- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 0.8
- 缺口冲击强度: 0.534
- 弯曲模量 [MPa]: 8.41
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % @Time 86400 sec | 0.80 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 and ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 98 | 98 | ASTM D785 |
| Tensile Strength at Break | 113 MPa | 16400 psi | ISO 527-2 |
| 114 MPa | 16500 psi | ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| Flexural Strength | 172 MPa | 24900 psi | ISO 178 |
| 172 MPa | 25000 psi | ASTM D790 | |
| Flexural Modulus | 8.41 GPa | 1220 ksi | ISO 178 |
| 8.62 GPa | 1250 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 4.20 kJ/m² | 2.00 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 445 °F | Unannealed; ASTM D648 |