- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 0.9
- 成型收缩率 [%]: 0.003
- 缺口冲击强度: 0.8
- 弯曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | DAM; ASTM D792 | ||
| Density | 1.49 g/cc | 0.0538 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 25 % | 25 % | DAM | ||
| Water Absorption | 0.90 % @Temperature 23.0 °C | 0.90 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 3.4 % @Temperature 23.0 °C | 3.4 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 1.60 mm | 0.0030 in/in @Thickness 0.0630 in | Flow; DAM | ||
| 0.0035 cm/cm @Thickness 3.20 mm | 0.0035 in/in @Thickness 0.126 in | Flow; DAM | |||
| 0.011 cm/cm @Thickness 1.60 mm | 0.011 in/in @Thickness 0.0630 in | Transverse; DAM | |||
| 0.011 cm/cm @Thickness 3.20 mm | 0.011 in/in @Thickness 0.126 in | Transverse; DAM | |||
| Linear Mold Shrinkage, Flow | 0.0023 cm/cm @Thickness 2.00 mm | 0.0023 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm | 0.010 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C | 16000 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 125 MPa @Temperature 23.0 °C | 18100 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength | 138 MPa @Temperature 23.0 °C | 20000 psi @Temperature 73.4 °F | DAM; ASTM D638 | ||
| Elongation at Break | 2.0 % @Temperature 23.0 °C | 2.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 2.3 % @Temperature 23.0 °C | 2.3 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| 2.6 % @Temperature 23.0 °C | 2.6 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 7.50 GPa @Temperature 23.0 °C | 1090 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 9.00 GPa @Temperature 23.0 °C | 1310 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Strength | 190 MPa @Temperature 23.0 °C | 27600 psi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| Flexural Modulus | 8.00 GPa @Temperature 23.0 °C | 1160 ksi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C | 1.50 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | ||
| 6.50 kJ/m² @Temperature 23.0 °C | 3.09 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Charpy Impact Unnotched | 4.30 J/cm² @Temperature 23.0 °C | 20.5 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| 4.50 J/cm² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | ||
| 1.00 J/cm² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; ASTM D257 | ||
| Surface Resistance | 1.00e+14 ohm @Temperature 23.0 °C | 1.00e+14 ohm @Temperature 73.4 °F | DAM; ASTM D257 | ||
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.4 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; ASTM D150 | ||
| 3.5 @Frequency 1000 Hz, Temperature 23.0 °C | 3.5 @Frequency 1000 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |||
| Dielectric Strength | 15.6 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 396 kV/in @Thickness 0.126 in, Temperature 73.4 °F | DAM; Short Time; ASTM D149 | ||
| 26.0 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C | 660 kV/in @Thickness 0.0394 in, Temperature 73.4 °F | 50%RH; IEC 60243-1 | |||
| 37.0 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C | 940 kV/in @Thickness 0.0394 in, Temperature 73.4 °F | DAM; IEC 60243-1 | |||
| Dissipation Factor | 0.010 @Frequency 1000 Hz, Temperature 23.0 °C | 0.010 @Frequency 1000 Hz, Temperature 73.4 °F | DAM; ASTM D150 | ||
| 0.010 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.010 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |||
| Comparative Tracking Index | 250 - 400 V @Temperature 23.0 °C | 250 - 400 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| 250 - 400 V @Temperature 23.0 °C | 250 - 400 V @Temperature 73.4 °F | 50%RH; IEC 60112 | |||
| 250 - 400 V @Temperature 23.0 °C | 250 - 400 V @Temperature 73.4 °F | DAM; UL 746A | |||
| 250 - 400 V @Thickness 3.00 mm, Temperature 23.0 °C | 250 - 400 V @Thickness 0.118 in, Temperature 73.4 °F | DAM; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | 50%RH; ASTM E 831 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | 50%RH; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 46.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 83.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 46.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 263 °C | 505 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 469 °F | DAM; ISO 75-1/-2 | ||
| 243 °C | 469 °F | DAM; ASTM D648 | |||
| UL RTI, Electrical | 65.0 °C @Thickness 0.500 mm | 149 °F @Thickness 0.0197 in | DAM; UL 746B | ||
| 120 °C @Thickness 0.830 mm | 248 °F @Thickness 0.0327 in | DAM; UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.500 mm | 149 °F @Thickness 0.0197 in | DAM; UL 746B | ||
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 120 °C @Thickness 0.830 mm | 248 °F @Thickness 0.0327 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.500 mm | 149 °F @Thickness 0.0197 in | DAM; UL 746B | ||
| 130 °C @Thickness 0.830 mm | 266 °F @Thickness 0.0327 in | DAM; UL 746B | |||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | V-0 @Thickness 0.500 mm | V-0 @Thickness 0.0197 in | DAM; IEC 60695-11-10 | ||
| V-0 @Thickness 0.830 mm | V-0 @Thickness 0.0327 in | DAM; IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | DAM; UL94 | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | DAM; UL94 | |||
| V-0 @Thickness 0.830 mm | V-0 @Thickness 0.0327 in | DAM; UL94 | |||
| V-0 @Thickness 0.500 mm | V-0 @Thickness 0.0197 in | DAM; UL94 | |||
| 5VA @Thickness 1.50 mm | 5VA @Thickness 0.0591 in | DAM; IEC 60695-11-20 | |||
| 5VA @Thickness 1.50 mm | 5VA @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| 5VA @Thickness 1.50 mm | 5VA @Thickness 0.0591 in | DAM; UL94 | |||
| Glow Wire Test | 850 °C @Thickness 0.830 mm | 1560 °F @Thickness 0.0327 in | DAM; IEC 60695-2-12 | ||
| 850 °C @Thickness 3.00 mm | 1560 °F @Thickness 0.118 in | DAM; IEC 60695-2-12 | |||
| 960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | DAM; IEC 60695-2-12 | |||
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | DAM; Ignition; IEC 60695-2-13 | |||
| 960 °C @Thickness 0.830 mm | 1760 °F @Thickness 0.0327 in | DAM; Ignition; IEC 60695-2-13 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 295 - 305 °C | 563 - 581 °F | DAM | |||
| Mold Temperature | 90.0 °C | 194 °F | DAM; optimum | ||
| 70.0 - 110 °C | 158 - 230 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Flame Retardant | DAM | |||
| Appearance | Natural Color | DAM | |||
| Contains Flame Retardant | Yes | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Flame Retardant | DAM | |||
| Filler | Glass fiber reinforcement | DAM | |||
| Flame Retardant - Halogen/Red Phosphorus Free | Yes | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Polyamide (Nylon 66) | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-GF25FR(17)< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Flame Retardant Resins | DAM | |||
| Glass Reinforced Resins | DAM | ||||
| Resin Identification | PA66-GF25FR(17) | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Electrical/Electronic Applications | DAM | |||