BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)

BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned) 物性表: BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)物性表及特性介绍,BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)注塑参数详情,如需BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.34
  • 断裂伸长率 [%]: 140
  • 弯曲强度 [MPa]: 90.0
  • 弯曲模量 [MPa]: 4.83
 
Physical PropertiesMetricEnglishComments
Density 1.34 g/cc0.0484 lb/in³(Dry)
Linear Mold Shrinkage 0.0030 cm/cm0.0030 in/inASTM Data MD (Dry)
Linear Mold Shrinkage, Transverse 0.0090 cm/cm0.0090 in/inISO Data (Dry)
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Ultimate 90.0 MPa13100 psiSame value from ASTM and ISO tests; 5 mm/min.
Elongation at Break 6.0 %6.0 %Strain at break, ASTM, 5 mm/min
 6.0 %6.0 %Strain at break, ISO, 5 mm/min
Tensile Modulus 4.61 GPa669 ksisame value from ASTM and ISO test.
Flexural Yield Strength 140 MPa20300 psiASTM Data
Flexural Modulus 4.83 GPa701 ksiASTM Data
 
Thermal PropertiesMetricEnglishComments
Melting Point 220 °C428 °F(Dry)
 
Processing PropertiesMetricEnglishComments
Processing Temperature 275 °C527 °FSee Materials Notes
Mold Temperature 95.0 °C203 °FSee Materials Notes
Drying Temperature 85.0 °C185 °FSee Materials Notes

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45956.html

免责声明: 本文 BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4