  4. Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled

Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled

Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled 物性表: Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled物性表及特性介绍,Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled注塑参数详情,如需Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.36
  • 吸水率 [%]: 1.2
  • 弯曲模量 [MPa]: 8.50
  • 热变形温度 [℃]: 220.0
 
Physical PropertiesMetricEnglishComments
Density 1.36 g/cc
@Temperature 23.0 °C		0.0491 lb/in³
@Temperature 73.4 °F		ISO 1183
Filler Content 30 %30 %ISO 1172
Water Absorption 1.2 %1.2 %
 2.1 - 2.3 %
@Temperature 23.0 °C		2.1 - 2.3 %
@Temperature 73.4 °F		50% r.h.; ISO 62
Water Absorption at Saturation  0.50 %
@Temperature 30.0 °C		0.50 %
@Temperature 86.0 °F
 1.45 %
@Temperature 100 °C		1.45 %
@Temperature 212 °F
 1.7 %
@Temperature 140 °C		1.7 %
@Temperature 284 °F
 1.95 %
@Temperature 240 °C		1.95 %
@Temperature 464 °F
 2.05 %
@Temperature 280 °C		2.05 %
@Temperature 536 °F
 2.1 %
@Temperature 330 °C		2.1 %
@Temperature 626 °F
 2.15 %
@Temperature 405 °C		2.15 %
@Temperature 761 °F
 6.3 - 6.9 %
@Time 82800 sec		6.3 - 6.9 %
@Time 23.0 hour		ISO 62
Linear Mold Shrinkage, Flow 0.0014 cm/cm0.0014 in/inISO 294-4
Linear Mold Shrinkage, Transverse 0.0083 cm/cm0.0083 in/inISO 294-4
Spiral Flow 655 cm258 inCross Section: 7[mm]x3.5[mm]; AKRO
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 185 MPa26800 psi5 [mm/min]; ISO 527-1/2
 92.5 MPa
@Temperature 160 - 175 °C,
Time 1.80e+7 sec		13400 psi
@Temperature 320 - 347 °F,
Time 5000 hour		5 [mm/min], 50% Loss of Tensile Strength; ISO 527-1/2
 92.5 MPa
@Temperature 130 - 150 °C,
Time 7.20e+7 sec		13400 psi
@Temperature 266 - 302 °F,
Time 20000 hour		5 [mm/min], 50% Loss of Tensile Strength; ISO 527-1/2
Tensile Stress 110 MPa16000 psi
Elongation at Break 3.0 %3.0 %5 [mm/min]; ISO 527-1/2
Tensile Modulus 9.60 GPa1390 ksi1[mm/min]; ISO 527-1/2
 6.00 GPa
@Treatment Temp. 70.0 °C,
Time 1.22e+6 sec		870 ksi
@Treatment Temp. 158 °F,
Time 340 hour		62% rel. humidity
 6.00 GPa
@Treatment Temp. 70.0 °C,
Time 1.48e+6 sec		870 ksi
@Treatment Temp. 158 °F,
Time 410 hour		62% rel. humidity
 6.00 GPa
@Treatment Temp. 70.0 °C,
Time 1.69e+6 sec		870 ksi
@Treatment Temp. 158 °F,
Time 470 hour		62% rel. humidity
 6.10 GPa
@Treatment Temp. 70.0 °C,
Time 1.04e+6 sec		885 ksi
@Treatment Temp. 158 °F,
Time 290 hour		62% rel. humidity
 6.25 GPa
@Treatment Temp. 70.0 °C,
Time 864000 sec		906 ksi
@Treatment Temp. 158 °F,
Time 240 hour		62% rel. humidity
 7.00 GPa
@Treatment Temp. 70.0 °C,
Time 504000 sec		1020 ksi
@Treatment Temp. 158 °F,
Time 140 hour		62% rel. humidity
 8.00 GPa
@Treatment Temp. 70.0 °C,
Time 360000 sec		1160 ksi
@Treatment Temp. 158 °F,
Time 100 hour		62% rel. humidity
Flexural Strength 270 MPa39200 psi2 [mm/min]; ISO 178
Flexural Modulus 8.50 GPa1230 ksi2 [mm/min]; ISO 178
Charpy Impact Unnotched  8.50 J/cm²
@Temperature -30.0 °C		40.4 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 9.50 J/cm²
@Temperature 23.0 °C		45.2 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched 1.70 J/cm²8.09 ft-lb/in²
 1.20 J/cm²
@Temperature -30.0 °C		5.71 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 1.30 J/cm²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+13 ohm-cm1.00e+13 ohm-cmIEC 60093
Surface Resistance 1.00e+12 ohm1.00e+12 ohmIEC 60093
Comparative Tracking Index 575 V575 VTest Solution A; IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 16.0 µm/m-°C
@Temperature 23.0 - 80.0 °C		8.89 µin/in-°F
@Temperature 73.4 - 176 °F		ISO 11359-1/2
CTE, linear, Transverse to Flow 95.0 µm/m-°C
@Temperature 23.0 - 80.0 °C		52.8 µin/in-°F
@Temperature 73.4 - 176 °F		ISO 11359-1/2
Melting Point 220 °C428 °FISO 11357-1/3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C428 °FHDT/B; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C410 °FHDT/A; ISO 75-2
Deflection Temperature at 8.0 MPa 150 °C302 °FHDT/C; ISO 75-2
Flammability, UL94 HB
@Thickness 1.60 mm		HB
@Thickness 0.0630 in
Glow Wire Test 650 °C
@Thickness 1.60 mm		1200 °F
@Thickness 0.0630 in		ICE 60695-12
 
