  4. DuPont Performance Polymers Zytel® 70K20HSL NC010 Nylon 66

DuPont Performance Polymers Zytel® 70K20HSL NC010 Nylon 66

DuPont Performance Polymers Zytel® 70K20HSL NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 70K20HSL NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 70K20HSL NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 70K20HSL NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.19
  • 吸水率 [%]: 2.7
  • 缺口冲击强度: 5.0
  • 弯曲模量 [MPa]: 3.30
  • 热变形温度 [℃]: 255.0
 
Physical PropertiesMetricEnglishComments
Density 1.19 g/cc0.0430 lb/in³DAM; ISO 1183
Water Absorption  2.7 %
@Temperature 23.0 °C		2.7 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 6.8 %
@Temperature 23.0 °C		6.8 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0090 cm/cm
@Thickness 2.00 mm		0.0090 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  85.0 MPa
@Temperature 23.0 °C		12300 psi
@Temperature 73.4 °F		50%RH; ISO 527
 110 MPa
@Temperature 23.0 °C		16000 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Stress  9.04 MPa
@Strain 0.820 %,
Temperature 150 °C		1310 psi
@Strain 0.820 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.04 MPa
@Strain 0.820 %,
Temperature 150 °C		1310 psi
@Strain 0.820 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.76 MPa
@Strain 0.840 %,
Temperature 120 °C		1561 psi
@Strain 0.840 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.76 MPa
@Strain 0.840 %,
Temperature 120 °C		1561 psi
@Strain 0.840 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.93 MPa
@Strain 0.860 %,
Temperature 90.0 °C		2020 psi
@Strain 0.860 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 13.93 MPa
@Strain 0.860 %,
Temperature 90.0 °C		2020 psi
@Strain 0.860 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 15.78 MPa
@Strain 1.64 %,
Temperature 150 °C		2289 psi
@Strain 1.64 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.78 MPa
@Strain 1.64 %,
Temperature 150 °C		2289 psi
@Strain 1.64 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.75 MPa
@Strain 1.69 %,
Temperature 120 °C		2719 psi
@Strain 1.69 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.75 MPa
@Strain 1.69 %,
Temperature 120 °C		2719 psi
@Strain 1.69 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.3 MPa
@Strain 2.45 %,
Temperature 150 °C		3090 psi
@Strain 2.45 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.3 MPa
@Strain 2.45 %,
Temperature 150 °C		3090 psi
@Strain 2.45 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.39 MPa
@Strain 0.830 %,
Temperature 60.0 °C		3392 psi
@Strain 0.830 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 23.39 MPa
@Strain 0.830 %,
Temperature 60.0 °C		3392 psi
@Strain 0.830 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.5 MPa
@Strain 1.70 %,
Temperature 90.0 °C		3410 psi
@Strain 1.70 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.5 MPa
@Strain 1.70 %,
Temperature 90.0 °C		3410 psi
@Strain 1.70 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 25.16 MPa
@Strain 2.51 %,
Temperature 120 °C		3649 psi
@Strain 2.51 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.16 MPa
@Strain 2.51 %,
Temperature 120 °C		3649 psi
@Strain 2.51 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.02 MPa
@Strain 0.540 %,
Temperature 23.0 °C		3774 psi
@Strain 0.540 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.02 MPa
@Strain 0.540 %,
Temperature 23.0 °C		3774 psi
@Strain 0.540 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 26.2 MPa
@Strain 3.25 %,
Temperature 150 °C		3800 psi
@Strain 3.25 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.2 MPa
@Strain 3.25 %,
Temperature 150 °C		3800 psi
@Strain 3.25 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 27.21 MPa
@Strain 0.540 %,
Temperature 0.000 °C		3946 psi
@Strain 0.540 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 27.21 MPa
@Strain 0.540 %,
Temperature 0.000 °C		3946 psi
@Strain 0.540 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 28.08 MPa
@Strain 0.660 %,
Temperature 40.0 °C		4073 psi
@Strain 0.660 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 28.08 MPa
@Strain 0.660 %,
Temperature 40.0 °C		4073 psi
@Strain 0.660 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 29.33 MPa
@Strain 0.560 %,
Temperature -20.0 °C		4254 psi
