- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.34
- 拉伸强度 [MPa]: 47.0
- 断裂伸长率 [%]: 63.0
- 弯曲强度 [MPa]: 38.0
- 弯曲模量 [MPa]: 2.26
- 硬度: 110.0
- 热变形温度 [℃]: 177.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 - 1.56 g/cc | 0.0379 - 0.0564 lb/in³ | Average value: 1.24 g/cc Grade Count:19 |
| Filler Content | 20.0 - 23.0 % | 20.0 - 23.0 % | Average value: 21.0 % Grade Count:3 |
| Water Absorption | 0.200 - 7.20 % | 0.200 - 7.20 % | Average value: 1.23 % Grade Count:11 |
| Moisture Absorption at Equilibrium | 1.70 - 2.50 % | 1.70 - 2.50 % | Average value: 2.08 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00100 - 0.0150 cm/cm | 0.00100 - 0.0150 in/in | Average value: 0.00906 cm/cm Grade Count:18 |
| Linear Mold Shrinkage, Transverse | 0.00750 - 0.0100 cm/cm | 0.00750 - 0.0100 in/in | Average value: 0.00860 cm/cm Grade Count:4 |
| Melt Flow | 3.00 - 20.0 g/10 min | 3.00 - 20.0 g/10 min | Average value: 8.50 g/10 min Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90.0 - 93.0 | 90.0 - 93.0 | Average value: 91.5 Grade Count:4 |
| Hardness, Rockwell R | 110 - 121 | 110 - 121 | Average value: 118 Grade Count:5 |
| Tensile Strength, Ultimate | 38.0 - 105 MPa | 5510 - 15200 psi | Average value: 68.2 MPa Grade Count:9 |
| 24.0 - 65.0 MPa @Temperature -40.0 - 80.0 °C | 3480 - 9430 psi @Temperature -40.0 - 176 °F | Average value: 44.5 MPa Grade Count:1 | |
| Tensile Strength, Yield | 47.0 - 85.0 MPa | 6810 - 12300 psi | Average value: 67.2 MPa Grade Count:9 |
| Elongation at Break | 1.50 - 50.0 % | 1.50 - 50.0 % | Average value: 11.5 % Grade Count:14 |
| Modulus of Elasticity | 1.80 - 5.50 GPa | 261 - 798 ksi | Average value: 4.51 GPa Grade Count:7 |
| Flexural Yield Strength | 63.0 - 130 MPa | 9140 - 18900 psi | Average value: 103 MPa Grade Count:15 |
| 38.0 - 110 MPa @Temperature -40.0 - 80.0 °C | 5510 - 16000 psi @Temperature -40.0 - 176 °F | Average value: 75.5 MPa Grade Count:1 | |
| Flexural Modulus | 2.26 - 6.10 GPa | 328 - 885 ksi | Average value: 4.05 GPa Grade Count:13 |
| 1.20 - 7.20 GPa @Temperature -40.0 - 80.0 °C | 174 - 1040 ksi @Temperature -40.0 - 176 °F | Average value: 4.55 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.340 - 1.90 J/cm | 0.637 - 3.56 ft-lb/in | Average value: 0.612 J/cm Grade Count:13 |
| 0.300 - 0.450 J/cm @Temperature -40.0 - -40.0 °C | 0.562 - 0.843 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.375 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 4.00 - 4.00 kJ/m² @Temperature -30.0 - -30.0 °C | 1.90 - 1.90 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 4.00 kJ/m² Grade Count:1 |
| Charpy Impact Unnotched | 3.00 J/cm² - NB | 14.3 ft-lb/in² - NB | Average value: 3.77 J/cm² Grade Count:5 |
| 1.00 - 2.00 J/cm² @Temperature -20.0 - -20.0 °C | 4.76 - 9.52 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 1.50 J/cm² Grade Count:2 | |
| Charpy Impact, Notched | 0.200 - 2.00 J/cm² | 0.952 - 9.52 ft-lb/in² | Average value: 0.790 J/cm² Grade Count:5 |
| 0.200 - 0.200 J/cm² @Temperature -20.0 - -20.0 °C | 0.952 - 0.952 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 0.200 J/cm² Grade Count:2 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+8 - 1.00e+15 ohm-cm | 1.00e+8 - 1.00e+15 ohm-cm | Average value: 7.00e+14 ohm-cm Grade Count:9 |
| Surface Resistance | 1.00e+10 - 1.00e+13 ohm | 1.00e+10 - 1.00e+13 ohm | Average value: 3.00e+12 ohm Grade Count:4 |
| Dielectric Constant | 3.50 - 6.00 | 3.50 - 6.00 | Average value: 4.98 Grade Count:5 |
| Dielectric Strength | 20.0 - 100 kV/mm | 508 - 2540 kV/in | Average value: 37.6 kV/mm Grade Count:6 |
| Arc Resistance | 15.0 - 185 sec | 15.0 - 185 sec | Average value: 103 sec Grade Count:3 |
| Comparative Tracking Index | 350 - 600 V | 350 - 600 V | Average value: 488 V Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 42.0 - 100 µm/m-°C | 23.3 - 55.6 µin/in-°F | Average value: 65.4 µm/m-°C Grade Count:6 |
| Melting Point | 215 - 223 °C | 419 - 433 °F | Average value: 219 °C Grade Count:8 |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 - 230 °C | 350 - 446 °F | Average value: 206 °C Grade Count:11 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 200 °C | 158 - 392 °F | Average value: 131 °C Grade Count:12 |
| Vicat Softening Point | 200 - 203 °C | 392 - 397 °F | Average value: 201 °C Grade Count:4 |
| UL RTI, Electrical | 60.0 - 65.0 °C | 140 - 149 °F | Average value: 61.3 °C Grade Count:4 |
| UL RTI, Mechanical with Impact | 60.0 - 65.0 °C | 140 - 149 °F | Average value: 61.3 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 60.0 - 65.0 °C | 140 - 149 °F | Average value: 61.3 °C Grade Count:4 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:18 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 830 °C Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 220 - 271 °C | 428 - 520 °F | Average value: 240 °C Grade Count:3 |
| Nozzle Temperature | 250 - 275 °C | 482 - 527 °F | Average value: 264 °C Grade Count:4 |
| Melt Temperature | 230 - 290 °C | 446 - 554 °F | Average value: 259 °C Grade Count:11 |
| Mold Temperature | 40.0 - 100 °C | 104 - 212 °F | Average value: 73.8 °C Grade Count:14 |
| Drying Temperature | 70.0 - 100 °C | 158 - 212 °F | Average value: 83.6 °C Grade Count:9 |
| Dry Time | 2.00 - 5.00 hour | 2.00 - 5.00 hour | Average value: 3.85 hour Grade Count:10 |
| Moisture Content | 0.150 - 0.200 % | 0.150 - 0.200 % | Average value: 0.175 % Grade Count:4 |
| Injection Pressure | 40.0 - 120 MPa | 5800 - 17400 psi | Average value: 85.4 MPa Grade Count:6 |