- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 缺口冲击强度: 0.45
- 拉伸强度 [MPa]: 80.0
- 弯曲模量 [MPa]: 2.62
- 硬度: 119.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO Test | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hr; ISO Test | ||
| 9.5 % | 9.5 % | ISO Test | |||
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 23°C/50% R.H.; ISO Test | ||
| Oxygen Transmission | 40.3 cc-mm/m²-24hr-atm | 102 cc-mil/100 in²-24hr-atm | ASTM Test | ||
| Nitrogen Transmission | 14.0 cc-mm/m²-24hr-atm | 35.6 cc-mil/100 in²-24hr-atm | ASTM Test | ||
| Carbon Dioxide Transmission | 72.8 cc-mm/m²-24hr-atm | 185 cc-mil/100 in²-24hr-atm | ASTM Test | ||
| Viscosity | 3.15 cP | 3.15 cP | 96% Sulfuric Acid; ISO Test | ||
| 3.2 cP | 3.2 cP | 95% Sulfuric Acid; ISO Test | |||
| 3.4 cP | 3.4 cP | 98% Sulfuric Acid; ISO Test | |||
| 85 cP | 85 cP | Formic Acid Viscosity; ISO Test | |||
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | MD; ASTM Test | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM Test | ||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 2 in/min; ASTM Test | ||
| 80.0 MPa | 11600 psi | 50 mm/min; ISO Test | |||
| Flexural Strength | 100 MPa | 14500 psi | ASTM Test | ||
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM Test | ||
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | 1/8 in; ASTM Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ASTM Test | ||
| 220 °C | 428 °F | 10 K/min; ISO Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM Test | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Primary Processing | Film Extrusion | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.