- 密度 [g/cm3]: 1.62
- 吸水率 [%]: 4.0
- 断裂伸长率 [%]: 210
- 弯曲强度 [MPa]: 145.0
- 弯曲模量 [MPa]: 9.17
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO data |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 4.0 % | 4.0 % | in water; 23°C; ISO data |
| Viscosity Measurement | 50 | 50 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 2.5 % | 2.5 % | Strain at break, ASTM, 5 mm/min |
| 2.5 % | 2.5 % | Strain at break, ISO, 5 mm/min | |
| Flexural Yield Strength | 210 MPa | 30500 psi | ASTM Data |
| Flexural Modulus | 9.17 GPa | 1330 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM Data |
| Flammability, UL94 | V-0 @Thickness 0.840 mm | V-0 @Thickness 0.0331 in | |
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||
| 5VA @Thickness 2.50 mm | 5VA @Thickness 0.0984 in | ||
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |
| Injection Pressure | 3.45 - 10.3 MPa | 500 - 1500 psi | |