- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.27
- 吸水率 [%]: 2.5
- 弯曲强度 [MPa]: 52.0
- 热变形温度 [℃]: 190.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | |
| Water Absorption | 2.5 % | 2.5 % | |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | Humidity Absorption |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | 5 mm/min |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min |
| Tensile Modulus | 4.80 GPa | 696 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Oxygen Index | 22 % | 22 % | |