- 密度 [g/cm3]: 1.28
- 吸水率 [%]: 1.3
- 弯曲强度 [MPa]: 150.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO data |
| Water Absorption | 1.3 % | 1.3 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 7.6 % | 7.6 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | ISO data |
| 0.0040 cm/cm | 0.0040 in/in | ASTM data MD | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 3.5 % | 3.5 % | Strain at break, ASTM, 5 mm/min |
| 3.5 % | 3.5 % | Strain at break, ISO, 5 mm/min | |
| Tensile Modulus | 7.00 GPa | 1020 ksi | same value from ASTM and ISO test. |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 2.60 GPa | 377 ksi | calculated |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature 20.0 °C | 13.9 µin/in-°F @Temperature 68.0 °F | ISO data |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 20.0 °C | 61.1 µin/in-°F @Temperature 68.0 °F | ISO data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO Data |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |