- 密度 [g/cm3]: 1.13
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Oxygen Transmission | 3.60 cc-mm/m²-24hr-atm | 9.14 cc-mil/100 in²-24hr-atm | or 47 cc/m²-24hr-atm for the film at 23°C, 0% RH. ASTM D1434-66 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 45.0 MPa | 6530 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 45.0 MPa | 6530 psi | ASTM D882 |
| Film Elongation at Break, MD | 370 % | 370 % | ASTM D882 |
| Film Elongation at Break, TD | 400 % | 400 % | ASTM D882 |
| Secant Modulus, MD | 0.965 GPa | 140 ksi | ASTM D882 |
| Secant Modulus, TD | 0.965 GPa | 140 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 1.80 g/micron | 45.7 g/mil | ASTM D1922-67 |
| Elmendorf Tear Strength, TD | 2.20 g/micron | 55.9 g/mil | ASTM D1922-67 |
| Film Tensile Strength at Break, MD | 79.0 MPa | 11500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 76.0 MPa | 11000 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.50 % | 0.50 % | |
| Gloss | 150 % | 150 % | |