@Strain 0.560 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 29.33 MPa
@Strain 0.560 %,
Temperature -20.0 °C		4254 psi
@Strain 0.560 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 30.8 MPa
@Strain 4.08 %,
Temperature 150 °C		4470 psi
@Strain 4.08 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.8 MPa
@Strain 4.08 %,
Temperature 150 °C		4470 psi
@Strain 4.08 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 30.81 MPa
@Strain 2.52 %,
Temperature 90.0 °C		4469 psi
@Strain 2.52 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 30.81 MPa
@Strain 2.52 %,
Temperature 90.0 °C		4469 psi
@Strain 2.52 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 31.08 MPa
@Strain 3.36 %,
Temperature 120 °C		4508 psi
@Strain 3.36 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.08 MPa
@Strain 3.36 %,
Temperature 120 °C		4508 psi
@Strain 3.36 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.81 MPa
@Strain 4.88 %,
Temperature 150 °C		5049 psi
@Strain 4.88 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.81 MPa
@Strain 4.88 %,
Temperature 150 °C		5049 psi
@Strain 4.88 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.33 MPa
@Strain 4.18 %,
Temperature 120 °C		5269 psi
@Strain 4.18 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.33 MPa
@Strain 4.18 %,
Temperature 120 °C		5269 psi
@Strain 4.18 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.59 MPa
@Strain 3.36 %,
Temperature 90.0 °C		5452 psi
@Strain 3.36 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 37.59 MPa
@Strain 3.36 %,
Temperature 90.0 °C		5452 psi
@Strain 3.36 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 37.79 MPa
@Strain 5.68 %,
Temperature 150 °C		5481 psi
@Strain 5.68 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 37.79 MPa
@Strain 5.68 %,
Temperature 150 °C		5481 psi
@Strain 5.68 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.49 MPa
@Strain 1.63 %,
Temperature 60.0 °C		5728 psi
@Strain 1.63 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.49 MPa
@Strain 1.63 %,
Temperature 60.0 °C		5728 psi
@Strain 1.63 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 39.84 MPa
@Strain 6.51 %,
Temperature 150 °C		5778 psi
@Strain 6.51 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.84 MPa
@Strain 6.51 %,
Temperature 150 °C		5778 psi
@Strain 6.51 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.85 MPa
@Strain 7.31 %,
Temperature 150 °C		5925 psi
@Strain 7.31 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.85 MPa
@Strain 7.31 %,
Temperature 150 °C		5925 psi
@Strain 7.31 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 41.0 MPa
@Strain 5.03 %,
Temperature 120 °C		5950 psi
@Strain 5.03 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.0 MPa
@Strain 5.03 %,
Temperature 120 °C		5950 psi
@Strain 5.03 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.14 MPa
@Strain 8.11 %,
Temperature 150 °C		5967 psi
@Strain 8.11 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 41.14 MPa
@Strain 8.11 %,
Temperature 150 °C		5967 psi
@Strain 8.11 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.8 MPa
@Strain 4.20 %,
Temperature 90.0 °C		6350 psi
@Strain 4.20 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 43.8 MPa
@Strain 4.20 %,
Temperature 90.0 °C		6350 psi
@Strain 4.20 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 44.69 MPa
@Strain 5.85 %,
Temperature 120 °C		6482 psi
@Strain 5.85 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.69 MPa
@Strain 5.85 %,
Temperature 120 °C		6482 psi
@Strain 5.85 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.26 MPa
@Strain 6.70 %,
Temperature 120 °C		6854 psi
@Strain 6.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.26 MPa
@Strain 6.70 %,
Temperature 120 °C		6854 psi
@Strain 6.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 48.5 MPa
@Strain 7.53 %,
Temperature 120 °C		7030 psi
@Strain 7.53 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 48.5 MPa
@Strain 7.53 %,
Temperature 120 °C		7030 psi
@Strain 7.53 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.84 MPa
@Strain 8.38 %,
Temperature 120 °C		7084 psi
@Strain 8.38 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.84 MPa
@Strain 8.38 %,
Temperature 120 °C		7084 psi
@Strain 8.38 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 49.28 MPa
