- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 1.0
- 缺口冲击强度: 0.5
- 断裂伸长率 [%]: 179
- 弯曲强度 [MPa]: 124.0
- 弯曲模量 [MPa]: 5.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | 24 hours; ASTM D570 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | ASTM D570 |
| Water Absorption at Saturation | 7.1 % | 7.1 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 5.50 GPa | 798 ksi | ASTM D790 |
| Compressive Yield Strength | 172 MPa | 24900 psi | at 1% deformation; ASTM D695 |
| Shear Strength | 76.0 MPa | 11000 psi | ASTM D732 |
| Izod Impact, Notched | 0.500 J/cm @Thickness 3.17 mm | 0.937 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 27.0 µm/m-°C @Temperature -40.0 - 82.0 °C | 15.0 µin/in-°F @Temperature -40.0 - 180 °F | |
| Melting Point | 260 °C | 500 °F | ASTM D1525 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C @Thickness 3.17 mm | 473 °F @Thickness 0.125 in | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Oxygen Index | 25 % | 25 % | ASTM D2863 |