Processing PropertiesMetricEnglishComments
Feed Temperature 60.0 - 80.0 °C140 - 176 °F
Nozzle Temperature 240 - 280 °C464 - 536 °F
Zone 1 225 - 300 °C437 - 572 °F
Zone 2 225 - 300 °C437 - 572 °F
Zone 3 225 - 300 °C437 - 572 °F
Zone 4 225 - 300 °C437 - 572 °F
Melt Temperature 260 - 300 °C500 - 572 °F
Mold Temperature 80.0 - 100 °C176 - 212 °F
Drying Temperature 80.0 °C176 °F
Dry Time 4 - 12.0 hour4 - 12.0 hour
Injection Pressure 100 MPa14500 psi
Hold Pressure 75.0 MPa10900 psi
Back Pressure 0.400 - 1.00 MPa58.0 - 145 psi
 
Descriptive Properties
Rate acc. FMVSS 302 (<100/min)Passed
Rate acc. FMVSS 302,(<100/min)FMVSS 302, >1 [mm] Thickness
Resistance to Oleic acidPass100% Conc. at 23°C
Resistance to AcetaldehydeFail40% Conc. at 23°C
Resistance to Acetic AcidPass20% Conc. at 23°C
Resistance to AcetonePass100% Conc. at 23°C
Resistance to AcetonitrilePass100% Conc. at 23°C
Resistance to AcrylonitrilePass100% Conc. at 23°C
Resistance to Allyl alcoholFail96% Conc. at 23°C
Resistance to Amyl alcoholPass100% Conc. at 23°C
Resistance to Aqueous AmmoniaPass10% Conc. at 23°C
Resistance to BenzeneFail100% Conc. at 40°C
 Pass100% Conc. at 23°C
 Pass100% Conc. at 23°C
Resistance to BiodieselPass100% Conc. at 23°C
Resistance to Boric acidFail100% Conc. at 23°C
 Pass10% Conc. at 23°C
Resistance to Brake fluid (DOT 4)Fail100% Conc. at 130°C
 Pass100% Conc. at 23°C
Resistance to Calcium chloride, alcoholicFail10% Conc. at 23°C
Resistance to Calcium chloride, aqueousPass10% Conc. at 23°C
Resistance to Carbonic acidPass100% Conc. at 60°C
Resistance to Caustic potash solution, aqueousPass50% Conc. at 23°C
Resistance to Chloracetic acidFail50% Conc. at 23°C
Resistance to ChlorineFail100% Conc. at 23°C
Resistance to Chlorine waterFail100% Conc. at 23°C
Resistance to Chromic acidFail10% Conc. at 23°C
Resistance to CyclohexanePass100% Conc. at 23°C
Resistance to CyclohexanolPass100% Conc. at 23°C
Resistance to Dichloro-Acetic acidFail50% Conc. at 23°C
Resistance to Diesel fuel (DIN 51601)Pass100% Conc. at 23°C
Resistance to EthanolPass96% Conc. at 23°C
Resistance to Ethylene glycol/waterFail50% Conc. at 120°C
Resistance to Formaldehyde, aqueousPass10% Conc. at 23°C
Resistance to Formic acidFail2% Conc. at 23°C
Resistance to GlycerinPass100% Conc. at 23°C
Resistance to Hydraulic oil H and HL (DIN 51524)Pass100% Conc. at 100°C
Resistance to Hydrogen chloride, gasFail100% Conc. at 23°C
Resistance to Iso-octanolPass100% Conc. at 23°C
Resistance to IsopropanolPass100% Conc. at 23°C
Resistance to MethanolPass100% Conc. at 23°C
Resistance to Methylene chlorideFail100% Conc. at 23°C
Resistance to Motor oil (SAE 10W-40)Pass100% Conc. at 130°C
 Pass100% Conc. at 23°C
Resistance to Natural GasPass100% Conc. at 23°C
Resistance to Nitric acidFail40% Conc. at 23°C
Resistance to OzoneFail100% Conc. at 23°C
Resistance to PhenolFail100% Conc. at 23°C
Resistance to Phosphoric acidFail30% Conc. at 23°C
Resistance to Potassium chloride, aqueousPass10% Conc. at 23°C
Resistance to Potassium permanganate, aqueousFail10% Conc. at 23°C
Resistance to Sodium chloride, aqueousPass10% Conc. at 23°C
Resistance to Sodium hydroxide solution, aqueousPass1% Conc. at 23°C
Resistance to Sodium hypochlorite, aqueousFail10% Conc. at 23°C
Resistance to Transmission oil (ATF m 1375.4)Pass100% Conc. at 150°C
Resistance to Urea, aqueousPass20% Conc. at 23°C
Resistant to Carbon disulphidePass100% Conc. at 23°C
Resistant to Carbon tetrachloridePass100% Conc. at 23°C
Resistant to Citric acidPass10% Conc. at 23°C
Resistant to Ethyl acetatePass100% Conc. at 23°C
Resistant to Hydrochloric acidFail36% Conc. at 23°C
Resistant to Hydrogen peroxideFail23°C
Resistant to SeawaterPass100% Conc. at 23°C
Resistant to Silicone fluidPass23°C
Resistant to Sulphuric acidFail96% Conc. at 23°C
Resistant to Super-grade petrol (DIN 51600)Pass100% Conc. at 23°C
Resistant to ToluolPass100% Conc. at 23°C
Resistant to WaterPass100% Conc. up to 50°C
Resistant to XylolPass100% Conc. at 23°C
Resistant to Zinc chloride, aqueousFail50% Conc. at 23°C

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45826.html

免责声明: 本文 Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4