- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.267
- 断裂伸长率 [%]: 84.1
- 弯曲强度 [MPa]: 59.3
- 弯曲模量 [MPa]: 2.24
- 硬度: 110.0
- 热变形温度 [℃]: 204.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 - 1.61 g/cc | 0.0401 - 0.0582 lb/in³ | Average value: 1.38 g/cc Grade Count:38 |
| Filler Content | 10.0 - 45.0 % | 10.0 - 45.0 % | Average value: 30.9 % Grade Count:22 |
| Water Absorption | 0.300 - 1.40 % | 0.300 - 1.40 % | Average value: 0.801 % Grade Count:19 |
| Water Absorption at Saturation | 6.00 - 7.00 % | 6.00 - 7.00 % | Average value: 6.43 % Grade Count:6 |
| Linear Mold Shrinkage | 0.000500 - 0.00600 cm/cm | 0.000500 - 0.00600 in/in | Average value: 0.00259 cm/cm Grade Count:26 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.0100 cm/cm | 0.00300 - 0.0100 in/in | Average value: 0.00508 cm/cm Grade Count:13 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 59.0 - 85.0 | 59.0 - 85.0 | Average value: 76.0 Grade Count:6 |
| Hardness, Rockwell R | 110 - 120 | 110 - 120 | Average value: 118 Grade Count:9 |
| Hardness, Shore D | 73.0 - 85.0 | 73.0 - 85.0 | Average value: 78.0 Grade Count:3 |
| Tensile Strength, Ultimate | 59.3 - 179 MPa | 8600 - 26000 psi | Average value: 129 MPa Grade Count:36 |
| Elongation at Break | 2.00 - 50.0 % | 2.00 - 50.0 % | Average value: 8.03 % Grade Count:34 |
| Modulus of Elasticity | 2.75 - 15.2 GPa | 399 - 2200 ksi | Average value: 8.48 GPa Grade Count:32 |
| Flexural Yield Strength | 84.1 - 290 MPa | 12200 - 42000 psi | Average value: 196 MPa Grade Count:37 |
| Flexural Modulus | 2.24 - 13.8 GPa | 325 - 2000 ksi | Average value: 7.66 GPa Grade Count:37 |
| Compressive Yield Strength | 26.0 - 138 MPa | 3770 - 20000 psi | Average value: 87.4 MPa Grade Count:12 |
| Compressive Modulus | 2.28 - 3.00 GPa | 330 - 435 ksi | Average value: 2.56 GPa Grade Count:5 |
| Shear Strength | 64.1 - 68.9 MPa | 9300 - 10000 psi | Average value: 65.7 MPa Grade Count:3 |
| Izod Impact, Notched | 0.267 - 2.40 J/cm | 0.500 - 4.50 ft-lb/in | Average value: 1.14 J/cm Grade Count:34 |
| Izod Impact, Unnotched | 4.27 - 12.8 J/cm | 8.00 - 24.0 ft-lb/in | Average value: 9.44 J/cm Grade Count:24 |
| Charpy Impact Unnotched | 2.50 - 9.00 J/cm² | 11.9 - 42.8 ft-lb/in² | Average value: 5.50 J/cm² Grade Count:3 |
| Charpy Impact, Notched | 0.400 - 1.30 J/cm² | 1.90 - 6.19 ft-lb/in² | Average value: 0.700 J/cm² Grade Count:3 |
| Coefficient of Friction | 0.120 - 0.350 | 0.120 - 0.350 | Average value: 0.186 Grade Count:8 |
| K (wear) Factor | 24.2 - 161 x 10-8 mm³/N-M | 12.0 - 80.0 x 10-10 in³-min/ft-lb-hr | Average value: 108 x 10-8 mm³/N-M Grade Count:6 |
| Limiting Pressure Velocity | 0.0800 - 0.701 MPa-m/sec | 2280 - 20000 psi-ft/min | Average value: 0.379 MPa-m/sec Grade Count:8 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+15 ohm-cm | 1.00e+14 - 1.00e+15 ohm-cm | Average value: 2.06e+14 ohm-cm Grade Count:17 |
| Surface Resistance | 1.00e+12 - 1.00e+14 ohm | 1.00e+12 - 1.00e+14 ohm | Average value: 2.20e+13 ohm Grade Count:6 |
| Dielectric Constant | 3.50 - 4.00 | 3.50 - 4.00 | Average value: 3.77 Grade Count:5 |
| Dielectric Strength | 15.7 - 25.0 kV/mm | 400 - 635 kV/in | Average value: 19.6 kV/mm Grade Count:6 |
| Dissipation Factor | 0.0150 - 0.0160 | 0.0150 - 0.0160 | Average value: 0.0157 Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 23.4 - 101 µm/m-°C | 13.0 - 56.0 µin/in-°F | Average value: 68.1 µm/m-°C Grade Count:12 |
| Thermal Conductivity | 0.280 - 0.519 W/m-K | 1.94 - 3.60 BTU-in/hr-ft²-°F | Average value: 0.447 W/m-K Grade Count:7 |
| Melting Point | 215 - 220 °C | 419 - 428 °F | Average value: 217 °C Grade Count:8 |
| Maximum Service Temperature, Air | 90.0 - 190 °C | 194 - 374 °F | Average value: 110 °C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 - 218 °C | 400 - 425 °F | Average value: 213 °C Grade Count:17 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 216 °C | 158 - 420 °F | Average value: 183 °C Grade Count:37 |
| Flammability, UL94 | HB | HB | Grade Count:31 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 271 °C | 430 - 520 °F | Average value: 246 °C Grade Count:13 |
| Melt Temperature | 243 - 279 °C | 470 - 535 °F | Average value: 261 °C Grade Count:11 |
| Mold Temperature | 54.4 - 93.3 °C | 130 - 200 °F | Average value: 73.9 °C Grade Count:24 |
| Drying Temperature | 82.2 °C | 180 °F | Average value: 82.2 °C Grade Count:11 |
| Dry Time | 2.00 hour | 2.00 hour | Average value: 2.00 hour Grade Count:9 |
| Moisture Content | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:11 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:11 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:24 |