Akro-Plastic Akromid® B3 (2500) PA 6 Dry

Akro-Plastic Akromid® B3 (2500) PA 6 Dry 物性表: Akro-Plastic Akromid® B3 (2500) PA 6 Dry物性表及特性介绍,Akro-Plastic Akromid® B3 (2500) PA 6 Dry注塑参数详情,如需Akro-Plastic Akromid® B3 (2500) PA 6 Dry下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.13
  • 吸水率 [%]: 2.6
  • 拉伸强度 [MPa]: 85.0
  • 弯曲模量 [MPa]: 3.10
  • 热变形温度 [℃]: 180.0
 
Physical PropertiesMetricEnglishComments
Density 1.13 g/cc
@Temperature 23.0 °C		0.0408 lb/in³
@Temperature 73.4 °F		ISO 1183
Water Absorption 2.6 - 3.4 %
@Temperature 23.0 °C		2.6 - 3.4 %
@Temperature 73.4 °F		50% r.h.; ISO 62
Water Absorption at Saturation 9.0 - 10 %
@Time 82800 sec		9.0 - 10 %
@Time 23.0 hour		ISO 62
Linear Mold Shrinkage, Flow 0.0111 cm/cm0.0111 in/inISO 294-4
Linear Mold Shrinkage, Transverse 0.0095 cm/cm0.0095 in/inISO 294-4
Spiral Flow 1070 cm421 inCross Section: 7[mm]x3.5[mm]; AKRO
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Yield 85.0 MPa12300 psi5 [mm/min], Test Speed 50 [mm/min]; ISO 527-1/2
 42.5 MPa
@Temperature 100 - 140 °C,
Time 1.80e+7 sec		6160 psi
@Temperature 212 - 284 °F,
Time 5000 hour		5 [mm/min], 50% Loss of Tensile Strength; ICE 216
 42.5 MPa
@Temperature 90.0 - 120 °C,
Time 7.20e+7 sec		6160 psi
@Temperature 194 - 248 °F,
Time 20000 hour		5 [mm/min], 50% Loss of Tensile Strength; ICE 216
Elongation at Break >= 20 %>= 20 %5 [mm/min]; ISO 527-1/2
Tensile Modulus 3.60 GPa522 ksi1[mm/min]; ISO 527-1/2
Flexural Strength 120 MPa17400 psi2 [mm/min]; ISO 178
Flexural Modulus 3.10 GPa450 ksi2 [mm/min]; ISO 178
Charpy Impact Unnotched  NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  0.200 J/cm²
@Temperature -30.0 °C		0.952 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 0.300 J/cm²
@Temperature 23.0 °C		1.43 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+13 ohm-cm1.00e+13 ohm-cmIEC 60093
Surface Resistance 1.00e+12 ohm1.00e+12 ohmIEC 60093
Comparative Tracking Index 600 V600 VTest Solution A; IEC 60112
 
Thermal PropertiesMetricEnglishComments
Melting Point 220 °C428 °FISO 11357-1/3
Deflection Temperature at 0.46 MPa (66 psi) 180 °C356 °FHDT/B; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C140 °FHDT/A; ISO 75-2
Flammability, UL94 V-2
@Thickness 1.60 mm		V-2
@Thickness 0.0630 in
Glow Wire Test 750 °C
@Thickness 1.60 mm		1380 °F
@Thickness 0.0630 in		ICE 60695-12
 
Processing PropertiesMetricEnglishComments
Feed Temperature 60.0 - 80.0 °C140 - 176 °F
Nozzle Temperature 240 - 280 °C464 - 536 °F
Zone 1 225 - 300 °C437 - 572 °F
Zone 2 225 - 300 °C437 - 572 °F
Zone 3 225 - 300 °C437 - 572 °F
Zone 4 225 - 300 °C437 - 572 °F
Melt Temperature 260 - 300 °C500 - 572 °F
Mold Temperature 80.0 - 100 °C176 - 212 °F
Drying Temperature 80.0 °C176 °F
Dry Time 4 - 12.0 hour4 - 12.0 hour
Injection Pressure 100 MPa14500 psi
Hold Pressure 75.0 MPa10900 psi
Back Pressure 0.400 - 1.00 MPa58.0 - 145 psi
 
