- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 6.6
- 断裂伸长率 [%]: 131
- 弯曲模量 [MPa]: 3.58
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183-1 |
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | 50% RH |
| Water Absorption at Saturation | 6.6 % | 6.6 % | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85 | 85 | ISO 2039-2 |
| Hardness, Shore D | 80 | 80 | |
| Ball Indentation Hardness | 160 MPa | 23200 psi | ISO 2039-1 |
| Tensile Strength | 84.0 MPa | 12200 psi | at Yield; ISO 527-1/-2 |
| Elongation at Break | 35 % | 35 % | ISO 527-1/-2 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-1/-2 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527-1/-2 |
| Flexural Yield Strength | 131 MPa | 19000 psi | |
| Flexural Modulus | 3.58 GPa | 519 ksi | |
| Compressive Strength | 32.0 MPa @Strain 1 % | 4640 psi @Strain 1 % | ISO 604 |
| 61.0 MPa @Strain 2 % | 8850 psi @Strain 2 % | ISO 604 | |
| 90.0 MPa @Strain 5 % | 13100 psi @Strain 5 % | ISO 604 | |
| K Factor (ISO) | 12 µm/km | 12 µm/km | |
| Charpy Impact Unnotched | NB | NB | ISO 179-1/1eU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179-1/1eA |
| Coefficient of Friction, Dynamic | 0.40 - 0.60 | 0.40 - 0.60 | |
| Limiting Pressure Velocity | 0.0800 MPa-m/sec | 2280 psi-ft/min | at 1 m/s unlubricated |
| 0.130 MPa-m/sec | 3710 psi-ft/min | at 0.1 m/s unlubricated | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.0e+14 ohm-cm | >= 1.0e+14 ohm-cm | IEC 60093 |
| Surface Resistivity per Square | >= 1.0e+13 ohm | >= 1.0e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency >=100000 Hz | 3.6 @Frequency >=100000 Hz | IEC 60250 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | |
| Dissipation Factor | 0.012 @Frequency 100000 Hz | 0.012 @Frequency 100000 Hz | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 µm/m-°C @Temperature 23.0 - 100 °C | 50.0 µin/in-°F @Temperature 73.4 - 212 °F | |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | |
| Melting Point | 215 °C | 419 °F | DSC, 10°C/min.; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | Continuous; 20,000 h |
| 105 °C | 221 °F | Continuous; 5,000 h | |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | |
| Oxygen Index | 25 % | 25 % | ISO 4589-1/-2 |
| Compliance Properties | Metric | English | Comments |
| 3A-Dairy | No | No | |
| European Food 1935/2004 | No | No | |
| FDA | No | No | |
| USP Class VI | No | No | |
| Chemical Resistance Properties | Metric | English | Comments |
| Acids, Strong (pH 1-3) | Unacceptable | Unacceptable | |
| Acids, Weak | Limited | Limited | |
| Alcohols | Limited | Limited | |
| Alkalies, Strong (pH 11-14) | Unacceptable | Unacceptable | |
| Alkalies, Weak | Limited | Limited | |
| Chlorinated Solvents | Limited | Limited | |
| Continuous Sunlight | Limited | Limited | |
| Hot Water / Steam | Limited | Limited | |
| Hydrocarbons - Aliphatic | Acceptable | Acceptable | |
| Hydrocarbons - Aromatic | Acceptable | Acceptable | |
| Inorganic Salt Solutions | Acceptable | Acceptable | |
| Ketones, Esters | Acceptable | Acceptable | |