- 吸水率 [%]: 1.2
- 缺口冲击强度: 1.6
- 拉伸强度 [MPa]: 46.2
- 弯曲模量 [MPa]: 0.896
- 硬度: 94.0
- 热变形温度 [℃]: 229.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Water Absorption | 1.2 % @Time 86400 sec | 1.2 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.013 - 0.017 cm/cm @Thickness 3.17 mm | 0.013 - 0.017 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 94 | 94 | Conditioned; ASTM D785 |
| 114 | 114 | ASTM D785 | |
| Tensile Strength, Yield | 46.2 MPa | 6700 psi | Conditioned; ASTM D638 |
| 65.5 MPa | 9500 psi | ASTM D638 | |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| 130 % | 130 % | Conditioned; ASTM D638 | |
| Flexural Strength | 34.5 MPa | 5000 psi | Conditioned; ASTM D790 |
| 82.7 MPa | 12000 psi | ASTM D790 | |
| Flexural Modulus | 0.896 GPa | 130 ksi | Conditioned; ASTM D790 |
| 2.21 GPa | 320 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| 2.14 J/cm | 4.00 ft-lb/in | Conditioned; ASTM D256 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | Conditioned; ASTM D257 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | |
| Dielectric Constant | 3.5 | 3.5 | ASTM D150 |
| 5.8 | 5.8 | Conditioned; ASTM D150 | |
| Dielectric Strength | 21.3 kV/mm | 540 kV/in | Method A (Short-time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 113 µm/m-°C | 63.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 229 °C | 445 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | Conditioned | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 277 - 293 °C | 530 - 560 °F | |
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 73.9 °C @Time 7200 - 14400 sec | 165 °F @Time 2.00 - 4.00 hour | |
| Moisture Content | <= 0.18 % | <= 0.18 % | Suggested Maximum |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm | |