 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.47 MPa
@Strain 42.9 %,
Temperature 100 °C		4709 psi
@Strain 42.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.48 MPa
@Strain 46.9 %,
Temperature 100 °C		4711 psi
@Strain 46.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.5 MPa
@Strain 44.9 %,
Temperature 100 °C		4710 psi
@Strain 44.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.5 MPa
@Strain 45.9 %,
Temperature 100 °C		4710 psi
@Strain 45.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.5 MPa
@Strain 48.9 %,
Temperature 100 °C		4710 psi
@Strain 48.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.5 MPa
@Strain 54.9 %,
Temperature 100 °C		4710 psi
@Strain 54.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.5 MPa
@Strain 1.00 %,
Temperature -40.0 °C		4710 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 32.53 MPa
@Strain 49.9 %,
Temperature 100 °C		4718 psi
@Strain 49.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.54 MPa
@Strain 47.9 %,
Temperature 100 °C		4720 psi
@Strain 47.9 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.62 MPa
@Strain 15.0 %,
Temperature 80.0 °C		4731 psi
@Strain 15.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.71 MPa
@Strain 4.70 %,
Temperature 23.0 °C		4744 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.73 MPa
@Strain 2.50 %,
Temperature 60.0 °C		4747 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.92 MPa
@Strain 9.50 %,
Temperature 80.0 °C		4775 psi
@Strain 9.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.93 MPa
@Strain 16.9 %,
Temperature 100 °C		4776 psi
@Strain 16.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.98 MPa
@Strain 4.80 %,
Temperature 23.0 °C		4783 psi
@Strain 4.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.08 MPa
@Strain 1.10 %,
Temperature 23.0 °C		4798 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 33.12 MPa
@Strain 16.0 %,
Temperature 80.0 °C		4804 psi
@Strain 16.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.14 MPa
@Strain 4.90 %,
Temperature 23.0 °C		4807 psi
@Strain 4.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.31 MPa
@Strain 11.0 %,
Temperature 60.0 °C		4831 psi
@Strain 11.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.32 MPa
@Strain 2.60 %,
Temperature 60.0 °C		4833 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.34 MPa
@Strain 17.9 %,
Temperature 100 °C		4836 psi
@Strain 17.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.41 MPa
@Strain 1.10 %,
Temperature 0.000 °C		4846 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 33.45 MPa
@Strain 5.00 %,
Temperature 23.0 °C		4852 psi
@Strain 5.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.51 MPa
@Strain 10.0 %,
Temperature 80.0 °C		4860 psi
@Strain 10.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 33.57 MPa
@Strain 17.0 %,
Temperature 80.0 °C		4869 psi
@Strain 17.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.59 MPa
@Strain 1.10 %,
Temperature 0.000 °C		4872 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 33.78 MPa
@Strain 18.9 %,
Temperature 100 °C		4899 psi
@Strain 18.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.79 MPa
@Strain 2.70 %,
Temperature 60.0 °C		4901 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.96 MPa
@Strain 18.0 %,
Temperature 80.0 °C		4925 psi
@Strain 18.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.08 MPa
@Strain 19.9 %,
Temperature 100 °C		4943 psi
@Strain 19.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.27 MPa
@Strain 2.80 %,
Temperature 60.0 °C		4970 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.29 MPa
@Strain 19.0 %,
Temperature 80.0 °C		4973 psi
@Strain 19.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.44 MPa
@Strain 20.9 %,
Temperature 100 °C		4995 psi
@Strain 20.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.51 MPa
@Strain 5.50 %,
Temperature 23.0 °C		5005 psi
@Strain 5.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 34.52 MPa
@Strain 12.0 %,
Temperature 60.0 °C		5007 psi
@Strain 12.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 34.57 MPa
@Strain 11.0 %,
Temperature 80.0 °C		5014 psi
@Strain 11.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.57 MPa
@Strain 20.0 %,
Temperature 80.0 °C		5014 psi
@Strain 20.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.62 MPa
@Strain 2.90 %,
Temperature 60.0 °C		5021 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.74 MPa
@Strain 21.9 %,
Temperature 100 °C		5039 psi
@Strain 21.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.84 MPa
@Strain 21.0 %,
Temperature 80.0 °C		5053 psi
@Strain 21.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.92 MPa
@Strain 3.00 %,
Temperature 60.0 °C		5065 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.02 MPa
@Strain 22.9 %,
Temperature 100 °C		5079 psi
@Strain 22.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.07 MPa
@Strain 22.0 %,
Temperature 80.0 °C		5086 psi
@Strain 22.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.23 MPa
@Strain 23.0 %,
Temperature 80.0 °C		5110 psi
@Strain 23.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.28 MPa
@Strain 23.9 %,
Temperature 100 °C		5117 psi
@Strain 23.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.34 MPa
@Strain 3.10 %,
Temperature 60.0 °C		5126 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.34 MPa
@Strain 0.900 %,
Temperature -40.0 °C		5126 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 35.42 MPa
@Strain 24.0 %,
Temperature 80.0 °C		5137 psi
@Strain 24.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.47 MPa
@Strain 13.0 %,
Temperature 60.0 °C		5144 psi
@Strain 13.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.48 MPa
@Strain 24.9 %,
Temperature 100 °C		5146 psi
@Strain 24.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.57 MPa
@Strain 3.20 %,
Temperature 60.0 °C		5159 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.59 MPa
@Strain 25.0 %,
Temperature 80.0 °C		5162 psi
@Strain 25.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.64 MPa
@Strain 1.10 %,
Temperature -40.0 °C		5169 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 35.68 MPa
@Strain 26.0 %,
Temperature 80.0 °C		5175 psi
@Strain 26.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.68 MPa
@Strain 25.9 %,
Temperature 100 °C		5175 psi
@Strain 25.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.77 MPa
@Strain 12.0 %,
Temperature 80.0 °C		5188 psi
@Strain 12.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 35.81 MPa
@Strain 27.0 %,
Temperature 80.0 °C		5194 psi
@Strain 27.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.82 MPa
@Strain 1.20 %,
Temperature 0.000 °C		5195 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 35.86 MPa
@Strain 6.00 %,
Temperature 23.0 °C		5201 psi
@Strain 6.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.86 MPa
@Strain 26.9 %,
Temperature 100 °C		5201 psi
@Strain 26.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.91 MPa
@Strain 28.0 %,
Temperature 80.0 °C		5208 psi
@Strain 28.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.93 MPa
@Strain 3.30 %,
Temperature 60.0 °C		5211 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.98 MPa
@Strain 29.0 %,
Temperature 80.0 °C		5218 psi
@Strain 29.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.01 MPa
@Strain 1.20 %,
Temperature 23.0 °C		5223 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 36.05 MPa
@Strain 27.9 %,
Temperature 100 °C		5229 psi
@Strain 27.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.06 MPa
@Strain 30.0 %,
Temperature 80.0 °C		5230 psi
@Strain 30.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.13 MPa
@Strain 31.0 %,
Temperature 80.0 °C		5240 psi
@Strain 31.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.15 MPa
@Strain 32.0 %,
Temperature 80.0 °C		5243 psi
@Strain 32.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.17 MPa
@Strain 3.40 %,
Temperature 60.0 °C		5246 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.19 MPa
@Strain 33.0 %,
Temperature 80.0 °C		5249 psi
@Strain 33.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.2 MPa
@Strain 50.0 %,
Temperature 80.0 °C		5250 psi
@Strain 50.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.22 MPa
@Strain 49.0 %,
Temperature 80.0 °C		5253 psi
@Strain 49.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.24 MPa
@Strain 14.0 %,
Temperature 60.0 °C		5256 psi
@Strain 14.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.25 MPa
@Strain 28.9 %,
Temperature 100 °C		5258 psi
@Strain 28.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.26 MPa
@Strain 47.0 %,
Temperature 80.0 °C		5259 psi
@Strain 47.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.26 MPa
@Strain 48.0 %,
Temperature 80.0 °C		5259 psi
@Strain 48.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.26 MPa
@Strain 34.0 %,
Temperature 80.0 °C		5259 psi
@Strain 34.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.26 MPa
@Strain 35.0 %,
Temperature 80.0 °C		5259 psi
@Strain 35.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.26 MPa
@Strain 36.0 %,
Temperature 80.0 °C		5259 psi
@Strain 36.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.28 MPa
@Strain 46.0 %,
Temperature 80.0 °C		5262 psi
@Strain 46.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.3 MPa
@Strain 37.0 %,
Temperature 80.0 °C		5260 psi
@Strain 37.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.31 MPa
@Strain 38.0 %,
Temperature 80.0 °C		5266 psi
@Strain 38.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.31 MPa
@Strain 45.0 %,
Temperature 80.0 °C		5266 psi
@Strain 45.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.32 MPa
@Strain 44.0 %,
Temperature 80.0 °C		5268 psi
@Strain 44.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.32 MPa
@Strain 42.0 %,
Temperature 80.0 °C		5268 psi
@Strain 42.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.33 MPa
@Strain 41.0 %,
Temperature 80.0 °C		5269 psi
@Strain 41.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.33 MPa
@Strain 39.0 %,
Temperature 80.0 °C		5269 psi
@Strain 39.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.34 MPa
@Strain 40.0 %,
Temperature 80.0 °C		5271 psi
@Strain 40.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.34 MPa
@Strain 3.50 %,
Temperature 60.0 °C		5271 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.35 MPa
@Strain 43.0 %,
Temperature 80.0 °C		5272 psi
@Strain 43.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.37 MPa
@Strain 1.20 %,
Temperature 0.000 °C		5275 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 36.42 MPa
@Strain 29.9 %,
Temperature 100 °C		5282 psi
@Strain 29.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.51 MPa
@Strain 30.9 %,
Temperature 100 °C		5295 psi
@Strain 30.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.64 MPa
@Strain 3.60 %,
Temperature 60.0 °C		5314 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.7 MPa
@Strain 31.9 %,
Temperature 100 °C		5320 psi
@Strain 31.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.73 MPa
@Strain 13.0 %,
Temperature 80.0 °C		5327 psi
@Strain 13.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 36.84 MPa
@Strain 32.9 %,
Temperature 100 °C		5343 psi
@Strain 32.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.9 MPa
@Strain 33.9 %,
Temperature 100 °C		5350 psi
@Strain 33.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.94 MPa
@Strain 3.70 %,
Temperature 60.0 °C		5358 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.96 MPa
@Strain 15.0 %,
Temperature 60.0 °C		5361 psi
@Strain 15.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.99 MPa
@Strain 6.50 %,
Temperature 23.0 °C		5365 psi
@Strain 6.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.02 MPa
@Strain 34.9 %,
Temperature 100 °C		5369 psi
@Strain 34.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.11 MPa
@Strain 3.80 %,
Temperature 60.0 °C		5382 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.14 MPa
@Strain 35.9 %,
Temperature 100 °C		5387 psi
@Strain 35.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.23 MPa
@Strain 36.9 %,
Temperature 100 °C		5400 psi
@Strain 36.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.23 MPa
@Strain 3.90 %,
Temperature 60.0 °C		5400 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.33 MPa
@Strain 37.9 %,
Temperature 100 °C		5414 psi
@Strain 37.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.4 MPa
@Strain 38.9 %,
Temperature 100 °C		5420 psi
@Strain 38.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.46 MPa
@Strain 39.9 %,
Temperature 100 °C		5433 psi
@Strain 39.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.47 MPa
@Strain 4.00 %,
Temperature 60.0 °C		5435 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.48 MPa
@Strain 40.9 %,
Temperature 100 °C		5436 psi
@Strain 40.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.57 MPa
@Strain 16.0 %,
Temperature 60.0 °C		5449 psi
@Strain 16.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.59 MPa
@Strain 4.10 %,
Temperature 60.0 °C		5452 psi
@Strain 4.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.59 MPa
@Strain 41.9 %,
Temperature 100 °C		5452 psi
@Strain 41.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.6 MPa
@Strain 14.0 %,
Temperature 80.0 °C		5450 psi
@Strain 14.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.69 MPa
@Strain 42.9 %,
Temperature 100 °C		5466 psi
@Strain 42.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.74 MPa
@Strain 43.9 %,
Temperature 100 °C		5474 psi
@Strain 43.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.77 MPa
@Strain 44.9 %,
Temperature 100 °C		5478 psi
@Strain 44.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.77 MPa
@Strain 4.20 %,
Temperature 60.0 °C		5478 psi
@Strain 4.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.82 MPa
@Strain 45.9 %,
Temperature 100 °C		5485 psi
@Strain 45.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.87 MPa
@Strain 46.9 %,
Temperature 100 °C		5493 psi
@Strain 46.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.89 MPa
@Strain 47.9 %,
Temperature 100 °C		5495 psi
@Strain 47.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.94 MPa
@Strain 4.30 %,
Temperature 60.0 °C		5503 psi
@Strain 4.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.97 MPa
@Strain 48.9 %,
Temperature 100 °C		5507 psi
@Strain 48.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.02 MPa
@Strain 49.9 %,
Temperature 100 °C		5514 psi
@Strain 49.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.02 MPa
@Strain 50.0 %,
Temperature 100 °C		5514 psi
@Strain 50.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.06 MPa
@Strain 4.40 %,
Temperature 60.0 °C		5520 psi
@Strain 4.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.1 MPa
@Strain 7.00 %,
Temperature 23.0 °C		5530 psi
@Strain 7.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.11 MPa
@Strain 17.0 %,
Temperature 60.0 °C		5527 psi
@Strain 17.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.36 MPa
@Strain 15.0 %,
Temperature 80.0 °C		5564 psi
@Strain 15.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.36 MPa
@Strain 4.50 %,
Temperature 60.0 °C		5564 psi
@Strain 4.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.41 MPa
@Strain 1.30 %,
Temperature 23.0 °C		5571 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 38.42 MPa
@Strain 4.60 %,
Temperature 60.0 °C		5572 psi
@Strain 4.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.43 MPa
@Strain 1.30 %,
Temperature 0.000 °C		5574 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 38.48 MPa
@Strain 4.70 %,
Temperature 60.0 °C		5581 psi
@Strain 4.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.56 MPa
@Strain 18.0 %,
Temperature 60.0 °C		5593 psi
@Strain 18.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.72 MPa
@Strain 1.20 %,
Temperature -40.0 °C		5616 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 38.77 MPa
@Strain 4.80 %,
Temperature 60.0 °C		5623 psi
@Strain 4.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.8 MPa
@Strain 1.30 %,
Temperature 0.000 °C		5630 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 38.84 MPa
@Strain 1.00 %,
Temperature -40.0 °C		5633 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 38.89 MPa
@Strain 4.90 %,
Temperature 60.0 °C		5641 psi
@Strain 4.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.96 MPa
@Strain 19.0 %,
Temperature 60.0 °C		5651 psi
@Strain 19.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.0 MPa
@Strain 16.0 %,
Temperature 80.0 °C		5660 psi
@Strain 16.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.09 MPa
@Strain 7.50 %,
Temperature 23.0 °C		5670 psi
@Strain 7.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.29 MPa
@Strain 20.0 %,
Temperature 60.0 °C		5699 psi
@Strain 20.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.45 MPa
@Strain 5.40 %,
Temperature 60.0 °C		5722 psi
@Strain 5.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 39.55 MPa
@Strain 17.0 %,
Temperature 80.0 °C		5736 psi
@Strain 17.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.6 MPa
@Strain 21.0 %,
Temperature 60.0 °C		5740 psi
@Strain 21.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.85 MPa
@Strain 22.0 %,
Temperature 60.0 °C		5780 psi
@Strain 22.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.92 MPa
@Strain 8.00 %,
Temperature 23.0 °C		5790 psi
@Strain 8.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 40.04 MPa
@Strain 18.0 %,
Temperature 80.0 °C		5807 psi
@Strain 18.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.06 MPa
@Strain 23.0 %,
Temperature 60.0 °C		5810 psi
@Strain 23.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.26 MPa
@Strain 24.0 %,
Temperature 60.0 °C		5839 psi
@Strain 24.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.32 MPa
@Strain 5.90 %,
Temperature 60.0 °C		5848 psi
@Strain 5.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.42 MPa
@Strain 25.0 %,
Temperature 60.0 °C		5862 psi
@Strain 25.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.53 MPa
@Strain 26.0 %,
Temperature 60.0 °C		5878 psi
@Strain 26.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.53 MPa
@Strain 19.0 %,
Temperature 80.0 °C		5878 psi
@Strain 19.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.66 MPa
@Strain 27.0 %,
Temperature 60.0 °C		5897 psi
@Strain 27.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.68 MPa
@Strain 8.50 %,
Temperature 23.0 °C		5900 psi
@Strain 8.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 40.73 MPa
@Strain 50.0 %,
Temperature 60.0 °C		5907 psi
@Strain 50.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.75 MPa
@Strain 28.0 %,
Temperature 60.0 °C		5910 psi
@Strain 28.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.76 MPa
@Strain 49.0 %,
Temperature 60.0 °C		5912 psi
@Strain 49.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.79 MPa
@Strain 47.0 %,
Temperature 60.0 °C		5916 psi
@Strain 47.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.8 MPa
@Strain 48.0 %,
Temperature 60.0 °C		5920 psi
@Strain 48.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.82 MPa
@Strain 1.40 %,
Temperature 23.0 °C		5920 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 40.85 MPa
@Strain 46.0 %,
Temperature 60.0 °C		5925 psi
@Strain 46.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.86 MPa
@Strain 29.0 %,
Temperature 60.0 °C		5926 psi
@Strain 29.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.88 MPa
@Strain 45.0 %,
Temperature 60.0 °C		5929 psi
@Strain 45.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.9 MPa
@Strain 30.0 %,
Temperature 60.0 °C		5930 psi
@Strain 30.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.9 MPa
@Strain 44.0 %,
Temperature 60.0 °C		5930 psi
@Strain 44.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.94 MPa
@Strain 31.0 %,
Temperature 60.0 °C		5938 psi
@Strain 31.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.95 MPa
@Strain 43.0 %,
Temperature 60.0 °C		5939 psi
@Strain 43.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.96 MPa
@Strain 42.0 %,
Temperature 60.0 °C		5941 psi
@Strain 42.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.98 MPa
@Strain 33.0 %,
Temperature 60.0 °C		5944 psi
@Strain 33.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.98 MPa
@Strain 32.0 %,
Temperature 60.0 °C		5944 psi
@Strain 32.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.98 MPa
@Strain 6.40 %,
Temperature 60.0 °C		5944 psi
@Strain 6.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.0 MPa
@Strain 38.0 %,
Temperature 60.0 °C		5950 psi
@Strain 38.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.0 MPa
@Strain 41.0 %,
Temperature 60.0 °C		5950 psi
@Strain 41.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.0 MPa
@Strain 1.40 %,
Temperature 0.000 °C		5950 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 41.01 MPa
@Strain 39.0 %,
Temperature 60.0 °C		5948 psi
@Strain 39.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.01 MPa
@Strain 40.0 %,
Temperature 60.0 °C		5948 psi
@Strain 40.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.01 MPa
@Strain 20.0 %,
Temperature 80.0 °C		5948 psi
@Strain 20.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.02 MPa
@Strain 36.0 %,
Temperature 60.0 °C		5949 psi
@Strain 36.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.03 MPa
@Strain 34.0 %,
Temperature 60.0 °C		5951 psi
@Strain 34.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.03 MPa
@Strain 35.0 %,
Temperature 60.0 °C		5951 psi
@Strain 35.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.05 MPa
@Strain 37.0 %,
Temperature 60.0 °C		5954 psi
@Strain 37.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.15 MPa
@Strain 1.30 %,
Temperature -40.0 °C		5968 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 41.23 MPa
@Strain 1.40 %,
Temperature 0.000 °C		5980 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 41.38 MPa
@Strain 21.0 %,
Temperature 80.0 °C		6002 psi
@Strain 21.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.54 MPa
@Strain 9.00 %,
Temperature 23.0 °C		6025 psi
@Strain 9.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 41.65 MPa
@Strain 6.90 %,
Temperature 60.0 °C		6041 psi
@Strain 6.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.8 MPa
@Strain 22.0 %,
Temperature 80.0 °C		6060 psi
@Strain 22.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.07 MPa
@Strain 23.0 %,
Temperature 80.0 °C		6102 psi
@Strain 23.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.26 MPa
@Strain 7.40 %,
Temperature 60.0 °C		6129 psi
@Strain 7.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.37 MPa
@Strain 24.0 %,
Temperature 80.0 °C		6145 psi
@Strain 24.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.39 MPa
@Strain 9.50 %,
Temperature 23.0 °C		6148 psi
@Strain 9.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 42.58 MPa
@Strain 25.0 %,
Temperature 80.0 °C		6176 psi
@Strain 25.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.83 MPa
@Strain 26.0 %,
Temperature 80.0 °C		6212 psi
@Strain 26.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.83 MPa
@Strain 1.50 %,
Temperature 0.000 °C		6212 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 42.98 MPa
@Strain 7.90 %,
Temperature 60.0 °C		6234 psi
@Strain 7.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.98 MPa
@Strain 1.10 %,
Temperature -40.0 °C		6234 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 43.07 MPa
@Strain 27.0 %,
Temperature 80.0 °C		6247 psi
@Strain 27.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.26 MPa
@Strain 10.0 %,
Temperature 23.0 °C		6274 psi
@Strain 10.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.27 MPa
@Strain 28.0 %,
Temperature 80.0 °C		6276 psi
@Strain 28.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.47 MPa
@Strain 29.0 %,
Temperature 80.0 °C		6305 psi
@Strain 29.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.61 MPa
@Strain 8.40 %,
Temperature 60.0 °C		6325 psi
@Strain 8.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.64 MPa
@Strain 30.0 %,
Temperature 80.0 °C		6329 psi
@Strain 30.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.77 MPa
@Strain 31.0 %,
Temperature 80.0 °C		6348 psi
@Strain 31.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.79 MPa
@Strain 1.50 %,
Temperature 23.0 °C		6351 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.9 MPa
@Strain 32.0 %,
Temperature 80.0 °C		6370 psi
@Strain 32.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.09 MPa
@Strain 33.0 %,
Temperature 80.0 °C		6395 psi
@Strain 33.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.15 MPa
@Strain 8.90 %,
Temperature 60.0 °C		6403 psi
@Strain 8.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.17 MPa
@Strain 34.0 %,
Temperature 80.0 °C		6406 psi
@Strain 34.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.22 MPa
@Strain 1.40 %,
Temperature -40.0 °C		6414 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 44.23 MPa
@Strain 1.50 %,
Temperature 0.000 °C		6415 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 44.25 MPa
@Strain 35.0 %,
Temperature 80.0 °C		6418 psi
@Strain 35.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.37 MPa
@Strain 36.0 %,
Temperature 80.0 °C		6435 psi
@Strain 36.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.44 MPa
@Strain 37.0 %,
Temperature 80.0 °C		6445 psi
@Strain 37.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.45 MPa
@Strain 11.0 %,
Temperature 23.0 °C		6447 psi
@Strain 11.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.54 MPa
@Strain 1.60 %,
Temperature 0.000 °C		6460 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 44.57 MPa
@Strain 38.0 %,
Temperature 80.0 °C		6464 psi
@Strain 38.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.65 MPa
@Strain 39.0 %,
Temperature 80.0 °C		6476 psi
@Strain 39.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.77 MPa
@Strain 40.0 %,
Temperature 80.0 °C		6493 psi
@Strain 40.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.82 MPa
@Strain 41.0 %,
Temperature 80.0 °C		6501 psi
@Strain 41.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.82 MPa
@Strain 9.40 %,
Temperature 60.0 °C		6501 psi
@Strain 9.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.87 MPa
@Strain 42.0 %,
Temperature 80.0 °C		6508 psi
@Strain 42.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.9 MPa
@Strain 43.0 %,
Temperature 80.0 °C		6510 psi
@Strain 43.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.95 MPa
@Strain 44.0 %,
Temperature 80.0 °C		6519 psi
@Strain 44.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.07 MPa
@Strain 45.0 %,
Temperature 80.0 °C		6537 psi
@Strain 45.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.1 MPa
@Strain 46.0 %,
Temperature 80.0 °C		6540 psi
@Strain 46.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.1 MPa
@Strain 47.0 %,
Temperature 80.0 °C		6540 psi
@Strain 47.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.19 MPa
@Strain 48.0 %,
Temperature 80.0 °C		6554 psi
@Strain 48.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.22 MPa
@Strain 49.0 %,
Temperature 80.0 °C		6559 psi
@Strain 49.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.22 MPa
@Strain 50.0 %,
Temperature 80.0 °C		6559 psi
@Strain 50.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.33 MPa
@Strain 9.90 %,
Temperature 60.0 °C		6575 psi
@Strain 9.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.68 MPa
@Strain 1.20 %,
Temperature -40.0 °C		6625 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 45.74 MPa
@Strain 12.0 %,
Temperature 23.0 °C		6634 psi
@Strain 12.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.3 MPa
@Strain 10.9 %,
Temperature 60.0 °C		6720 psi
@Strain 10.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.55 MPa
@Strain 1.70 %,
Temperature 0.000 °C		6752 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 46.57 MPa
@Strain 1.60 %,
Temperature 23.0 °C		6754 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 46.77 MPa
@Strain 13.0 %,
Temperature 23.0 °C		6783 psi
@Strain 13.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.04 MPa
@Strain 1.60 %,
Temperature 0.000 °C		6823 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 47.2 MPa
@Strain 1.50 %,
Temperature -40.0 °C		6850 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 47.34 MPa
@Strain 11.9 %,
Temperature 60.0 °C		6866 psi
@Strain 11.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 47.65 MPa
@Strain 14.0 %,
Temperature 23.0 °C		6911 psi
@Strain 14.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.22 MPa
@Strain 12.9 %,
Temperature 60.0 °C		6994 psi
@Strain 12.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 48.49 MPa
@Strain 15.0 %,
Temperature 23.0 °C		7033 psi
@Strain 15.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.54 MPa
@Strain 1.80 %,
Temperature 0.000 °C		7040 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.57 MPa
@Strain 1.30 %,
Temperature -40.0 °C		7044 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 48.99 MPa
@Strain 13.9 %,
Temperature 60.0 °C		7105 psi
@Strain 13.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 49.15 MPa
@Strain 16.0 %,
Temperature 23.0 °C		7129 psi
@Strain 16.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.3 MPa
@Strain 1.70 %,
Temperature 23.0 °C		7150 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.45 MPa
@Strain 1.60 %,
Temperature -40.0 °C		7172 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 49.72 MPa
@Strain 14.9 %,
Temperature 60.0 °C		7211 psi
@Strain 14.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 49.75 MPa
@Strain 17.0 %,
Temperature 23.0 °C		7216 psi
@Strain 17.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.8 MPa
@Strain 1.70 %,
Temperature 0.000 °C		7220 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.27 MPa
@Strain 18.0 %,
Temperature 23.0 °C		7291 psi
@Strain 18.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.32 MPa
@Strain 15.9 %,
Temperature 60.0 °C		7298 psi
@Strain 15.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.42 MPa
@Strain 1.90 %,
Temperature 0.000 °C		7313 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 50.74 MPa
@Strain 19.0 %,
Temperature 23.0 °C		7359 psi
@Strain 19.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.88 MPa
@Strain 16.9 %,
Temperature 60.0 °C		7380 psi
@Strain 16.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.13 MPa
@Strain 20.0 %,
Temperature 23.0 °C		7416 psi
@Strain 20.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.4 MPa
@Strain 17.9 %,
Temperature 60.0 °C		7450 psi
@Strain 17.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.45 MPa
@Strain 21.0 %,
Temperature 23.0 °C		7462 psi
@Strain 21.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.73 MPa
@Strain 22.0 %,
Temperature 23.0 °C		7503 psi
@Strain 22.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.8 MPa
@Strain 50.0 %,
Temperature 23.0 °C		7510 psi
@Strain 50.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.82 MPa
@Strain 2.00 %,
Temperature 0.000 °C		7516 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 51.83 MPa
@Strain 49.0 %,
Temperature 23.0 °C		7517 psi
@Strain 49.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.83 MPa
@Strain 18.9 %,
Temperature 60.0 °C		7517 psi
@Strain 18.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.94 MPa
@Strain 48.0 %,
Temperature 23.0 °C		7533 psi
@Strain 48.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.96 MPa
@Strain 23.0 %,
Temperature 23.0 °C		7536 psi
@Strain 23.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.97 MPa
@Strain 1.80 %,
Temperature 23.0 °C		7538 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 52.04 MPa
@Strain 47.0 %,
Temperature 23.0 °C		7548 psi
@Strain 47.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.09 MPa
@Strain 46.0 %,
Temperature 23.0 °C		7555 psi
@Strain 46.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.09 MPa
@Strain 1.40 %,
Temperature -40.0 °C		7555 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 52.13 MPa
@Strain 45.0 %,
Temperature 23.0 °C		7561 psi
@Strain 45.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.14 MPa
@Strain 24.0 %,
Temperature 23.0 °C		7562 psi
@Strain 24.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.14 MPa
@Strain 19.9 %,
Temperature 60.0 °C		7562 psi
@Strain 19.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.19 MPa
@Strain 44.0 %,
Temperature 23.0 °C		7570 psi
@Strain 44.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.24 MPa
@Strain 43.0 %,
Temperature 23.0 °C		7577 psi
@Strain 43.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.24 MPa
@Strain 1.70 %,
Temperature -40.0 °C		7577 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 52.3 MPa
@Strain 42.0 %,
Temperature 23.0 °C		7590 psi
@Strain 42.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.3 MPa
@Strain 25.0 %,
Temperature 23.0 °C		7590 psi
@Strain 25.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.38 MPa
@Strain 41.0 %,
Temperature 23.0 °C		7597 psi
@Strain 41.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.41 MPa
@Strain 40.0 %,
Temperature 23.0 °C		7601 psi
@Strain 40.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.43 MPa
@Strain 26.0 %,
Temperature 23.0 °C		7604 psi
@Strain 26.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.44 MPa
@Strain 20.9 %,
Temperature 60.0 °C		7606 psi
@Strain 20.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.49 MPa
@Strain 1.80 %,
Temperature 0.000 °C		7613 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 52.5 MPa
@Strain 39.0 %,
Temperature 23.0 °C		7610 psi
@Strain 39.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.52 MPa
@Strain 38.0 %,
Temperature 23.0 °C		7617 psi
@Strain 38.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.53 MPa
@Strain 27.0 %,
Temperature 23.0 °C		7619 psi
@Strain 27.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.57 MPa
@Strain 28.0 %,
Temperature 23.0 °C		7625 psi
@Strain 28.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.57 MPa
@Strain 37.0 %,
Temperature 23.0 °C		7625 psi
@Strain 37.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.59 MPa
@Strain 36.0 %,
Temperature 23.0 °C		7628 psi
@Strain 36.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.63 MPa
@Strain 35.0 %,
Temperature 23.0 °C		7633 psi
@Strain 35.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.63 MPa
@Strain 29.0 %,
Temperature 23.0 °C		7633 psi
@Strain 29.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.67 MPa
@Strain 34.0 %,
Temperature 23.0 °C		7639 psi
@Strain 34.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.68 MPa
@Strain 30.0 %,
Temperature 23.0 °C		7641 psi
@Strain 30.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.68 MPa
@Strain 31.0 %,
Temperature 23.0 °C		7641 psi
@Strain 31.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.69 MPa
@Strain 32.0 %,
Temperature 23.0 °C		7642 psi
@Strain 32.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.7 MPa
@Strain 33.0 %,
Temperature 23.0 °C		7640 psi
@Strain 33.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.77 MPa
@Strain 21.9 %,
Temperature 60.0 °C		7654 psi
@Strain 21.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.99 MPa
@Strain 22.9 %,
Temperature 60.0 °C		7686 psi
@Strain 22.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.13 MPa
@Strain 2.10 %,
Temperature 0.000 °C		7706 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 53.19 MPa
@Strain 23.9 %,
Temperature 60.0 °C		7715 psi
@Strain 23.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.38 MPa
@Strain 24.9 %,
Temperature 60.0 °C		7742 psi
@Strain 24.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.53 MPa
@Strain 25.9 %,
Temperature 60.0 °C		7764 psi
@Strain 25.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.7 MPa
@Strain 26.9 %,
Temperature 60.0 °C		7790 psi
@Strain 26.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.8 MPa
@Strain 27.9 %,
Temperature 60.0 °C		7800 psi
@Strain 27.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.89 MPa
@Strain 28.9 %,
Temperature 60.0 °C		7816 psi
@Strain 28.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.96 MPa
@Strain 1.90 %,
Temperature 23.0 °C		7826 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 53.97 MPa
@Strain 29.9 %,
Temperature 60.0 °C		7828 psi
@Strain 29.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.99 MPa
@Strain 46.9 %,
Temperature 60.0 °C		7831 psi
@Strain 46.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.0 MPa
@Strain 48.9 %,
Temperature 60.0 °C		7830 psi
@Strain 48.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.0 MPa
@Strain 50.0 %,
Temperature 60.0 °C		7830 psi
@Strain 50.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.0 MPa
@Strain 30.9 %,
Temperature 60.0 °C		7830 psi
@Strain 30.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.01 MPa
@Strain 47.9 %,
Temperature 60.0 °C		7834 psi
@Strain 47.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.05 MPa
@Strain 45.9 %,
Temperature 60.0 °C		7839 psi
@Strain 45.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.05 MPa
@Strain 43.9 %,
Temperature 60.0 °C		7839 psi
@Strain 43.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.06 MPa
@Strain 44.9 %,
Temperature 60.0 °C		7841 psi
@Strain 44.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.07 MPa
@Strain 31.9 %,
Temperature 60.0 °C		7842 psi
@Strain 31.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.12 MPa
@Strain 32.9 %,
Temperature 60.0 °C		7849 psi
@Strain 32.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.12 MPa
@Strain 33.9 %,
Temperature 60.0 °C		7849 psi
@Strain 33.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.12 MPa
@Strain 42.9 %,
Temperature 60.0 °C		7849 psi
@Strain 42.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.13 MPa
@Strain 34.9 %,
Temperature 60.0 °C		7851 psi
@Strain 34.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.14 MPa
@Strain 41.9 %,
Temperature 60.0 °C		7852 psi
@Strain 41.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.15 MPa
@Strain 40.9 %,
Temperature 60.0 °C		7854 psi
@Strain 40.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.16 MPa
@Strain 38.9 %,
Temperature 60.0 °C		7855 psi
@Strain 38.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.17 MPa
@Strain 37.9 %,
Temperature 60.0 °C		7857 psi
@Strain 37.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.17 MPa
@Strain 35.9 %,
Temperature 60.0 °C		7857 psi
@Strain 35.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.19 MPa
@Strain 36.9 %,
Temperature 60.0 °C		7860 psi
@Strain 36.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.2 MPa
@Strain 39.9 %,
Temperature 60.0 °C		7860 psi
@Strain 39.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.27 MPa
@Strain 2.20 %,
Temperature 0.000 °C		7871 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 54.5 MPa
@Strain 1.90 %,
Temperature 0.000 °C		7900 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 55.38 MPa
@Strain 2.30 %,
Temperature 0.000 °C		8032 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 55.4 MPa
@Strain 1.80 %,
Temperature -40.0 °C		8040 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 55.43 MPa
@Strain 1.50 %,
Temperature -40.0 °C		8039 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 55.89 MPa
@Strain 2.00 %,
Temperature 23.0 °C		8106 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 56.45 MPa
@Strain 2.00 %,
Temperature 0.000 °C		8187 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 56.53 MPa
@Strain 2.40 %,
Temperature 0.000 °C		8199 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 57.5 MPa
@Strain 2.50 %,
Temperature 0.000 °C		8340 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 58.11 MPa
@Strain 1.90 %,
Temperature -40.0 °C		8428 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 58.25 MPa
@Strain 2.10 %,
Temperature 23.0 °C		8448 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.37 MPa
@Strain 2.60 %,
Temperature 0.000 °C		8466 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 58.68 MPa
@Strain 1.60 %,
Temperature -40.0 °C		8511 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 58.84 MPa
@Strain 2.10 %,
Temperature 0.000 °C		8534 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 59.15 MPa
@Strain 2.70 %,
Temperature 0.000 °C		8579 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 59.87 MPa
@Strain 2.80 %,
Temperature 0.000 °C		8683 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 60.46 MPa
@Strain 2.90 %,
Temperature 0.000 °C		8769 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 60.53 MPa
@Strain 41.0 %,
Temperature 23.0 °C		8779 psi
@Strain 41.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 60.78 MPa
@Strain 2.00 %,
Temperature -40.0 °C		8815 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 60.88 MPa
@Strain 3.00 %,
Temperature 0.000 °C		8830 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.07 MPa
@Strain 2.20 %,
Temperature 23.0 °C		8857 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 61.35 MPa
@Strain 3.10 %,
Temperature 0.000 °C		8898 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.39 MPa
@Strain 50.0 %,
Temperature 23.0 °C		8904 psi
@Strain 50.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 61.46 MPa
@Strain 1.70 %,
Temperature -40.0 °C		8914 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 61.52 MPa
@Strain 49.0 %,
Temperature 23.0 °C		8923 psi
@Strain 49.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 61.69 MPa
@Strain 2.20 %,
Temperature 0.000 °C		8947 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 61.7 MPa
@Strain 42.0 %,
Temperature 23.0 °C		8950 psi
@Strain 42.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 61.82 MPa
@Strain 48.0 %,
Temperature 23.0 °C		8966 psi
@Strain 48.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 61.88 MPa
@Strain 3.20 %,
Temperature 0.000 °C		8975 psi
@Strain 3.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.0 MPa
@Strain 47.0 %,
Temperature 23.0 °C		8990 psi
@Strain 47.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.21 MPa
@Strain 43.0 %,
Temperature 23.0 °C		9023 psi
@Strain 43.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.23 MPa
@Strain 46.0 %,
Temperature 23.0 °C		9026 psi
@Strain 46.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.25 MPa
@Strain 45.0 %,
Temperature 23.0 °C		9029 psi
@Strain 45.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.32 MPa
@Strain 3.30 %,
Temperature 0.000 °C		9039 psi
@Strain 3.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.34 MPa
@Strain 44.0 %,
Temperature 23.0 °C		9042 psi
@Strain 44.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.66 MPa
@Strain 3.40 %,
Temperature 0.000 °C		9088 psi
@Strain 3.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.88 MPa
@Strain 3.50 %,
Temperature 0.000 °C		9120 psi
@Strain 3.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.14 MPa
@Strain 40.0 %,
Temperature 23.0 °C		9158 psi
@Strain 40.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 63.16 MPa
@Strain 3.60 %,
Temperature 0.000 °C		9161 psi
@Strain 3.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.33 MPa
@Strain 2.10 %,
Temperature -40.0 °C		9185 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 63.41 MPa
@Strain 3.70 %,
Temperature 0.000 °C		9197 psi
@Strain 3.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.46 MPa
@Strain 2.30 %,
Temperature 23.0 °C		9204 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 63.66 MPa
@Strain 3.80 %,
Temperature 0.000 °C		9233 psi
@Strain 3.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.94 MPa
@Strain 3.90 %,
Temperature 0.000 °C		9274 psi
@Strain 3.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.1 MPa
@Strain 2.30 %,
Temperature 0.000 °C		9300 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 64.15 MPa
@Strain 1.80 %,
Temperature -40.0 °C		9304 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 64.19 MPa
@Strain 4.00 %,
Temperature 0.000 °C		9310 psi
@Strain 4.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.53 MPa
@Strain 4.10 %,
Temperature 0.000 °C		9359 psi
@Strain 4.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.78 MPa
@Strain 4.20 %,
Temperature 0.000 °C		9396 psi
@Strain 4.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.95 MPa
@Strain 4.30 %,
Temperature 0.000 °C		9420 psi
@Strain 4.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.17 MPa
@Strain 4.40 %,
Temperature 0.000 °C		9452 psi
@Strain 4.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.28 MPa
@Strain 4.50 %,
Temperature 0.000 °C		9468 psi
@Strain 4.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.39 MPa
@Strain 2.40 %,
Temperature 23.0 °C		9484 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.45 MPa
@Strain 4.60 %,
Temperature 0.000 °C		9493 psi
@Strain 4.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.59 MPa
@Strain 4.70 %,
Temperature 0.000 °C		9513 psi
@Strain 4.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.76 MPa
@Strain 37.9 %,
Temperature 0.000 °C		9538 psi
@Strain 37.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 65.78 MPa
@Strain 4.80 %,
Temperature 0.000 °C		9541 psi
@Strain 4.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.8 MPa
@Strain 2.20 %,
Temperature -40.0 °C		9540 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 66.03 MPa
@Strain 4.90 %,
Temperature 0.000 °C		9577 psi
@Strain 4.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.05 MPa
@Strain 2.40 %,
Temperature 0.000 °C		9580 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 66.34 MPa
@Strain 5.00 %,
Temperature 0.000 °C		9622 psi
@Strain 5.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.83 MPa
@Strain 5.50 %,
Temperature 0.000 °C		9693 psi
@Strain 5.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.27 MPa
@Strain 1.90 %,
Temperature -40.0 °C		9757 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 67.53 MPa
@Strain 38.9 %,
Temperature 0.000 °C		9794 psi
@Strain 38.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 67.55 MPa
@Strain 39.0 %,
Temperature 23.0 °C		9797 psi
@Strain 39.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.68 MPa
@Strain 2.50 %,
Temperature 23.0 °C		9816 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.74 MPa
@Strain 6.00 %,
Temperature 0.000 °C		9825 psi
@Strain 6.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.1 MPa
@Strain 36.9 %,
Temperature 0.000 °C		9880 psi
@Strain 36.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 68.25 MPa
@Strain 2.30 %,
Temperature -40.0 °C		9899 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 68.35 MPa
@Strain 6.50 %,
Temperature 0.000 °C		9913 psi
@Strain 6.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.36 MPa
@Strain 2.50 %,
Temperature 0.000 °C		9915 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 68.52 MPa
@Strain 39.9 %,
Temperature 0.000 °C		9938 psi
@Strain 39.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 68.98 MPa
@Strain 7.00 %,
Temperature 0.000 °C		10000 psi
@Strain 7.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.56 MPa
@Strain 7.50 %,
Temperature 0.000 °C		10090 psi
@Strain 7.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.73 MPa
@Strain 2.60 %,
Temperature 23.0 °C		10110 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 69.85 MPa
@Strain 2.00 %,
Temperature -40.0 °C		10130 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 70.09 MPa
@Strain 8.00 %,
Temperature 0.000 °C		10170 psi
@Strain 8.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.15 MPa
@Strain 2.40 %,
Temperature -40.0 °C		10170 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 70.37 MPa
@Strain 38.0 %,
Temperature 23.0 °C		10210 psi
@Strain 38.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 70.43 MPa
@Strain 2.60 %,
Temperature 0.000 °C		10220 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 70.73 MPa
@Strain 8.50 %,
Temperature 0.000 °C		10260 psi
@Strain 8.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 71.29 MPa
@Strain 9.00 %,
Temperature 0.000 °C		10340 psi
@Strain 9.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 71.37 MPa
@Strain 2.70 %,
Temperature 23.0 °C		10350 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 71.94 MPa
@Strain 9.50 %,
Temperature 0.000 °C		10430 psi
@Strain 9.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.09 MPa
@Strain 2.70 %,
Temperature 0.000 °C		10460 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 72.36 MPa
@Strain 2.10 %,
Temperature -40.0 °C		10490 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 72.43 MPa
@Strain 10.0 %,
Temperature 0.000 °C		10510 psi
@Strain 10.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.64 MPa
@Strain 2.50 %,
Temperature -40.0 °C		10540 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 72.85 MPa
@Strain 37.0 %,
Temperature 23.0 °C		10570 psi
@Strain 37.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.42 MPa
@Strain 11.0 %,
Temperature 0.000 °C		10650 psi
@Strain 11.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.81 MPa
@Strain 2.80 %,
Temperature 23.0 °C		10710 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.05 MPa
@Strain 35.9 %,
Temperature 0.000 °C		10740 psi
@Strain 35.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 74.13 MPa
@Strain 2.80 %,
Temperature 0.000 °C		10750 psi
@Strain 2.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 74.41 MPa
@Strain 12.0 %,
Temperature 0.000 °C		10790 psi
@Strain 12.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.63 MPa
@Strain 36.0 %,
Temperature 23.0 °C		10820 psi
@Strain 36.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.78 MPa
@Strain 2.20 %,
Temperature -40.0 °C		10850 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 74.83 MPa
@Strain 50.0 %,
Temperature 0.000 °C		10850 psi
@Strain 50.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.01 MPa
@Strain 2.60 %,
Temperature -40.0 °C		10880 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 75.03 MPa
@Strain 49.0 %,
Temperature 0.000 °C		10880 psi
@Strain 49.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.04 MPa
@Strain 13.0 %,
Temperature 0.000 °C		10880 psi
@Strain 13.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.22 MPa
@Strain 48.0 %,
Temperature 0.000 °C		10910 psi
@Strain 48.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.4 MPa
@Strain 2.90 %,
Temperature 23.0 °C		10900 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.46 MPa
@Strain 47.0 %,
Temperature 0.000 °C		10940 psi
@Strain 47.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.53 MPa
@Strain 14.0 %,
Temperature 0.000 °C		10950 psi
@Strain 14.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.69 MPa
@Strain 46.0 %,
Temperature 0.000 °C		10980 psi
@Strain 46.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.75 MPa
@Strain 35.0 %,
Temperature 23.0 °C		10990 psi
@Strain 35.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.92 MPa
@Strain 15.0 %,
Temperature 0.000 °C		11010 psi
@Strain 15.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.93 MPa
@Strain 45.0 %,
Temperature 0.000 °C		11010 psi
@Strain 45.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.12 MPa
@Strain 2.90 %,
Temperature 0.000 °C		11040 psi
@Strain 2.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.18 MPa
@Strain 44.0 %,
Temperature 0.000 °C		11050 psi
@Strain 44.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.33 MPa
@Strain 16.0 %,
Temperature 0.000 °C		11070 psi
@Strain 16.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.4 MPa
@Strain 43.0 %,
Temperature 0.000 °C		11100 psi
@Strain 43.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.49 MPa
@Strain 34.0 %,
Temperature 23.0 °C		11090 psi
@Strain 34.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 76.67 MPa
@Strain 42.0 %,
Temperature 0.000 °C		11120 psi
@Strain 42.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.74 MPa
@Strain 17.0 %,
Temperature 0.000 °C		11130 psi
@Strain 17.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.8 MPa
@Strain 3.00 %,
Temperature 23.0 °C		11100 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 76.84 MPa
@Strain 41.0 %,
Temperature 0.000 °C		11140 psi
@Strain 41.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.98 MPa
@Strain 33.0 %,
Temperature 23.0 °C		11170 psi
@Strain 33.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 77.02 MPa
@Strain 40.0 %,
Temperature 0.000 °C		11170 psi
@Strain 40.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.08 MPa
@Strain 18.0 %,
Temperature 0.000 °C		11180 psi
@Strain 18.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.13 MPa
@Strain 39.0 %,
Temperature 0.000 °C		11190 psi
@Strain 39.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.21 MPa
@Strain 2.30 %,
Temperature -40.0 °C		11200 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 77.3 MPa
@Strain 2.70 %,
Temperature -40.0 °C		11200 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 77.31 MPa
@Strain 38.0 %,
Temperature 0.000 °C		11210 psi
@Strain 38.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.43 MPa
@Strain 32.0 %,
Temperature 23.0 °C		11230 psi
@Strain 32.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 77.48 MPa
@Strain 37.0 %,
Temperature 0.000 °C		11240 psi
@Strain 37.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.49 MPa
@Strain 19.0 %,
Temperature 0.000 °C		11240 psi
@Strain 19.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.6 MPa
@Strain 3.00 %,
Temperature 0.000 °C		11300 psi
@Strain 3.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 77.6 MPa
@Strain 36.0 %,
Temperature 0.000 °C		11300 psi
@Strain 36.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.67 MPa
@Strain 35.0 %,
Temperature 0.000 °C		11270 psi
@Strain 35.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.72 MPa
@Strain 34.0 %,
Temperature 0.000 °C		11270 psi
@Strain 34.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.73 MPa
@Strain 33.0 %,
Temperature 0.000 °C		11270 psi
@Strain 33.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.73 MPa
@Strain 31.0 %,
Temperature 23.0 °C		11270 psi
@Strain 31.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 77.87 MPa
@Strain 32.0 %,
Temperature 0.000 °C		11290 psi
@Strain 32.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.87 MPa
@Strain 20.0 %,
Temperature 0.000 °C		11290 psi
@Strain 20.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.0 MPa
@Strain 30.0 %,
Temperature 23.0 °C		11300 psi
@Strain 30.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 78.11 MPa
@Strain 21.0 %,
Temperature 0.000 °C		11330 psi
@Strain 21.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.15 MPa
@Strain 31.0 %,
Temperature 0.000 °C		11330 psi
@Strain 31.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.24 MPa
@Strain 22.0 %,
Temperature 0.000 °C		11350 psi
@Strain 22.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.24 MPa
@Strain 29.0 %,
Temperature 23.0 °C		11350 psi
@Strain 29.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 78.29 MPa
@Strain 25.0 %,
Temperature 0.000 °C		11360 psi
@Strain 25.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.3 MPa
@Strain 23.0 %,
Temperature 0.000 °C		11400 psi
@Strain 23.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.3 MPa
@Strain 3.10 %,
Temperature 23.0 °C		11400 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 78.33 MPa
@Strain 26.0 %,
Temperature 0.000 °C		11360 psi
@Strain 26.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.34 MPa
@Strain 24.0 %,
Temperature 0.000 °C		11360 psi
@Strain 24.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.36 MPa
@Strain 30.0 %,
Temperature 0.000 °C		11370 psi
@Strain 30.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.45 MPa
@Strain 27.0 %,
Temperature 0.000 °C		11380 psi
@Strain 27.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.47 MPa
@Strain 29.0 %,
Temperature 0.000 °C		11380 psi
@Strain 29.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.5 MPa
@Strain 28.0 %,
Temperature 23.0 °C		11400 psi
@Strain 28.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 78.52 MPa
@Strain 28.0 %,
Temperature 0.000 °C		11390 psi
@Strain 28.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.79 MPa
@Strain 27.0 %,
Temperature 23.0 °C		11430 psi
@Strain 27.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 78.98 MPa
@Strain 26.0 %,
Temperature 23.0 °C		11460 psi
@Strain 26.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.0 MPa
@Strain 34.9 %,
Temperature 0.000 °C		11500 psi
@Strain 34.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 79.13 MPa
@Strain 25.0 %,
Temperature 23.0 °C		11480 psi
@Strain 25.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.22 MPa
@Strain 8.50 %,
Temperature 23.0 °C		11490 psi
@Strain 8.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.25 MPa
@Strain 9.00 %,
Temperature 23.0 °C		11490 psi
@Strain 9.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.26 MPa
@Strain 8.00 %,
Temperature 23.0 °C		11500 psi
@Strain 8.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.28 MPa
@Strain 9.50 %,
Temperature 23.0 °C		11500 psi
@Strain 9.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.28 MPa
@Strain 10.0 %,
Temperature 23.0 °C		11500 psi
@Strain 10.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.3 MPa
@Strain 24.0 %,
Temperature 23.0 °C		11500 psi
@Strain 24.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.36 MPa
@Strain 11.0 %,
Temperature 23.0 °C		11510 psi
@Strain 11.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.36 MPa
@Strain 7.50 %,
Temperature 23.0 °C		11510 psi
@Strain 7.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.42 MPa
@Strain 3.10 %,
Temperature 0.000 °C		11520 psi
@Strain 3.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 79.43 MPa
@Strain 12.0 %,
Temperature 23.0 °C		11520 psi
@Strain 12.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.44 MPa
@Strain 7.00 %,
Temperature 23.0 °C		11520 psi
@Strain 7.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.45 MPa
@Strain 23.0 %,
Temperature 23.0 °C		11520 psi
@Strain 23.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.5 MPa
@Strain 2.40 %,
Temperature -40.0 °C		11500 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 79.52 MPa
@Strain 13.0 %,
Temperature 23.0 °C		11530 psi
@Strain 13.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.57 MPa
@Strain 22.0 %,
Temperature 23.0 °C		11540 psi
@Strain 22.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.58 MPa
@Strain 6.50 %,
Temperature 23.0 °C		11540 psi
@Strain 6.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.64 MPa
@Strain 2.80 %,
Temperature -40.0 °C		11550 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 79.65 MPa
@Strain 21.0 %,
Temperature 23.0 °C		11550 psi
@Strain 21.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.65 MPa
@Strain 14.0 %,
Temperature 23.0 °C		11550 psi
@Strain 14.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.71 MPa
@Strain 15.0 %,
Temperature 23.0 °C		11560 psi
@Strain 15.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.71 MPa
@Strain 20.0 %,
Temperature 23.0 °C		11560 psi
@Strain 20.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.73 MPa
@Strain 16.0 %,
Temperature 23.0 °C		11560 psi
@Strain 16.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.73 MPa
@Strain 19.0 %,
Temperature 23.0 °C		11560 psi
@Strain 19.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.75 MPa
@Strain 17.0 %,
Temperature 23.0 °C		11570 psi
@Strain 17.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.78 MPa
@Strain 6.00 %,
Temperature 23.0 °C		11570 psi
@Strain 6.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.79 MPa
@Strain 18.0 %,
Temperature 23.0 °C		11570 psi
@Strain 18.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.14 MPa
@Strain 5.50 %,
Temperature 23.0 °C		11620 psi
@Strain 5.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.2 MPa
@Strain 3.20 %,
Temperature 23.0 °C		11600 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.53 MPa
@Strain 4.90 %,
Temperature 23.0 °C		11680 psi
@Strain 4.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.53 MPa
@Strain 5.00 %,
Temperature 23.0 °C		11680 psi
@Strain 5.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.58 MPa
@Strain 4.80 %,
Temperature 23.0 °C		11690 psi
@Strain 4.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.64 MPa
@Strain 4.70 %,
Temperature 23.0 °C		11700 psi
@Strain 4.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.76 MPa
@Strain 4.60 %,
Temperature 23.0 °C		11710 psi
@Strain 4.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.0 MPa
@Strain 4.40 %,
Temperature 23.0 °C		11700 psi
@Strain 4.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.0 MPa
@Strain 4.50 %,
Temperature 23.0 °C		11700 psi
@Strain 4.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.12 MPa
@Strain 4.30 %,
Temperature 23.0 °C		11770 psi
@Strain 4.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.16 MPa
@Strain 3.20 %,
Temperature 0.000 °C		11770 psi
@Strain 3.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 81.24 MPa
@Strain 4.20 %,
Temperature 23.0 °C		11780 psi
@Strain 4.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.25 MPa
@Strain 2.50 %,
Temperature -40.0 °C		11780 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 81.36 MPa
@Strain 4.10 %,
Temperature 23.0 °C		11800 psi
@Strain 4.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.47 MPa
@Strain 3.30 %,
Temperature 23.0 °C		11820 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.59 MPa
@Strain 3.90 %,
Temperature 23.0 °C		11830 psi
@Strain 3.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.59 MPa
@Strain 3.60 %,
Temperature 23.0 °C		11830 psi
@Strain 3.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.59 MPa
@Strain 3.70 %,
Temperature 23.0 °C		11830 psi
@Strain 3.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.59 MPa
@Strain 4.00 %,
Temperature 23.0 °C		11830 psi
@Strain 4.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.59 MPa
@Strain 3.40 %,
Temperature 23.0 °C		11830 psi
@Strain 3.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.65 MPa
@Strain 3.50 %,
Temperature 23.0 °C		11840 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.65 MPa
@Strain 3.80 %,
Temperature 23.0 °C		11840 psi
@Strain 3.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.81 MPa
@Strain 2.90 %,
Temperature -40.0 °C		11870 psi
@Strain 2.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 82.34 MPa
@Strain 3.30 %,
Temperature 0.000 °C		11940 psi
@Strain 3.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 82.53 MPa
@Strain 33.9 %,
Temperature 0.000 °C		11970 psi
@Strain 33.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 83.34 MPa
@Strain 2.60 %,
Temperature -40.0 °C		12090 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 83.43 MPa
@Strain 3.00 %,
Temperature -40.0 °C		12100 psi
@Strain 3.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 83.59 MPa
@Strain 3.40 %,
Temperature 0.000 °C		12120 psi
@Strain 3.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 84.19 MPa
@Strain 32.9 %,
Temperature 0.000 °C		12210 psi
@Strain 32.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 84.56 MPa
@Strain 31.9 %,
Temperature 0.000 °C		12260 psi
@Strain 31.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 84.89 MPa
@Strain 3.50 %,
Temperature 0.000 °C		12310 psi
@Strain 3.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 85.17 MPa
@Strain 3.10 %,
Temperature -40.0 °C		12350 psi
@Strain 3.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 85.41 MPa
@Strain 30.9 %,
Temperature 0.000 °C		12390 psi
@Strain 30.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 85.43 MPa
@Strain 2.70 %,
Temperature -40.0 °C		12390 psi
@Strain 2.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 85.78 MPa
@Strain 3.60 %,
Temperature 0.000 °C		12440 psi
@Strain 3.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 86.13 MPa
@Strain 29.9 %,
Temperature 0.000 °C		12490 psi
@Strain 29.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 86.68 MPa
@Strain 28.9 %,
Temperature 0.000 °C		12570 psi
@Strain 28.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 86.84 MPa
@Strain 3.70 %,
Temperature 0.000 °C		12600 psi
@Strain 3.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.13 MPa
@Strain 2.80 %,
Temperature -40.0 °C		12640 psi
@Strain 2.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 87.28 MPa
@Strain 25.9 %,
Temperature 0.000 °C		12660 psi
@Strain 25.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.29 MPa
@Strain 27.9 %,
Temperature 0.000 °C		12660 psi
@Strain 27.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.29 MPa
@Strain 3.20 %,
Temperature -40.0 °C		12660 psi
@Strain 3.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 87.52 MPa
@Strain 26.9 %,
Temperature 0.000 °C		12690 psi
@Strain 26.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.66 MPa
@Strain 24.9 %,
Temperature 0.000 °C		12710 psi
@Strain 24.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.7 MPa
@Strain 23.9 %,
Temperature 0.000 °C		12700 psi
@Strain 23.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.71 MPa
@Strain 20.9 %,
Temperature 0.000 °C		12720 psi
@Strain 20.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.85 MPa
@Strain 22.9 %,
Temperature 0.000 °C		12740 psi
@Strain 22.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.85 MPa
@Strain 3.80 %,
Temperature 0.000 °C		12740 psi
@Strain 3.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.86 MPa
@Strain 15.9 %,
Temperature 0.000 °C		12740 psi
@Strain 15.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.92 MPa
@Strain 19.9 %,
Temperature 0.000 °C		12750 psi
@Strain 19.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.98 MPa
@Strain 18.9 %,
Temperature 0.000 °C		12760 psi
@Strain 18.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.05 MPa
@Strain 21.9 %,
Temperature 0.000 °C		12770 psi
@Strain 21.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.07 MPa
@Strain 13.9 %,
Temperature 0.000 °C		12770 psi
@Strain 13.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.08 MPa
@Strain 14.9 %,
Temperature 0.000 °C		12770 psi
@Strain 14.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.1 MPa
@Strain 17.9 %,
Temperature 0.000 °C		12800 psi
@Strain 17.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.15 MPa
@Strain 16.9 %,
Temperature 0.000 °C		12790 psi
@Strain 16.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.25 MPa
@Strain 12.9 %,
Temperature 0.000 °C		12800 psi
@Strain 12.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.38 MPa
@Strain 11.9 %,
Temperature 0.000 °C		12820 psi
@Strain 11.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.5 MPa
@Strain 3.90 %,
Temperature 0.000 °C		12800 psi
@Strain 3.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.68 MPa
@Strain 10.9 %,
Temperature 0.000 °C		12860 psi
@Strain 10.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.83 MPa
@Strain 3.30 %,
Temperature -40.0 °C		12880 psi
@Strain 3.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 89.0 MPa
@Strain 9.90 %,
Temperature 0.000 °C		12900 psi
@Strain 9.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.04 MPa
@Strain 9.40 %,
Temperature 0.000 °C		12910 psi
@Strain 9.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.04 MPa
@Strain 4.00 %,
Temperature 0.000 °C		12910 psi
@Strain 4.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.1 MPa
@Strain 2.90 %,
Temperature -40.0 °C		12900 psi
@Strain 2.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 89.25 MPa
@Strain 8.90 %,
Temperature 0.000 °C		12940 psi
@Strain 8.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.57 MPa
@Strain 8.40 %,
Temperature 0.000 °C		12990 psi
@Strain 8.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.63 MPa
@Strain 4.10 %,
Temperature 0.000 °C		13000 psi
@Strain 4.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.89 MPa
@Strain 7.90 %,
Temperature 0.000 °C		13040 psi
@Strain 7.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.12 MPa
@Strain 7.40 %,
Temperature 0.000 °C		13070 psi
@Strain 7.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.16 MPa
@Strain 4.20 %,
Temperature 0.000 °C		13080 psi
@Strain 4.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.43 MPa
@Strain 3.40 %,
Temperature -40.0 °C		13120 psi
@Strain 3.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 90.44 MPa
@Strain 6.90 %,
Temperature 0.000 °C		13120 psi
@Strain 6.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.58 MPa
@Strain 4.30 %,
Temperature 0.000 °C		13140 psi
@Strain 4.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.97 MPa
@Strain 6.40 %,
Temperature 0.000 °C		13190 psi
@Strain 6.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.98 MPa
@Strain 3.00 %,
Temperature -40.0 °C		13200 psi
@Strain 3.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 90.99 MPa
@Strain 4.40 %,
Temperature 0.000 °C		13200 psi
@Strain 4.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.11 MPa
@Strain 4.50 %,
Temperature 0.000 °C		13210 psi
@Strain 4.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.35 MPa
@Strain 4.60 %,
Temperature 0.000 °C		13250 psi