Descriptive Properties
Rate acc. FMVSS 302 (<100/min)Passed
Rate acc. FMVSS 302,(<100/min)FMVSS 302, >1 [mm] Thickness
Resistance to Oleic acidPass100% Conc. at 23°C
Resistance to AcetaldehydeFail40% Conc. at 23°C
Resistance to Acetic AcidPass20% Conc. at 23°C
Resistance to AcetonePass100% Conc. at 23°C
Resistance to AcetonitrilePass100% Conc. at 23°C
Resistance to AcrylonitrilePass100% Conc. at 23°C
Resistance to Allyl alcoholFail96% Conc. at 23°C
Resistance to Amyl alcoholPass100% Conc. at 23°C
Resistance to Aqueous AmmoniaPass10% Conc. at 23°C
Resistance to BenzeneFail100% Conc. at 40°C
 Pass100% Conc. at 23°C
 Pass100% Conc. at 23°C
Resistance to BiodieselPass100% Conc. at 23°C
Resistance to Boric acidFail100% Conc. at 23°C
 Pass10% Conc. at 23°C
Resistance to Brake fluid (DOT 4)Fail100% Conc. at 130°C
 Pass100% Conc. at 23°C
Resistance to Calcium chloride, alcoholicFail10% Conc. at 23°C
Resistance to Calcium chloride, aqueousPass10% Conc. at 23°C
Resistance to Carbonic acidPass100% Conc. at 60°C
Resistance to Caustic potash solution, aqueousPass50% Conc. at 23°C
Resistance to Chloracetic acidFail50% Conc. at 23°C
Resistance to ChlorineFail100% Conc. at 23°C
Resistance to Chlorine waterFail100% Conc. at 23°C
Resistance to Chromic acidFail10% Conc. at 23°C
Resistance to CyclohexanePass100% Conc. at 23°C
Resistance to CyclohexanolPass100% Conc. at 23°C
Resistance to Dichloro-Acetic acidFail50% Conc. at 23°C
Resistance to Diesel fuel (DIN 51601)Pass100% Conc. at 23°C
Resistance to EthanolPass96% Conc. at 23°C
Resistance to Ethylene glycol/waterFail50% Conc. at 120°C
Resistance to Formaldehyde, aqueousPass10% Conc. at 23°C
Resistance to Formic acidFail2% Conc. at 23°C
Resistance to GlycerinPass100% Conc. at 23°C
Resistance to Hydraulic oil H and HL (DIN 51524)Pass100% Conc. at 100°C
Resistance to Hydrogen chloride, gasFail100% Conc. at 23°C
Resistance to Iso-octanolPass100% Conc. at 23°C
Resistance to IsopropanolPass100% Conc. at 23°C
Resistance to MethanolPass100% Conc. at 23°C
Resistance to Methylene chlorideFail100% Conc. at 23°C
Resistance to Motor oil (SAE 10W-40)Pass100% Conc. at 130°C
 Pass100% Conc. at 23°C
Resistance to Natural GasPass100% Conc. at 23°C
Resistance to Nitric acidFail40% Conc. at 23°C
Resistance to OzoneFail100% Conc. at 23°C
Resistance to PhenolFail100% Conc. at 23°C
Resistance to Phosphoric acidFail30% Conc. at 23°C
Resistance to Potassium chloride, aqueousPass10% Conc. at 23°C
Resistance to Potassium permanganate, aqueousFail10% Conc. at 23°C
Resistance to Sodium chloride, aqueousPass10% Conc. at 23°C
Resistance to Sodium hydroxide solution, aqueousPass1% Conc. at 23°C
Resistance to Sodium hypochlorite, aqueousFail10% Conc. at 23°C
Resistance to Transmission oil (ATF m 1375.4)Pass100% Conc. at 150°C
Resistance to Urea, aqueousPass20% Conc. at 23°C
Resistant to Carbon disulphidePass100% Conc. at 23°C
Resistant to Carbon tetrachloridePass100% Conc. at 23°C
Resistant to Citric acidPass10% Conc. at 23°C
Resistant to Ethyl acetatePass100% Conc. at 23°C
Resistant to Hydrochloric acidFail36% Conc. at 23°C
Resistant to Hydrogen peroxideFail23°C
Resistant to SeawaterPass100% Conc. at 23°C
Resistant to Silicone fluidPass23°C
Resistant to Sulphuric acidFail96% Conc. at 23°C
Resistant to Super-grade petrol (DIN 51600)Pass100% Conc. at 23°C
Resistant to ToluolPass100% Conc. at 23°C
Resistant to WaterPass100% Conc. up to 50°C
Resistant to XylolPass100% Conc. at 23°C
Resistant to Zinc chloride, aqueousFail50% Conc. at 23°C

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45825.html

免责声明: 本文 Akro-Plastic Akromid® B3 (2500) PA 6 Dry 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4