@Strain 1.08 %,
Temperature 23.0 °C		7147 psi
@Strain 1.08 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.28 MPa
@Strain 1.08 %,
Temperature 23.0 °C		7147 psi
@Strain 1.08 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.37 MPa
@Strain 5.05 %,
Temperature 90.0 °C		7161 psi
@Strain 5.05 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 49.37 MPa
@Strain 5.05 %,
Temperature 90.0 °C		7161 psi
@Strain 5.05 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 49.5 MPa
@Strain 2.43 %,
Temperature 60.0 °C		7180 psi
@Strain 2.43 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 2.43 %,
Temperature 60.0 °C		7180 psi
@Strain 2.43 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.79 MPa
@Strain 1.31 %,
Temperature 40.0 °C		7366 psi
@Strain 1.31 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 50.79 MPa
@Strain 1.31 %,
Temperature 40.0 °C		7366 psi
@Strain 1.31 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 51.72 MPa
@Strain 1.06 %,
Temperature 0.000 °C		7501 psi
@Strain 1.06 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.72 MPa
@Strain 1.06 %,
Temperature 0.000 °C		7501 psi
@Strain 1.06 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 53.89 MPa
@Strain 5.86 %,
Temperature 90.0 °C		7816 psi
@Strain 5.86 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 53.89 MPa
@Strain 5.86 %,
Temperature 90.0 °C		7816 psi
@Strain 5.86 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 55.7 MPa
@Strain 1.11 %,
Temperature -20.0 °C		8080 psi
@Strain 1.11 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 55.7 MPa
@Strain 1.11 %,
Temperature -20.0 °C		8080 psi
@Strain 1.11 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 56.53 MPa
@Strain 3.28 %,
Temperature 60.0 °C		8199 psi
@Strain 3.28 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 56.53 MPa
@Strain 3.28 %,
Temperature 60.0 °C		8199 psi
@Strain 3.28 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.21 MPa
@Strain 6.71 %,
Temperature 90.0 °C		8298 psi
@Strain 6.71 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 57.21 MPa
@Strain 6.71 %,
Temperature 90.0 °C		8298 psi
@Strain 6.71 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 58.93 MPa
@Strain 7.55 %,
Temperature 90.0 °C		8547 psi
@Strain 7.55 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 58.93 MPa
@Strain 7.55 %,
Temperature 90.0 °C		8547 psi
@Strain 7.55 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 59.5 MPa
@Strain 9.30 %,
Temperature 90.0 °C		8630 psi
@Strain 9.30 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 59.5 MPa
@Strain 9.30 %,
Temperature 90.0 °C		8630 psi
@Strain 9.30 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 62.28 MPa
@Strain 4.08 %,
Temperature 60.0 °C		9033 psi
@Strain 4.08 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 62.28 MPa
@Strain 4.08 %,
Temperature 60.0 °C		9033 psi
@Strain 4.08 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.46 MPa
@Strain 1.96 %,
Temperature 40.0 °C		9639 psi
@Strain 1.96 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 66.46 MPa
@Strain 1.96 %,
Temperature 40.0 °C		9639 psi
@Strain 1.96 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 67.84 MPa
@Strain 4.88 %,
Temperature 60.0 °C		9839 psi
@Strain 4.88 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.84 MPa
@Strain 4.88 %,
Temperature 60.0 °C		9839 psi
@Strain 4.88 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 68.01 MPa
@Strain 1.62 %,
Temperature 23.0 °C		9864 psi
@Strain 1.62 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 68.01 MPa
@Strain 1.62 %,
Temperature 23.0 °C		9864 psi
@Strain 1.62 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 72.47 MPa
@Strain 5.69 %,
Temperature 60.0 °C		10510 psi
@Strain 5.69 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 72.47 MPa
@Strain 5.69 %,
Temperature 60.0 °C		10510 psi
@Strain 5.69 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 72.87 MPa
@Strain 1.60 %,
Temperature 0.000 °C		10570 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.87 MPa
@Strain 1.60 %,
Temperature 0.000 °C		10570 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.18 MPa
@Strain 2.60 %,
Temperature 40.0 °C		10900 psi
@Strain 2.60 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 75.18 MPa
@Strain 2.60 %,
