- 密度 [g/cm3]: 1.15
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Moisture Vapor Transmission | 0.230 cc-mm/m²-24hr-atm | 0.584 cc-mil/100 in²-24hr-atm | 9 g/m²-24hr for the film. ASTM F-372, 38°C, 90% RH |
| Oxygen Transmission | 0.190 cc-mm/m²-24hr-atm | 0.483 cc-mil/100 in²-24hr-atm | or 7.7 cc/m²-24hr-atm for the film at 23°C, 0% RH. ASTM D1434-66 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882-64T |
| Film Elongation at Break, TD | 300 % | 300 % | ASTM D882-64T |
| Secant Modulus, MD | 0.690 GPa | 100 ksi | ASTM D882 |
| Secant Modulus, TD | 0.690 GPa | 100 ksi | ASTM D882 |
| Coefficient of Friction, Dynamic | 0.45 | 0.45 | film to coating; ASTM D1894-63 |
| Elmendorf Tear Strength, MD | 1.40 g/micron | 35.6 g/mil | ASTM D1922-67 |
| Elmendorf Tear Strength, TD | 1.20 g/micron | 30.5 g/mil | ASTM D1922-67 |
| Dart drop Test | 600 g | 1.32 lb | Impact Strength, ASTM D1709-62T |
| Film Tensile Strength at Break, MD | 62.0 MPa | 8990 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 62.0 MPa | 8990 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.5 % | 1.5 % | |
| Gloss | 150 % | 150 % | |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |