- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 1.1
- 缺口冲击强度: 0.85
- 弯曲强度 [MPa]: 155.0
- 弯曲模量 [MPa]: 8.07
- 硬度: 121.0
- 热变形温度 [℃]: 219.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| 6.7 % | 6.7 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Measurement | 55 | 55 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 155 MPa | 22500 psi | 0.2 in/min; ASTM Test | ||
| 65.0 MPa @Temperature 120 °C | 9430 psi @Temperature 248 °F | ISO Data | |||
| 65.0 MPa @Temperature 120 °C | 9430 psi @Temperature 248 °F | ASTM Test | |||
| 80.0 MPa @Temperature 80.0 °C | 11600 psi @Temperature 176 °F | ASTM Test | |||
| 80.0 MPa @Temperature 80.0 °C | 11600 psi @Temperature 176 °F | ISO Data | |||
| 220 MPa @Temperature -40.0 °C | 31900 psi @Temperature -40.0 °F | ASTM Test | |||
| 220 MPa @Temperature -40.0 °C | 31900 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 155 MPa | 22500 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 9.58 GPa | 1390 ksi | 1mm/min; ISO 527 | ||
| 2.73 GPa @Temperature 120 °C | 396 ksi @Temperature 248 °F | ISO Data | |||
| 3.815 GPa @Temperature 80.0 °C | 553.3 ksi @Temperature 176 °F | ISO Data | |||
| 8.74 GPa @Temperature -40.0 °C | 1270 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 230 MPa | 33400 psi | ISO Data | ||
| Flexural Modulus | 8.07 GPa | 1170 ksi | ISO Data | ||
| 8.48 GPa | 1230 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.850 J/cm @Thickness 3.17 mm | 1.59 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO Test | ||
| 6.50 kJ/m² @Temperature -40.0 °C | 3.09 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | 5.40 J/cm² | 25.7 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.860 J/cm² | 4.09 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 21.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C | 37.2 µin/in-°F | ISO 11359 | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM Test | ||
| 205 °C | 401 °F | ISO 75 | |||
| Flammability, UL94 | HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 115 °C | 239 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||