- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 4.0
- 缺口冲击强度: 15.0
- 弯曲模量 [MPa]: 12.5
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Filler Content | 50 % | 50 % | ISO 3451 |
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | Humidity Absorption, 50% RH, 23°C; ISO 62 |
| Water Absorption at Saturation | 4.0 % | 4.0 % | 23°C; ISO 62 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 235 MPa | 34100 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
| Flexural Strength | 320 MPa | 46400 psi | 23°C, at break; ISO 178 |
| Flexural Modulus | 12.5 GPa | 1810 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | ISO 180/1A |
| 18.0 kJ/m² @Temperature 23.0 °C | 8.57 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C | 40.5 ft-lb/in² @Temperature -22.0 °F | ISO 179/eU |
| 10.0 J/cm² @Temperature 23.0 °C | 47.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/eU | |
| Charpy Impact, Notched | 1.60 J/cm² @Temperature -30.0 °C | 7.61 ft-lb/in² @Temperature -22.0 °F | ISO 179/eA |
| 1.90 J/cm² @Temperature 23.0 °C | 9.04 ft-lb/in² @Temperature 73.4 °F | ISO 179/eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 500 V | 500 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 262 °C | 504 °F | 10 K/min; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-1/2 |
| Vicat Softening Point | 255 °C | 491 °F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Glow Wire Test | 650 °C @Thickness 2.00 mm | 1200 °F @Thickness 0.0787 in | plaque; IEC 60695 |