- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 1.0
- 拉伸强度 [MPa]: 50.0
- 弯曲强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 130.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO R1183 | ||
| Water Absorption | 1.0 % | 1.0 % | 23°C / 24 hrs; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 23°C / 50% RH; ISO 62 | ||
| 3.3 % | 3.3 % | in 23°C water; ISO 62 | |||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 455 °F | after drying; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 76 | 76 | ISO 868 | ||
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ISO R527 | ||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO R527 | ||
| Elongation at Break | 220 % | 220 % | ISO R527 | ||
| Elongation at Yield | 3.4 % | 3.4 % | ISO R527 | ||
| Modulus of Elasticity | 2.30 GPa | 334 ksi | ISO R527 | ||
| Flexural Strength | 63.0 MPa | 9140 psi | After conditioning at 23°C and 50% RH; ISO 178 | ||
| 70.0 MPa | 10200 psi | Dry; ISO 178 | |||
| Flexural Modulus | 2.00 GPa | 290 ksi | After conditioning at 23°C and 50% RH; ISO 178 | ||
| 2.20 GPa | 319 ksi | Dry; ISO 178 | |||
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af | ||
| 1.20 J/cm² @Temperature -20.0 °C | 5.71 ft-lb/in² @Temperature -4.00 °F | Dry; ISO 179/Af | |||
| 1.40 J/cm² @Temperature -20.0 °C | 6.66 ft-lb/in² @Temperature -4.00 °F | After conditioning at 23°C/50%RH; ISO 179/Af | |||
| 1.60 J/cm² @Temperature 23.0 °C | 7.61 ft-lb/in² @Temperature 73.4 °F | Dry; ISO 179/Af | |||
| Tensile Creep Modulus, 1 hour | 2030 MPa | 294000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.60e+15 ohm-cm | 1.60e+15 ohm-cm | ASTM D257 | ||
| Surface Resistance | 4.80e+15 ohm | 4.80e+15 ohm | ASTM D257 | ||
| Dielectric Strength | 38.0 kV/mm @Thickness 1.00 mm | 965 kV/in @Thickness 0.0394 in | ASTM D149 | ||
| Dissipation Factor | 0.025 @Frequency 100000 Hz | 0.025 @Frequency 100000 Hz | NFC 26 230 | ||
| 0.062 @Frequency 100 Hz | 0.062 @Frequency 100 Hz | NFC 26 230 | |||
| 0.065 @Frequency 1000 Hz | 0.065 @Frequency 1000 Hz | NFC 26 230 | |||
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 93.0 µm/m-°C @Temperature 20.0 - 60.0 °C | 51.7 µin/in-°F @Temperature 68.0 - 140 °F | TMS2 Perkin Elmer | ||
| CTE, linear, Transverse to Flow | 130 µm/m-°C @Temperature 20.0 - 60.0 °C | 72.2 µin/in-°F @Temperature 68.0 - 140 °F | TMS2 Perkin Elmer | ||
| Melting Point | 220 °C | 428 °F | ISO R1218 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO R75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO R75 | ||
| Vicat Softening Point | 130 °C | 266 °F | 50 N - B method; ISO 306 | ||
| 195 °C | 383 °F | 10 N - A method; ISO 306 | |||
| Flammability, UL94 | HB | HB | |||
| Flammability Test | 17 | 17 | [mm/min] Burning Speed; FMVSS 302 | ||
| Descriptive Properties | |||||
| Automotive classification | E-3 | FMVSS 302 | |||