Temperature 40.0 °C		10900 psi
@Strain 2.60 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 75.91 MPa
@Strain 1.65 %,
Temperature -20.0 °C		11010 psi
@Strain 1.65 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 75.91 MPa
@Strain 1.65 %,
Temperature -20.0 °C		11010 psi
@Strain 1.65 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 76.06 MPa
@Strain 6.49 %,
Temperature 60.0 °C		11030 psi
@Strain 6.49 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.06 MPa
@Strain 6.49 %,
Temperature 60.0 °C		11030 psi
@Strain 6.49 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 77.77 MPa
@Strain 7.29 %,
Temperature 60.0 °C		11280 psi
@Strain 7.29 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.77 MPa
@Strain 7.29 %,
Temperature 60.0 °C		11280 psi
@Strain 7.29 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 77.9 MPa
@Strain 8.14 %,
Temperature 60.0 °C		11300 psi
@Strain 8.14 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 77.9 MPa
@Strain 8.14 %,
Temperature 60.0 °C		11300 psi
@Strain 8.14 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 80.13 MPa
@Strain 3.25 %,
Temperature 40.0 °C		11620 psi
@Strain 3.25 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 80.13 MPa
@Strain 3.25 %,
Temperature 40.0 °C		11620 psi
@Strain 3.25 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 81.52 MPa
@Strain 2.17 %,
Temperature 23.0 °C		11820 psi
@Strain 2.17 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 81.52 MPa
@Strain 2.17 %,
Temperature 23.0 °C		11820 psi
@Strain 2.17 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.88 MPa
@Strain 3.92 %,
Temperature 40.0 °C		12170 psi
@Strain 3.92 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 83.88 MPa
@Strain 3.92 %,
Temperature 40.0 °C		12170 psi
@Strain 3.92 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 87.33 MPa
@Strain 4.57 %,
Temperature 40.0 °C		12670 psi
@Strain 4.57 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 87.33 MPa
@Strain 4.57 %,
Temperature 40.0 °C		12670 psi
@Strain 4.57 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 88.63 MPa
@Strain 2.12 %,
Temperature -20.0 °C		12850 psi
@Strain 2.12 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 88.63 MPa
@Strain 2.12 %,
Temperature -20.0 °C		12850 psi
@Strain 2.12 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 89.2 MPa
@Strain 2.21 %,
Temperature 0.000 °C		12900 psi
@Strain 2.21 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.2 MPa
@Strain 2.21 %,
Temperature 0.000 °C		12900 psi
@Strain 2.21 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 89.97 MPa
@Strain 2.71 %,
Temperature 23.0 °C		13050 psi
@Strain 2.71 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 89.97 MPa
@Strain 2.71 %,
Temperature 23.0 °C		13050 psi
@Strain 2.71 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.53 MPa
@Strain 5.22 %,
Temperature 40.0 °C		13130 psi
@Strain 5.22 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 90.53 MPa
@Strain 5.22 %,
Temperature 40.0 °C		13130 psi
@Strain 5.22 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 93.07 MPa
@Strain 5.87 %,
Temperature 40.0 °C		13500 psi
@Strain 5.87 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 93.07 MPa
@Strain 5.87 %,
Temperature 40.0 °C		13500 psi
@Strain 5.87 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 94.4 MPa
@Strain 6.50 %,
Temperature 40.0 °C		13700 psi
@Strain 6.50 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 94.4 MPa
@Strain 6.50 %,
Temperature 40.0 °C		13700 psi
@Strain 6.50 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 95.14 MPa
@Strain 3.25 %,
Temperature 23.0 °C		13800 psi
@Strain 3.25 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 95.14 MPa
@Strain 3.25 %,
Temperature 23.0 °C		13800 psi
@Strain 3.25 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 96.46 MPa
@Strain 2.76 %,
Temperature 0.000 °C		13990 psi
@Strain 2.76 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.46 MPa
@Strain 2.76 %,
Temperature 0.000 °C		13990 psi
@Strain 2.76 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.62 MPa
@Strain 3.79 %,
Temperature 23.0 °C		14300 psi
@Strain 3.79 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 98.62 MPa
@Strain 3.79 %,
Temperature 23.0 °C		14300 psi
@Strain 3.79 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 100.76 MPa
@Strain 2.65 %,
Temperature -20.0 °C		14614 psi
@Strain 2.65 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 100.76 MPa
@Strain 2.65 %,
Temperature -20.0 °C		14614 psi
@Strain 2.65 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 101.39 MPa
@Strain 4.32 %,
Temperature 23.0 °C		14705 psi
@Strain 4.32 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 101.39 MPa
@Strain 4.32 %,
Temperature 23.0 °C		14705 psi
@Strain 4.32 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 103.83 MPa
@Strain 4.86 %,
Temperature 23.0 °C		15059 psi
@Strain 4.86 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 103.83 MPa
@Strain 4.86 %,
Temperature 23.0 °C		15059 psi
@Strain 4.86 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 105.34 MPa
@Strain 5.40 %,
Temperature 23.0 °C		15278 psi
@Strain 5.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 105.34 MPa
@Strain 5.40 %,
Temperature 23.0 °C		15278 psi
@Strain 5.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 109.63 MPa
@Strain 3.19 %,
Temperature -20.0 °C		15901 psi
@Strain 3.19 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 109.63 MPa
@Strain 3.19 %,
Temperature -20.0 °C		15901 psi
@Strain 3.19 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 115.95 MPa
@Strain 3.71 %,
Temperature -20.0 °C		16817 psi
@Strain 3.71 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 115.95 MPa
@Strain 3.71 %,
Temperature -20.0 °C		16817 psi
@Strain 3.71 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 117.3 MPa
@Strain 5.50 %,
Temperature 0.000 °C		17010 psi
@Strain 5.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 117.3 MPa
@Strain 5.50 %,
Temperature 0.000 °C		17010 psi
@Strain 5.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 120.78 MPa
@Strain 4.25 %,
Temperature -20.0 °C		17518 psi
@Strain 4.25 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 120.78 MPa
@Strain 4.25 %,
Temperature -20.0 °C		17518 psi
@Strain 4.25 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 124.53 MPa
@Strain 4.78 %,
Temperature -20.0 °C		18062 psi
@Strain 4.78 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 124.53 MPa
@Strain 4.78 %,
Temperature -20.0 °C		18062 psi
@Strain 4.78 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 127.35 MPa
@Strain 5.30 %,
Temperature -20.0 °C		18471 psi
@Strain 5.30 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 127.35 MPa
@Strain 5.30 %,
Temperature -20.0 °C		18471 psi
@Strain 5.30 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
Elongation at Break  5.2 %
@Temperature 23.0 °C		5.2 %
@Temperature 73.4 °F		DAM; ISO 527
 7.2 %
@Temperature 23.0 °C		7.2 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  3.50 GPa
@Temperature 23.0 °C		508 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 5.30 GPa
@Temperature 23.0 °C		769 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  3.30 GPa
@Temperature 23.0 °C		479 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 4.90 GPa
@Temperature 23.0 °C		711 ksi
@Temperature 73.4 °F		DAM; ISO 178
Izod Impact, Notched (ISO)  5.00 kJ/m²
@Temperature 23.0 °C		2.38 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 7.00 kJ/m²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Charpy Impact Unnotched  5.00 J/cm²
@Temperature 23.0 °C		23.8 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 6.50 J/cm²
@Temperature 23.0 °C		30.9 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.600 J/cm²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 0.900 J/cm²
@Temperature 23.0 °C		4.28 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 255 °C491 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 222 °C432 °FDAM; ISO 75-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 263 °C505 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesFriction, LowDAM
 Wear Resistance, GoodDAM
FormsPelletsDAM
GenericNylon 66DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA66-RF20<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryLow Wear and Friction ResinsDAM
 Low Wear and Friction ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-RF20ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45484.html

免责声明: 本文 DuPont Performance Polymers Zytel® 70K20HSL NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4