- 缺口冲击强度: 8.54
- 弯曲模量 [MPa]: 1.83
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.017 - 0.021 cm/cm @Thickness 3.17 mm | 0.017 - 0.021 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 53.8 MPa | 7800 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 70.3 MPa | 10200 psi | ASTM D790 |
| Flexural Modulus | 1.83 GPa | 265 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.2 °C | 144 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.787 mm | HB @Thickness 0.0310 in | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 266 - 277 °C | 510 - 530 °F | |
| Mold Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Drying Temperature | 73.9 °C @Time 7200 - 14400 sec | 165 °F @Time 2.00 - 4.00 hour | |
| Moisture Content | <= 0.18 % | <= 0.18 % | Suggested Maximum |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm | |