- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.2
- 缺口冲击强度: 0.64
- 断裂伸长率 [%]: 117.2
- 弯曲模量 [MPa]: 2.80
- 硬度: 120.0
- 热变形温度 [℃]: 235.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hrs.; ASTM D570 |
| Water Absorption at Saturation | 8.5 % | 8.5 % | room temp; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 79 | 79 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 85.5 MPa | 12400 psi | ASTM D638 |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| Flexural Yield Strength | 117.2 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 @Frequency 60 Hz | 4.0 @Frequency 60 Hz | 50% RH; ASTM D150 |
| Dielectric Strength | 11.8 - 15.7 kV/mm | 300 - 399 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 81.0 µm/m-°C @Temperature -20.0 - 200 °C | 45.0 µin/in-°F @Temperature -4.00 - 392 °F | ASTM D696 |
| 90.0 µm/m-°C @Temperature 93.3 - 238 °C | 50.0 µin/in-°F @Temperature 200 - 460 °F | ASTM D696 | |
| Maximum Service Temperature, Air | 99.0 °C | 210 °F | Long Term |
| 179 °C | 354 °F | Short Term | |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |