- 密度 [g/cm3]: 1.16
- 断裂伸长率 [%]: 55.0
- 弯曲强度 [MPa]: 40.0
- 弯曲模量 [MPa]: 1.52
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM Data MD (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM data at 5 mm/min. |
| Flexural Yield Strength | 55.0 MPa | 7980 psi | ASTM Data |
| Flexural Modulus | 1.52 GPa | 220 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |