  3. PA66
  4. DuPont Performance Polymers Zytel® 8018HS NC010 Nylon 66

DuPont Performance Polymers Zytel® 8018HS NC010 Nylon 66

DuPont Performance Polymers Zytel® 8018HS NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 8018HS NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 8018HS NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 8018HS NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.19
  • 吸水率 [%]: 1.9
  • 缺口冲击强度: 1.4
  • 弯曲模量 [MPa]: 2.00
  • 热变形温度 [℃]: 246.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.19 g/cc1.19 g/ccDAM; ASTM D792
Density 1.19 g/cc0.0430 lb/in³DAM; ISO 1183
Filler Content 14 %14 %DAM
Water Absorption  1.9 %
@Thickness 1.00 mm,
Temperature 23.0 °C		1.9 %
@Thickness 0.0394 in,
Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 6.3 %
@Thickness 1.00 mm,
Temperature 23.0 °C		6.3 %
@Thickness 0.0394 in,
Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0080 cm/cm
@Thickness 2.00 mm		0.0080 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
@Thickness 2.00 mm		0.0070 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  58.0 MPa
@Temperature 23.0 °C		8410 psi
@Temperature 73.4 °F		50%RH; ISO 527
 85.0 MPa
@Temperature 23.0 °C		12300 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength  60.0 MPa
@Temperature 23.0 °C		8700 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 90.0 MPa
@Temperature 23.0 °C		13100 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  1.30 MPa
@Strain 0.100 %,
Temperature 80.0 °C		189 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 527
 3.159 MPa
@Strain 0.100 %,
Temperature 23.0 °C		458.2 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 527
 3.30 MPa
@Strain 0.200 %,
Temperature 80.0 °C		479 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 527
 4.80 MPa
@Strain 0.300 %,
Temperature 80.0 °C		696 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 527
 5.80 MPa
@Strain 0.400 %,
Temperature 80.0 °C		841 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 527
 7.70 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1120 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 527
 8.136 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1180 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 527
 9.60 MPa
@Strain 0.600 %,
Temperature 80.0 °C		1390 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 527
 11.3 MPa
@Strain 0.700 %,
Temperature 80.0 °C		1640 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 527
 12.172 MPa
@Strain 0.300 %,
Temperature 23.0 °C		1765.4 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 527
 12.7 MPa
@Strain 0.800 %,
Temperature 80.0 °C		1840 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 527
 14.0 MPa
@Strain 0.900 %,
Temperature 80.0 °C		2030 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 527
 15.3 MPa
@Strain 1.00 %,
Temperature 80.0 °C		2220 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 527
 15.3 MPa
@Strain 1.00 %,
Temperature 80.0 °C		2220 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 527
 15.385 MPa
@Strain 0.400 %,
Temperature 23.0 °C		2231.4 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 527
 16.4 MPa
@Strain 1.10 %,
Temperature 80.0 °C		2380 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 527
 17.6 MPa
@Strain 1.20 %,
Temperature 80.0 °C		2550 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 527
 18.6 MPa
@Strain 1.30 %,
Temperature 80.0 °C		2700 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 527
 19.7 MPa
@Strain 1.40 %,
Temperature 80.0 °C		2860 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 527
 19.985 MPa
@Strain 0.500 %,
Temperature 23.0 °C		2898.6 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 527
 20.0 MPa
@Strain 0.500 %,
Temperature 23.0 °C		2900 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 527
 20.7 MPa
@Strain 1.50 %,
Temperature 80.0 °C		3000 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 527
 21.7 MPa
@Strain 1.60 %,
Temperature 80.0 °C		3150 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 527
 22.7 MPa
@Strain 1.70 %,
Temperature 80.0 °C		3290 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 527
 23.6 MPa
@Strain 1.80 %,
Temperature 80.0 °C		3420 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 527
 23.932 MPa
@Strain 0.600 %,
Temperature 23.0 °C		3471.0 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 527
 24.5 MPa
@Strain 1.90 %,
Temperature 80.0 °C		3550 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 527
 25.3 MPa
@Strain 2.00 %,
Temperature 80.0 °C		3670 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 527
 25.3 MPa
@Strain 2.00 %,
Temperature 80.0 °C		3670 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 527
 26.0 MPa
@Strain 2.10 %,
Temperature 80.0 °C		3770 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 527
 26.9 MPa
@Strain 2.20 %,
Temperature 80.0 °C		3900 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 527
 27.575 MPa
@Strain 0.700 %,
Temperature 23.0 °C		3999.4 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 527
 27.7 MPa
@Strain 2.30 %,
Temperature 80.0 °C		4020 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 527
 28.3 MPa
@Strain 2.40 %,
Temperature 80.0 °C		4100 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 527
 29.3 MPa
@Strain 2.50 %,
Temperature 80.0 °C		4250 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 527
 29.9 MPa
@Strain 2.60 %,
Temperature 80.0 °C		4340 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 527
 30.6 MPa
@Strain 2.70 %,
Temperature 80.0 °C		4440 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 527
 31.236 MPa
@Strain 0.800 %,
Temperature 23.0 °C		4530.4 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 527
 31.4 MPa
@Strain 2.80 %,
Temperature 80.0 °C		4550 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 527
 32.1 MPa
@Strain 2.90 %,
Temperature 80.0 °C		4660 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 527
 32.7 MPa
@Strain 3.00 %,
Temperature 80.0 °C		4740 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 527
 33.3 MPa
@Strain 3.10 %,
Temperature 80.0 °C		4830 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 527
 33.8 MPa
@Strain 3.20 %,
Temperature 80.0 °C		4900 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 527
 34.4 MPa
@Strain 3.30 %,
Temperature 80.0 °C		4990 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 527
 34.807 MPa
@Strain 0.900 %,
Temperature 23.0 °C		5048.3 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 527
 35.0 MPa
@Strain 3.40 %,
Temperature 80.0 °C		5080 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 527
 35.4 MPa
@Strain 3.50 %,
Temperature 80.0 °C		5130 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 527
 36.1 MPa
@Strain 3.60 %,
Temperature 80.0 °C		5240 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 527
 36.6 MPa
@Strain 3.70 %,
Temperature 80.0 °C		5310 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 527
 37.1 MPa
@Strain 3.80 %,
Temperature 80.0 °C		5380 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 527
 37.6 MPa
@Strain 3.90 %,
Temperature 80.0 °C		5450 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 527
 38.1 MPa
@Strain 4.00 %,
Temperature 80.0 °C		5530 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 527
 38.1 MPa
@Strain 4.00 %,
Temperature 80.0 °C		5530 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 527
 38.378 MPa
@Strain 1.00 %,
Temperature 23.0 °C		5566.3 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 527
 38.4 MPa
@Strain 1.00 %,
Temperature 23.0 °C		5570 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 527
 38.5 MPa
@Strain 4.10 %,
Temperature 80.0 °C		5580 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 527
 38.9 MPa
@Strain 4.20 %,
Temperature 80.0 °C		5640 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 527
 39.3 MPa
@Strain 4.30 %,
Temperature 80.0 °C		5700 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 527
 39.6 MPa
@Strain 4.40 %,
Temperature 80.0 °C		5740 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 527
 40.2 MPa
@Strain 4.50 %,
Temperature 80.0 °C		5830 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 527
 40.6 MPa
@Strain 4.60 %,
Temperature 80.0 °C		5890 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 527
 40.9 MPa
@Strain 4.70 %,
Temperature 80.0 °C		5930 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 527
 41.4 MPa
@Strain 4.80 %,
Temperature 80.0 °C		6000 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 527
 41.7 MPa
@Strain 4.90 %,
Temperature 80.0 °C		6050 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 527
 41.85 MPa
@Strain 1.10 %,
Temperature 23.0 °C		6070 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 527
 42.0 MPa
@Strain 5.00 %,
Temperature 80.0 °C		6090 psi
@Strain 5.00 %,
Temperature 176 °F		DAM; ISO 527
 43.3 MPa
@Strain 5.50 %,
Temperature 80.0 °C		6280 psi
@Strain 5.50 %,
Temperature 176 °F		DAM; ISO 527
 44.9 MPa
@Strain 6.00 %,
Temperature 80.0 °C		6510 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 527
 44.9 MPa
@Strain 6.00 %,
Temperature 80.0 °C		6510 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 527
 45.153 MPa
@Strain 1.20 %,
Temperature 23.0 °C		6548.9 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 527
 46.1 MPa
@Strain 6.50 %,
Temperature 80.0 °C		6690 psi
@Strain 6.50 %,
Temperature 176 °F		DAM; ISO 527
 47.1 MPa
@Strain 7.00 %,
Temperature 80.0 °C		6830 psi
@Strain 7.00 %,
Temperature 176 °F		DAM; ISO 527
 48.0 MPa
@Strain 7.50 %,
Temperature 80.0 °C		6960 psi
@Strain 7.50 %,
Temperature 176 °F		DAM; ISO 527
 48.321 MPa
@Strain 1.30 %,
Temperature 23.0 °C		7008.4 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 527
 48.7 MPa
@Strain 8.00 %,
Temperature 80.0 °C		7060 psi
@Strain 8.00 %,
Temperature 176 °F		DAM; ISO 527
 48.7 MPa
@Strain 8.00 %,
Temperature 80.0 °C		7060 psi
@Strain 8.00 %,
Temperature 176 °F		DAM; ISO 527
 49.5 MPa
@Strain 8.50 %,
Temperature 80.0 °C		7180 psi
@Strain 8.50 %,
Temperature 176 °F		DAM; ISO 527
 50.1 MPa
@Strain 9.00 %,
Temperature 80.0 °C		7270 psi
@Strain 9.00 %,
Temperature 176 °F		DAM; ISO 527
 50.7 MPa
@Strain 9.50 %,
Temperature 80.0 °C		7350 psi
@Strain 9.50 %,
Temperature 176 °F		DAM; ISO 527
 51.2 MPa
@Strain 10.0 %,
Temperature 80.0 °C		7430 psi
@Strain 10.0 %,
Temperature 176 °F		DAM; ISO 527
 51.2 MPa
@Strain 10.0 %,
Temperature 80.0 °C		7430 psi
@Strain 10.0 %,
Temperature 176 °F		DAM; ISO 527
 51.292 MPa
@Strain 1.40 %,
Temperature 23.0 °C		7439.3 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 527
 52.0 MPa
@Strain 11.0 %,
Temperature 80.0 °C		7540 psi
@Strain 11.0 %,
Temperature 176 °F		DAM; ISO 527
 52.8 MPa
@Strain 12.0 %,
Temperature 80.0 °C		7660 psi
@Strain 12.0 %,
Temperature 176 °F		DAM; ISO 527
 52.8 MPa
@Strain 12.0 %,
Temperature 80.0 °C		7660 psi
@Strain 12.0 %,
Temperature 176 °F		DAM; ISO 527
 53.5 MPa
@Strain 13.0 %,
Temperature 80.0 °C		7760 psi
@Strain 13.0 %,
Temperature 176 °F		DAM; ISO 527
 54.0 MPa
@Strain 14.0 %,
Temperature 80.0 °C		7830 psi
@Strain 14.0 %,
Temperature 176 °F		DAM; ISO 527
 54.0 MPa
@Strain 14.0 %,
Temperature 80.0 °C		7830 psi
@Strain 14.0 %,
Temperature 176 °F		DAM; ISO 527
 54.3 MPa
@Strain 1.50 %,
Temperature 23.0 °C		7880 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 527
 54.318 MPa
@Strain 1.50 %,
Temperature 23.0 °C		7878.2 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 527
 54.4 MPa
@Strain 15.0 %,
Temperature 80.0 °C		7890 psi
@Strain 15.0 %,
Temperature 176 °F		DAM; ISO 527
 54.7 MPa
@Strain 16.0 %,
Temperature 80.0 °C		7930 psi
@Strain 16.0 %,
Temperature 176 °F		DAM; ISO 527
 54.7 MPa
@Strain 16.0 %,
Temperature 80.0 °C		7930 psi
@Strain 16.0 %,
Temperature 176 °F		DAM; ISO 527
 54.9 MPa
@Strain 17.0 %,
Temperature 80.0 °C		7960 psi
@Strain 17.0 %,
Temperature 176 °F		DAM; ISO 527
 55.1 MPa
@Strain 18.0 %,
Temperature 80.0 °C		7990 psi
@Strain 18.0 %,
Temperature 176 °F		DAM; ISO 527
 55.2 MPa
@Strain 19.0 %,
Temperature 80.0 °C		8010 psi
@Strain 19.0 %,
Temperature 176 °F		DAM; ISO 527
 55.3 MPa
@Strain 20.0 %,
Temperature 80.0 °C		8020 psi
@Strain 20.0 %,
Temperature 176 °F		DAM; ISO 527
 55.3 MPa
@Strain 20.0 %,
Temperature 80.0 °C		8020 psi
@Strain 20.0 %,
Temperature 176 °F		DAM; ISO 527
 57.074 MPa
@Strain 1.60 %,
Temperature 23.0 °C		8277.9 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 527
 59.607 MPa
@Strain 1.70 %,
Temperature 23.0 °C		8645.3 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 527
 62.167 MPa
@Strain 1.80 %,
Temperature 23.0 °C		9016.6 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 527
 64.377 MPa
@Strain 1.90 %,
Temperature 23.0 °C		9337.1 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 527
 66.597 MPa
@Strain 2.00 %,
Temperature 23.0 °C		9659.1 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 527
 66.6 MPa
@Strain 2.00 %,
Temperature 23.0 °C		9660 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 527
 68.602 MPa
@Strain 2.10 %,
Temperature 23.0 °C		9949.9 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 527
 70.41 MPa
@Strain 2.20 %,
Temperature 23.0 °C		10210 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 527
 72.101 MPa
@Strain 2.30 %,
Temperature 23.0 °C		10457 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 527
 73.596 MPa
@Strain 2.40 %,
Temperature 23.0 °C		10674 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 527
 74.956 MPa
@Strain 2.50 %,
Temperature 23.0 °C		10871 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 527
 75.0 MPa
@Strain 2.50 %,
Temperature 23.0 °C		10900 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 527
 76.147 MPa
@Strain 2.60 %,
Temperature 23.0 °C		11044 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 527
 77.283 MPa
@Strain 2.70 %,
Temperature 23.0 °C		11209 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 527
 78.348 MPa
@Strain 2.80 %,
Temperature 23.0 °C		11363 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 527
 79.288 MPa
@Strain 2.90 %,
Temperature 23.0 °C		11500 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 527
 80.1 MPa
@Strain 3.00 %,
Temperature 23.0 °C		11600 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 527
 80.129 MPa
@Strain 3.00 %,
Temperature 23.0 °C		11622 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 527
 80.854 MPa
@Strain 3.10 %,
Temperature 23.0 °C		11727 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 527
 81.543 MPa
@Strain 3.20 %,
Temperature 23.0 °C		11827 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 527
 82.179 MPa
@Strain 3.30 %,
Temperature 23.0 °C		11919 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 527
 82.779 MPa
@Strain 3.40 %,
Temperature 23.0 °C		12006 psi
@Strain 3.40 %,
Temperature 73.4 °F		DAM; ISO 527
 83.056 MPa
@Strain 9.00 %,
Temperature 23.0 °C		12046 psi
@Strain 9.00 %,
Temperature 73.4 °F		DAM; ISO 527
 83.271 MPa
@Strain 3.50 %,
Temperature 23.0 °C		12077 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; ISO 527
 83.3 MPa
@Strain 3.50 %,
Temperature 23.0 °C		12100 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; ISO 527
 83.414 MPa
@Strain 8.50 %,
Temperature 23.0 °C		12098 psi
@Strain 8.50 %,
Temperature 73.4 °F		DAM; ISO 527
 83.7 MPa
@Strain 3.60 %,
Temperature 23.0 °C		12100 psi
@Strain 3.60 %,
Temperature 73.4 °F		DAM; ISO 527
 83.79 MPa
@Strain 8.00 %,
Temperature 23.0 °C		12150 psi
@Strain 8.00 %,
Temperature 73.4 °F		DAM; ISO 527
 84.112 MPa
@Strain 3.70 %,
Temperature 23.0 °C		12199 psi
@Strain 3.70 %,
Temperature 73.4 °F		DAM; ISO 527
 84.148 MPa
@Strain 7.50 %,
