- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.9
- 缺口冲击强度: 0.481
- 弯曲模量 [MPa]: 2.83
- 热变形温度 [℃]: 238.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 % @Time 86400 sec | 0.90 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.016 - 0.020 cm/cm | 0.016 - 0.020 in/in | ASTM D955 and ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 75.8 MPa | 11000 psi | ISO 527-2 |
| 75.8 MPa | 11000 psi | ASTM D638 | |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| 97.2 MPa | 14100 psi | ISO 178 | |
| Flexural Modulus | 2.83 GPa | 410 ksi | ISO 178 |
| 2.83 GPa | 410 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 48.3 kJ/m² | 23.0 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 238 °C | 460 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | Unannealed; ASTM D648 |