- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.3
- 缺口冲击强度: 0.4
- 拉伸强度 [MPa]: 83.0
- 断裂伸长率 [%]: 120
- 弯曲模量 [MPa]: 3.00
- 硬度: 116.0
- 热变形温度 [℃]: 230.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 116 | 116 | ASTM D786 |
| Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 120 MPa | 17400 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Arc Resistance | 185 sec | 185 sec | Tungsten electrode; ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C | 38.9 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |