- 吸水率 [%]: 1.2
- 拉伸强度 [MPa]: 55.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ISO 1183 |
| Water Absorption | 1.2 % @Time 86400 sec | 1.2 % @Time 24.0 hour | ISO 62 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Thickness 2.00 mm | 0.015 in/in @Thickness 0.0787 in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 |
| Elongation at Yield | 25 % | 25 % | ISO 527 |
| Tensile Modulus | 1.30 GPa | 189 ksi | ISO 527 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 250 - 295 °C | 482 - 563 °F | |
| Die Temperature | 270 - 295 °C | 518 - 563 °F | |
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |
| Back Pressure | 3.00 - 17.0 MPa | 435 - 2470 psi | |