@Strain 4.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.46 MPa
@Strain 4.70 %,
Temperature 0.000 °C		13270 psi
@Strain 4.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.46 MPa
@Strain 5.90 %,
Temperature 0.000 °C		13270 psi
@Strain 5.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.58 MPa
@Strain 4.80 %,
Temperature 0.000 °C		13280 psi
@Strain 4.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.64 MPa
@Strain 4.90 %,
Temperature 0.000 °C		13290 psi
@Strain 4.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.74 MPa
@Strain 5.40 %,
Temperature 0.000 °C		13310 psi
@Strain 5.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.97 MPa
@Strain 3.50 %,
Temperature -40.0 °C		13340 psi
@Strain 3.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 92.4 MPa
@Strain 3.10 %,
Temperature -40.0 °C		13400 psi
@Strain 3.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 93.51 MPa
@Strain 3.60 %,
Temperature -40.0 °C		13560 psi
@Strain 3.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.77 MPa
@Strain 3.20 %,
Temperature -40.0 °C		13600 psi
@Strain 3.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 94.94 MPa
@Strain 3.70 %,
Temperature -40.0 °C		13770 psi
@Strain 3.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 95.08 MPa
@Strain 3.30 %,
Temperature -40.0 °C		13790 psi
@Strain 3.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 96.24 MPa
@Strain 3.80 %,
Temperature -40.0 °C		13960 psi
@Strain 3.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 96.39 MPa
@Strain 3.40 %,
Temperature -40.0 °C		13980 psi
@Strain 3.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 97.67 MPa
@Strain 3.50 %,
Temperature -40.0 °C		14170 psi
@Strain 3.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 97.78 MPa
@Strain 3.90 %,
Temperature -40.0 °C		14180 psi
@Strain 3.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 98.84 MPa
@Strain 3.60 %,
Temperature -40.0 °C		14340 psi
@Strain 3.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 99.03 MPa
@Strain 4.00 %,
Temperature -40.0 °C		14360 psi
@Strain 4.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 99.98 MPa
@Strain 3.70 %,
Temperature -40.0 °C		14500 psi
@Strain 3.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 100.27 MPa
@Strain 4.10 %,
Temperature -40.0 °C		14543 psi
@Strain 4.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 100.99 MPa
@Strain 3.80 %,
Temperature -40.0 °C		14647 psi
@Strain 3.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 101.4 MPa
@Strain 4.20 %,
Temperature -40.0 °C		14710 psi
@Strain 4.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 101.96 MPa
@Strain 3.90 %,
Temperature -40.0 °C		14788 psi
@Strain 3.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 102.53 MPa
@Strain 4.30 %,
Temperature -40.0 °C		14871 psi
@Strain 4.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 102.91 MPa
@Strain 4.00 %,
Temperature -40.0 °C		14926 psi
@Strain 4.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 103.65 MPa
@Strain 4.40 %,
Temperature -40.0 °C		15033 psi
@Strain 4.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 103.74 MPa
@Strain 4.10 %,
Temperature -40.0 °C		15046 psi
@Strain 4.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 104.14 MPa
@Strain 33.0 %,
Temperature -40.0 °C		15104 psi
@Strain 33.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 104.44 MPa
@Strain 4.20 %,
Temperature -40.0 °C		15148 psi
@Strain 4.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 104.54 MPa
@Strain 4.50 %,
Temperature -40.0 °C		15162 psi
@Strain 4.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 105.25 MPa
@Strain 4.60 %,
Temperature -40.0 °C		15265 psi
@Strain 4.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 105.31 MPa
@Strain 4.30 %,
Temperature -40.0 °C		15274 psi
@Strain 4.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 105.91 MPa
@Strain 4.70 %,
Temperature -40.0 °C		15361 psi
@Strain 4.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 106 MPa
@Strain 4.40 %,
Temperature -40.0 °C		15400 psi
@Strain 4.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 106.27 MPa
@Strain 32.0 %,
Temperature -40.0 °C		15413 psi
@Strain 32.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 106.59 MPa
@Strain 35.0 %,
Temperature -40.0 °C		15460 psi
@Strain 35.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 106.73 MPa
@Strain 4.50 %,
Temperature -40.0 °C		15480 psi
@Strain 4.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 106.8 MPa
@Strain 4.80 %,
Temperature -40.0 °C		15490 psi
@Strain 4.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 107.15 MPa
@Strain 4.60 %,
Temperature -40.0 °C		15541 psi
@Strain 4.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.16 MPa
@Strain 31.0 %,
Temperature -40.0 °C		15542 psi
@Strain 31.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 107.27 MPa
@Strain 4.90 %,
Temperature -40.0 °C		15558 psi
@Strain 4.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 107.62 MPa
@Strain 4.70 %,
Temperature -40.0 °C		15609 psi
@Strain 4.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.95 MPa
@Strain 30.0 %,
Temperature -40.0 °C		15657 psi
@Strain 30.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 107.98 MPa
@Strain 5.00 %,
Temperature -40.0 °C		15661 psi
@Strain 5.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108.18 MPa
@Strain 4.80 %,
Temperature -40.0 °C		15690 psi
@Strain 4.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 108.69 MPa
@Strain 29.0 %,
Temperature -40.0 °C		15764 psi
@Strain 29.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108.76 MPa
@Strain 4.90 %,
Temperature -40.0 °C		15774 psi
@Strain 4.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 108.99 MPa
@Strain 28.0 %,
Temperature -40.0 °C		15808 psi
@Strain 28.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 109.15 MPa
@Strain 5.00 %,
Temperature -40.0 °C		15831 psi
@Strain 5.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.35 MPa
@Strain 27.0 %,
Temperature -40.0 °C		15860 psi
@Strain 27.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 109.9 MPa
@Strain 34.0 %,
Temperature -40.0 °C		15940 psi
@Strain 34.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.97 MPa
@Strain 26.0 %,
Temperature -40.0 °C		15950 psi
@Strain 26.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 110.18 MPa
@Strain 5.50 %,
Temperature -40.0 °C		15980 psi
@Strain 5.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 110.26 MPa
@Strain 25.0 %,
Temperature -40.0 °C		15992 psi
@Strain 25.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 110.53 MPa
@Strain 5.50 %,
Temperature -40.0 °C		16031 psi
@Strain 5.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.59 MPa
@Strain 24.0 %,
Temperature -40.0 °C		16040 psi
@Strain 24.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 110.82 MPa
@Strain 33.0 %,
Temperature -40.0 °C		16073 psi
@Strain 33.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.42 MPa
@Strain 32.0 %,
Temperature -40.0 °C		16160 psi
@Strain 32.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.42 MPa
@Strain 23.0 %,
Temperature -40.0 °C		16160 psi
@Strain 23.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 111.8 MPa
@Strain 22.0 %,
Temperature -40.0 °C		16220 psi
@Strain 22.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 111.89 MPa
@Strain 31.0 %,
Temperature -40.0 °C		16228 psi
@Strain 31.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.09 MPa
@Strain 6.00 %,
Temperature -40.0 °C		16257 psi
@Strain 6.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.34 MPa
@Strain 30.0 %,
Temperature -40.0 °C		16294 psi
@Strain 30.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.44 MPa
@Strain 6.00 %,
Temperature -40.0 °C		16308 psi
@Strain 6.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 112.51 MPa
@Strain 15.0 %,
Temperature -40.0 °C		16318 psi
@Strain 15.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.52 MPa
@Strain 14.0 %,
Temperature -40.0 °C		16320 psi
@Strain 14.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.56 MPa
@Strain 21.0 %,
Temperature -40.0 °C		16325 psi
@Strain 21.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 112.62 MPa
@Strain 29.0 %,
Temperature -40.0 °C		16334 psi
@Strain 29.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.75 MPa
@Strain 13.0 %,
Temperature -40.0 °C		16353 psi
@Strain 13.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.77 MPa
@Strain 6.50 %,
Temperature -40.0 °C		16356 psi
@Strain 6.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.84 MPa
@Strain 16.0 %,
Temperature -40.0 °C		16366 psi
@Strain 16.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.94 MPa
@Strain 28.0 %,
Temperature -40.0 °C		16381 psi
@Strain 28.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.97 MPa
@Strain 12.0 %,
Temperature -40.0 °C		16385 psi
@Strain 12.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.19 MPa
@Strain 26.0 %,
Temperature -40.0 °C		16417 psi
@Strain 26.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.21 MPa
@Strain 17.0 %,
Temperature -40.0 °C		16420 psi
@Strain 17.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.22 MPa
@Strain 6.50 %,
Temperature -40.0 °C		16421 psi
@Strain 6.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.25 MPa
@Strain 27.0 %,
Temperature -40.0 °C		16426 psi
@Strain 27.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.3 MPa
@Strain 11.0 %,
Temperature -40.0 °C		16430 psi
@Strain 11.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.31 MPa
@Strain 25.0 %,
Temperature -40.0 °C		16434 psi
@Strain 25.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.34 MPa
@Strain 24.0 %,
Temperature -40.0 °C		16439 psi
@Strain 24.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.35 MPa
@Strain 18.0 %,
Temperature -40.0 °C		16440 psi
@Strain 18.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.35 MPa
@Strain 7.00 %,
Temperature -40.0 °C		16440 psi
@Strain 7.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.38 MPa
@Strain 20.0 %,
Temperature -40.0 °C		16444 psi
@Strain 20.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.41 MPa
@Strain 23.0 %,
Temperature -40.0 °C		16449 psi
@Strain 23.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.44 MPa
@Strain 22.0 %,
Temperature -40.0 °C		16453 psi
@Strain 22.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.47 MPa
@Strain 19.0 %,
Temperature -40.0 °C		16457 psi
@Strain 19.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.48 MPa
@Strain 21.0 %,
Temperature -40.0 °C		16459 psi
@Strain 21.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.49 MPa
@Strain 19.0 %,
Temperature -40.0 °C		16460 psi
@Strain 19.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.53 MPa
@Strain 10.0 %,
Temperature -40.0 °C		16466 psi
@Strain 10.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.53 MPa
@Strain 20.0 %,
Temperature -40.0 °C		16466 psi
@Strain 20.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.56 MPa
@Strain 7.50 %,
Temperature -40.0 °C		16471 psi
@Strain 7.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.58 MPa
@Strain 7.00 %,
Temperature -40.0 °C		16473 psi
@Strain 7.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.63 MPa
@Strain 9.50 %,
Temperature -40.0 °C		16481 psi
@Strain 9.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.73 MPa
@Strain 9.00 %,
Temperature -40.0 °C		16495 psi
@Strain 9.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.76 MPa
@Strain 8.50 %,
Temperature -40.0 °C		16500 psi
@Strain 8.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.82 MPa