Temperature 23.0 °C		12205 psi
@Strain 7.50 %,
Temperature 73.4 °F		DAM; ISO 527
 84.461 MPa
@Strain 3.80 %,
Temperature 23.0 °C		12250 psi
@Strain 3.80 %,
Temperature 73.4 °F		DAM; ISO 527
 84.604 MPa
@Strain 7.00 %,
Temperature 23.0 °C		12271 psi
@Strain 7.00 %,
Temperature 73.4 °F		DAM; ISO 527
 84.757 MPa
@Strain 3.90 %,
Temperature 23.0 °C		12293 psi
@Strain 3.90 %,
Temperature 73.4 °F		DAM; ISO 527
 84.962 MPa
@Strain 6.50 %,
Temperature 23.0 °C		12323 psi
@Strain 6.50 %,
Temperature 73.4 °F		DAM; ISO 527
 85.0 MPa
@Strain 4.00 %,
Temperature 23.0 °C		12300 psi
@Strain 4.00 %,
Temperature 73.4 °F		DAM; ISO 527
 85.025 MPa
@Strain 4.00 %,
Temperature 23.0 °C		12332 psi
@Strain 4.00 %,
Temperature 73.4 °F		DAM; ISO 527
 85.276 MPa
@Strain 4.10 %,
Temperature 23.0 °C		12368 psi
@Strain 4.10 %,
Temperature 73.4 °F		DAM; ISO 527
 85.294 MPa
@Strain 6.00 %,
Temperature 23.0 °C		12371 psi
@Strain 6.00 %,
Temperature 73.4 °F		DAM; ISO 527
 85.437 MPa
@Strain 4.20 %,
Temperature 23.0 °C		12392 psi
@Strain 4.20 %,
Temperature 73.4 °F		DAM; ISO 527
 85.562 MPa
@Strain 4.30 %,
Temperature 23.0 °C		12410 psi
@Strain 4.30 %,
Temperature 73.4 °F		DAM; ISO 527
 85.643 MPa
@Strain 5.50 %,
Temperature 23.0 °C		12421 psi
@Strain 5.50 %,
Temperature 73.4 °F		DAM; ISO 527
 85.705 MPa
@Strain 4.40 %,
Temperature 23.0 °C		12430 psi
@Strain 4.40 %,
Temperature 73.4 °F		DAM; ISO 527
 85.75 MPa
@Strain 4.50 %,
Temperature 23.0 °C		12440 psi
@Strain 4.50 %,
Temperature 73.4 °F		DAM; ISO 527
 85.8 MPa
@Strain 4.50 %,
Temperature 23.0 °C		12400 psi
@Strain 4.50 %,
Temperature 73.4 °F		DAM; ISO 527
 85.8 MPa
@Strain 5.00 %,
Temperature 23.0 °C		12400 psi
@Strain 5.00 %,
Temperature 73.4 °F		DAM; ISO 527
 85.804 MPa
@Strain 4.60 %,
Temperature 23.0 °C		12445 psi
@Strain 4.60 %,
Temperature 73.4 °F		DAM; ISO 527
 85.804 MPa
@Strain 4.70 %,
Temperature 23.0 °C		12445 psi
@Strain 4.70 %,
Temperature 73.4 °F		DAM; ISO 527
 85.804 MPa
@Strain 4.80 %,
Temperature 23.0 °C		12445 psi
@Strain 4.80 %,
Temperature 73.4 °F		DAM; ISO 527
 85.822 MPa
@Strain 4.90 %,
Temperature 23.0 °C		12447 psi
@Strain 4.90 %,
Temperature 73.4 °F		DAM; ISO 527
 85.839 MPa
@Strain 5.00 %,
Temperature 23.0 °C		12450 psi
@Strain 5.00 %,
Temperature 73.4 °F		DAM; ISO 527
Elongation at Break  6.0 %
@Temperature 23.0 °C		6.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 9.0 %
@Temperature 23.0 °C		9.0 %
@Temperature 73.4 °F		DAM; ISO 527
 14 %
@Temperature 23.0 °C		14 %
@Temperature 73.4 °F		50%RH; ASTM D638
 14 %
@Temperature 23.0 °C		14 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus 4.20 GPa
@Temperature 23.0 °C		609 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  2.00 GPa
@Temperature 23.0 °C		290 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 2.20 GPa
@Temperature 23.0 °C		319 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 3.60 GPa
@Temperature 23.0 °C		522 ksi
@Temperature 73.4 °F		DAM; ISO 178
 3.66 GPa
@Temperature 23.0 °C		531 ksi
@Temperature 73.4 °F		DAM; ASTM D790
Izod Impact, Notched  1.40 J/cm
@Temperature 23.0 °C		2.62 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 2.15 J/cm
@Temperature 23.0 °C		4.03 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Unnotched  9.60 J/cm
@Temperature 23.0 °C		18.0 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D4812
 10.65 J/cm
@Temperature 23.0 °C		19.95 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D4812
Izod Impact, Notched (ISO)  5.00 kJ/m²
@Temperature -40.0 °C		2.38 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 180/1A
 5.00 kJ/m²
@Temperature -30.0 °C		2.38 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 7.00 kJ/m²
@Temperature -40.0 °C		3.33 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 10.0 kJ/m²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 13.0 kJ/m²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 18.0 kJ/m²
@Temperature 23.0 °C		8.57 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  70.0 kJ/m²
@Temperature -30.0 °C		33.3 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1U
 90.0 kJ/m²
@Temperature -30.0 °C		42.8 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 90.0 kJ/m²
@Temperature 23.0 °C		42.8 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
 100 kJ/m²
@Temperature 23.0 °C		47.6 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1U
Charpy Impact Unnotched  7.50 J/cm²
@Temperature -30.0 °C		35.7 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 8.00 J/cm²
@Temperature -30.0 °C		38.1 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 8.00 J/cm²
@Temperature 23.0 °C		38.1 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 10.0 J/cm²
@Temperature 23.0 °C		47.6 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -40.0 °C		1.90 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.400 J/cm²
@Temperature -40.0 °C		1.90 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 179/1eA
 0.600 J/cm²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.600 J/cm²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 1.20 J/cm²
@Temperature 23.0 °C		5.71 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 1.80 J/cm²
@Temperature 23.0 °C		8.57 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index 580 V
@Temperature 23.0 °C		580 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  96.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		53.3 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 96.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		53.3 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 118 µm/m-°C
@Temperature 23.0 - 55.0 °C		65.6 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 118 µm/m-°C
@Temperature 23.0 - 55.0 °C		65.6 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 123 µm/m-°C
@Temperature 55.0 - 160 °C		68.3 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 123 µm/m-°C
@Temperature 55.0 - 160 °C		68.3 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 246 °C475 °FDAM; ISO 75-1/-2
 250 °C482 °FDAM; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 195 °C383 °FDAM; ISO 75-1/-2
 220 °C428 °FDAM; ASTM D648
UL RTI, Electrical  120 °C
@Thickness 3.00 mm		248 °F
@Thickness 0.118 in		DAM; UL 746B
 120 °C
@Thickness 1.50 mm		248 °F
@Thickness 0.0591 in		DAM; UL 746B
 120 °C
@Thickness 0.750 mm		248 °F
@Thickness 0.0295 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 0.750 mm		149 °F
@Thickness 0.0295 in		DAM; UL 746B
 95.0 °C
@Thickness 1.50 mm		203 °F
@Thickness 0.0591 in		DAM; UL 746B
 105 °C
@Thickness 3.00 mm		221 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical without Impact  85.0 °C
@Thickness 0.750 mm		185 °F
@Thickness 0.0295 in		DAM; UL 746B
 105 °C
@Thickness 3.00 mm		221 °F
@Thickness 0.118 in		DAM; UL 746B
 105 °C
@Thickness 1.50 mm		221 °F
@Thickness 0.0591 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; UL94
Oxygen Index 21 %21 %DAM; ISO 4589-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 263 °C505 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 50.0 - 100 °C122 - 212 °FDAM
 80.0 °C176 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveHeat StabilizerDAM
AppearanceColors AvailableDAM
 Natural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesImpact Resistance, HighDAM
 Toughness, GoodDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 66DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA66-IGF14<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
 Toughened ResinsDAM
Resin IdentificationPA66-IGF14ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 FastenersDAM
 Industrial ApplicationsDAM
 Sporting GoodsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45475.html

免责声明: 本文 DuPont Performance Polymers Zytel® 8018HS NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4