- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 1.0
- 缺口冲击强度: 0.374
- 弯曲模量 [MPa]: 4.48
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Water Absorption | 1.0 % @Time 86400 sec | 1.0 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00060 - 0.00090 cm/cm | 0.00060 - 0.00090 in/in | ASTM D955 and ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength at Break | 103 MPa | 14900 psi | ISO 527-2 |
| 103 MPa | 15000 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 165 MPa | 23900 psi | ISO 178 |
| 165 MPa | 24000 psi | ASTM D790 | |
| Flexural Modulus | 4.48 GPa | 650 ksi | ASTM D790 |
| 4.48 GPa | 650 ksi | ISO 178 | |
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 2.94 kJ/m² | 1.40 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C | 15.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Unannealed; ASTM D648 |