@Strain 8.00 %,
Temperature -40.0 °C		16508 psi
@Strain 8.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.94 MPa
@Strain 18.0 %,
Temperature -40.0 °C		16526 psi
@Strain 18.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.02 MPa
@Strain 15.0 %,
Temperature -40.0 °C		16537 psi
@Strain 15.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.23 MPa
@Strain 16.0 %,
Temperature -40.0 °C		16568 psi
@Strain 16.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.58 MPa
@Strain 7.50 %,
Temperature -40.0 °C		16618 psi
@Strain 7.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.7 MPa
@Strain 17.0 %,
Temperature -40.0 °C		16640 psi
@Strain 17.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.81 MPa
@Strain 13.0 %,
Temperature -40.0 °C		16652 psi
@Strain 13.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.81 MPa
@Strain 14.0 %,
Temperature -40.0 °C		16652 psi
@Strain 14.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115 MPa
@Strain 10.0 %,
Temperature -40.0 °C		16700 psi
@Strain 10.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.04 MPa
@Strain 9.50 %,
Temperature -40.0 °C		16685 psi
@Strain 9.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.15 MPa
@Strain 12.0 %,
Temperature -40.0 °C		16701 psi
@Strain 12.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.29 MPa
@Strain 8.00 %,
Temperature -40.0 °C		16721 psi
@Strain 8.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.33 MPa
@Strain 9.00 %,
Temperature -40.0 °C		16727 psi
@Strain 9.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.48 MPa
@Strain 8.50 %,
Temperature -40.0 °C		16749 psi
@Strain 8.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.71 MPa
@Strain 11.0 %,
Temperature -40.0 °C		16782 psi
@Strain 11.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Tensile Strength, Yield  55.0 MPa
@Temperature 23.0 °C		7980 psi
@Temperature 73.4 °F		50%RH; ISO 527
 82.0 MPa
@Temperature 23.0 °C		11900 psi
@Temperature 73.4 °F		DAM; ISO 527
 83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		DAM; ASTM D638
Elongation at Break  20 %
@Temperature 23.0 °C		20 %
@Temperature 73.4 °F		DAM; nominal; ISO 527
 40 %
@Temperature 23.0 °C		40 %
@Temperature 73.4 °F		50mm/min; DAM; ISO 527
 50 %
@Temperature 23.0 °C		50 %
@Temperature 73.4 °F		DAM; ASTM D638
 >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 >= 100 %
@Temperature 23.0 °C		>= 100 %
@Temperature 73.4 °F		50mm/min; 50%RH; ISO 527
 >= 100 %
@Temperature 23.0 °C		>= 100 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 >= 300 %
@Temperature 23.0 °C		>= 300 %
@Temperature 73.4 °F		50%RH; ASTM D638
Elongation at Yield  4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 4.5 %
@Temperature 23.0 °C		4.5 %
@Temperature 73.4 °F		DAM; ISO 527
 25 %
@Temperature 23.0 °C		25 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  1.40 GPa
@Temperature 23.0 °C		203 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 3.10 GPa
@Temperature 23.0 °C		450 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  0.500 GPa
@Temperature 121 °C		72.5 ksi
@Temperature 250 °F		DAM; ASTM D790
 0.700 GPa
@Temperature 77.0 °C		102 ksi
@Temperature 171 °F		DAM; ASTM D790
 1.20 GPa
@Temperature 23.0 °C		174 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 1.21 GPa
@Temperature 23.0 °C		175 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 2.80 GPa
@Temperature 23.0 °C		406 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 2.80 GPa
@Temperature 23.0 °C		406 ksi
@Temperature 73.4 °F		DAM; ISO 178
 3.20 GPa
@Temperature -40.0 °C		464 ksi
@Temperature -40.0 °F		DAM; ASTM D790
Izod Impact, Notched  0.320 J/cm
@Temperature -40.0 °C		0.599 ft-lb/in
@Temperature -40.0 °F		DAM; ASTM D256
 0.530 J/cm
@Temperature 23.0 °C		0.993 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 1.05 J/cm
@Temperature 23.0 °C		1.97 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  4.00 kJ/m²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 5.50 kJ/m²
@Temperature -40.0 °C		2.62 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 5.50 kJ/m²
@Temperature 23.0 °C		2.62 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 6.00 kJ/m²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 11.0 kJ/m²
@Temperature 23.0 °C		5.23 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  300 kJ/m²
@Temperature -30.0 °C		143 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 300 kJ/m²
@Temperature 23.0 °C		143 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 180/1U
Charpy Impact Unnotched  40.0 J/cm²
@Temperature -30.0 °C		190 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.300 J/cm²
@Temperature -40.0 °C		1.43 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.300 J/cm²
@Temperature -30.0 °C		1.43 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.450 J/cm²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.600 J/cm²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 1.30 J/cm²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour 1400 MPa
@Temperature 23.0 °C		203000 psi
@Temperature 73.4 °F		50%RH; ISO 899
Tensile Creep Modulus, 1000 hours 930 MPa
@Temperature 23.0 °C		135000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; ASTM D257
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
 >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+16 ohm-cm
@Temperature 23.0 °C		1.00e+16 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
Surface Resistance  1.00e+12 ohm
@Temperature 23.0 °C		1.00e+12 ohm
@Temperature 73.4 °F		DAM; IEC 60093
 1.00e+12 ohm
@Temperature 23.0 °C		1.00e+12 ohm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		DAM; ASTM D257
Dielectric Constant  3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 3.7
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.7
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.8
@Frequency 100 Hz,
Temperature 23.0 °C		3.8
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 3.9
@Frequency 1000 Hz,
Temperature 23.0 °C		3.9
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.0
@Frequency 1000 Hz,
Temperature 23.0 °C		4.0
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.1
@Frequency 100 Hz,
Temperature 23.0 °C		4.1
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 7.0
@Frequency 1000 Hz,
Temperature 23.0 °C		7.0
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 8.0
@Frequency 100 Hz,
Temperature 23.0 °C		8.0
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Dielectric Strength  16.5 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		419 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		DAM; Short Time; ASTM D149
 23.2 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		589 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		DAM; Short Time; ASTM D149
 26.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		660 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		50%RH; IEC 60243-1
 31.5 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		800 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.010
@Frequency 100 Hz,
Temperature 23.0 °C		0.010
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.014
@Frequency 100 Hz,
Temperature 23.0 °C		0.014
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.018
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.018
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.10
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.10
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Comparative Tracking Index  >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C
@Temperature 23.0 - 55.0 °C		61.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 110 µm/m-°C
@Temperature 23.0 - 55.0 °C		61.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 200 °C392 °FDAM; ISO 75-1/-2
 210 °C410 °FDAM; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C149 °FDAM; ASTM D648
 70.0 °C158 °FDAM; ISO 75-1/-2
Brittleness Temperature -80.0 °C-112 °FDAM; ASTM D746
 -65.0 °C-85.0 °F50%RH; ASTM D746
Glass Transition Temp, Tg 60.0 °C140 °F10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical  65.0 °C
@Thickness 0.400 mm		149 °F
@Thickness 0.0157 in		DAM; UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		DAM; UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		DAM; UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		DAM; UL 746B
 130 °C
@Thickness 0.710 mm		266 °F
@Thickness 0.0280 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 0.400 mm		149 °F
@Thickness 0.0157 in		DAM; UL 746B
 75.0 °C
@Thickness 0.710 mm		167 °F
@Thickness 0.0280 in		DAM; UL 746B
 75.0 °C
@Thickness 3.00 mm		167 °F
@Thickness 0.118 in		DAM; UL 746B
 75.0 °C
@Thickness 6.00 mm		167 °F
@Thickness 0.236 in		DAM; UL 746B
 75.0 °C
@Thickness 1.50 mm		167 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 0.400 mm		149 °F
@Thickness 0.0157 in		DAM; UL 746B
 85.0 °C
@Thickness 0.710 mm		185 °F
@Thickness 0.0280 in		DAM; UL 746B
 85.0 °C
@Thickness 3.00 mm		185 °F
@Thickness 0.118 in		DAM; UL 746B
 85.0 °C
@Thickness 6.00 mm		185 °F
@Thickness 0.236 in		DAM; UL 746B
 85.0 °C
@Thickness 1.50 mm		185 °F
@Thickness 0.0591 in		DAM; UL 746B
Flammability, UL94  V-2
@Thickness 0.400 mm		V-2
@Thickness 0.0157 in		DAM; IEC 60695-11-10
 V-2
@Thickness 0.710 mm		V-2
@Thickness 0.0280 in		DAM; IEC 60695-11-10
 V-2
@Thickness 1.50 mm		V-2
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 V-2
@Thickness 6.00 mm		V-2
@Thickness 0.236 in		DAM; IEC 60695-11-10
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; IEC 60695-11-10
 V-2
@Thickness 0.400 mm		V-2
@Thickness 0.0157 in		DAM; UL94
 V-2
@Thickness 0.710 mm		V-2
@Thickness 0.0280 in		DAM; UL94
 V-2
@Thickness 1.50 mm		V-2
@Thickness 0.0591 in		DAM; UL94
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; UL94
 V-2
@Thickness 6.00 mm		V-2
@Thickness 0.236 in		DAM; UL94
Oxygen Index 28 %28 %DAM; ISO 4589-1/-2
Glow Wire Test  725 °C
@Thickness 0.710 mm		1340 °F
@Thickness 0.0280 in		DAM; Ignition; IEC 60695-2-13
 750 °C
@Thickness 1.50 mm		1380 °F
@Thickness 0.0591 in		DAM; Ignition; IEC 60695-2-13
 800 °C
@Thickness 3.00 mm		1470 °F
@Thickness 0.118 in		DAM; Ignition; IEC 60695-2-13
 900 °C
@Thickness 0.400 mm		1650 °F
@Thickness 0.0157 in		DAM; Ignition; IEC 60695-2-13
 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 0.400 mm		1760 °F
@Thickness 0.0157 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 0.710 mm		1760 °F
@Thickness 0.0280 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 1.50 mm		1760 °F
@Thickness 0.0591 in		DAM; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 290 °C554 °FDAM; Optimum
 280 - 300 °C536 - 572 °FDAM
Mold Temperature 70.0 °C158 °FDAM; optimum
 50.0 - 90.0 °C122 - 194 °FDAM
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveLubricantDAM
 Mold ReleaseDAM
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesChemical Resistance, GoodDAM
 Cycle (Production), FastDAM
 Electrical Properties, GoodDAM
 Fatigue ResistantDAM
 Flow, HighDAM
 Fuel ResistantDAM
 Grease ResistantDAM
 LubricatedDAM
 Mold Release, GoodDAM
 Moldability, GoodDAM
 Molecular Wt., LowDAM
 Oil ResistantDAM
 Processability, GoodDAM
 Wear Resistance, GoodDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryUnreinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 ConnectorsDAM
 Electrical/Electronic ApplicationsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45432.html

免责声明: 本文 DuPont Performance Polymers Zytel® 101F NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4