- 密度 [g/cm3]: 1.14
- 拉伸强度 [MPa]: 88.0
- 弯曲模量 [MPa]: 2.80
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 88.0 MPa @Temperature 23.0 °C | 12800 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | 16 % @Temperature 23.0 °C | 16 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| Elongation at Yield | 4.6 % @Temperature 23.0 °C | 4.6 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 3.05 GPa @Temperature 23.0 °C | 442 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 2.80 GPa @Temperature 23.0 °C | 406 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Charpy Impact Unnotched | 13.4 J/cm² @Temperature -30.0 °C | 63.8 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| 20.3 J/cm² @Temperature 23.0 °C | 96.6 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.370 J/cm² @Temperature -30.0 °C | 1.76 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | ||
| 0.400 J/cm² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 0.400 mm | 149 °F @Thickness 0.0157 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 6.00 mm | 149 °F @Thickness 0.236 in | DAM; UL 746B | |||
| 130 °C @Thickness 0.710 mm | 266 °F @Thickness 0.0280 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.400 mm | 149 °F @Thickness 0.0157 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 6.00 mm | 149 °F @Thickness 0.236 in | DAM; UL 746B | |||
| 75.0 °C @Thickness 0.710 mm | 167 °F @Thickness 0.0280 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.400 mm | 149 °F @Thickness 0.0157 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 6.00 mm | 149 °F @Thickness 0.236 in | DAM; UL 746B | |||
| 85.0 °C @Thickness 0.710 mm | 185 °F @Thickness 0.0280 in | DAM; UL 746B | |||
| Flammability, UL94 | V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | DAM; IEC 60695-11-10 | ||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 0.710 mm | V-2 @Thickness 0.0280 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; UL94 | |||
| V-2 @Thickness 0.710 mm | V-2 @Thickness 0.0280 in | DAM; UL94 | |||
| V-2 @Thickness 0.400 mm | V-2 @Thickness 0.0157 in | DAM; UL94 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; UL94 | |||
| V-2 @Thickness 0.400 mm | V-2 @Thickness 0.0157 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | DAM; UL94 | |||
| V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | DAM; UL94 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; UL94 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; UL94 | |||
| Glow Wire Test | 725 °C @Thickness 0.710 mm | 1340 °F @Thickness 0.0280 in | DAM; Ignition; IEC 60695-2-13 | ||
| 750 °C @Thickness 1.50 mm | 1380 °F @Thickness 0.0591 in | DAM; Ignition; IEC 60695-2-13 | |||
| 800 °C @Thickness 3.00 mm | 1470 °F @Thickness 0.118 in | DAM; Ignition; IEC 60695-2-13 | |||
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | DAM; IEC 60695-2-12 | |||
| 960 °C @Thickness 0.710 mm | 1760 °F @Thickness 0.0280 in | DAM; IEC 60695-2-12 | |||
| 960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | DAM; IEC 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Unreinforced Resins | DAM | |||
| Resin Identification | PA66 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||